Fragrant environment-friendly plastic film material

A plastic film, environmental protection technology, applied in the field of energy-saving and environmental protection materials, can solve the problems of difficult degradation, environmental pollution, etc., and achieve the effects of low cost, reducing air pollution, and stable heat resistance

Inactive Publication Date: 2018-10-02
桐城市申科塑业有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, plastic is closely related to people's daily life. It has the advantages of convenience and durability, but it has the problem of being difficult to degrade, causing environmental pollution.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A kind of fragrance environment-friendly plastic film material is made of the following raw materials by weight:

[0028] 50 parts of degradable plastic masterbatch, 20 parts of polyolefin elastomer, 10 parts of silicone spherical micropowder, 10 parts of glass fiber, 5 parts of activated carbon, 3 parts of plasticizer, 5 parts of dried sweet potato residue, 10 parts of nano-zinc oxide, dispersion 3 parts of antibacterial agent, 3 parts of nano copper powder antibacterial agent, 3 parts of cyclodextrin modified polyether, 2 parts of photodegradant, 1 part of rose essential oil, 2 parts of silicone oil;

[0029] The degradable plastic masterbatch is composed of the following components in parts by weight: 30 parts of PVC resin, 15 parts of modified starch, 5 parts of polyamide resin, 3 parts of pigment, 5 parts of nano-montmorillonite, 2 parts of coupling agent, surface Active agent 1 part.

[0030] The dried sweet potato dregs are prepared through the following steps: ...

Embodiment 2

[0035] A kind of fragrance environment-friendly plastic film material is made of the following raw materials by weight:

[0036] 60 parts of degradable plastic masterbatch, 25 parts of polyolefin elastomer, 15 parts of silicone spherical micropowder, 15 parts of glass fiber, 9 parts of activated carbon, 7 parts of plasticizer, 9 parts of dried sweet potato residue, 14 parts of nano zinc oxide, dispersion 8 parts of antibacterial agent, 5 parts of nano copper powder antibacterial agent, 5 parts of cyclodextrin modified polyether, 4 parts of photodegradant, 3 parts of rose essential oil, 4 parts of silicone oil;

[0037] The degradable plastic master batch is composed of the following components in parts by weight: 45 parts of PVC resin, 20 parts of modified starch, 10 parts of polyamide resin, 8 parts of pigment, 10 parts of nano-montmorillonite, 5 parts of coupling agent, surface Active agent 6 parts.

[0038] The dried sweet potato dregs are prepared through the following st...

Embodiment 3

[0043] A kind of fragrance environment-friendly plastic film material is made of the following raw materials by weight:

[0044] 54 parts of degradable plastic masterbatch, 26 parts of polyolefin elastomer, 13 parts of silicone spherical micropowder, 13 parts of glass fiber, 7 parts of activated carbon, 5 parts of plasticizer, 7 parts of dried sweet potato residue, 12 parts of nano zinc oxide, dispersion 6 parts of antibacterial agent, 4 parts of nano copper powder antibacterial agent, 4 parts of cyclodextrin modified polyether, 3 parts of photodegradant, 2 parts of rose essential oil, 3 parts of silicone oil;

[0045] The degradable plastic masterbatch is composed of the following components in parts by weight: 37 parts of PVC resin, 18 parts of modified starch, 8 parts of polyamide resin, 5 parts of pigment, 8 parts of nano-montmorillonite, 4 parts of coupling agent, surface Active agent 3 parts.

[0046] The dried sweet potato dregs are prepared through the following steps...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a fragrant environment-friendly plastic film material which is prepared from the following raw materials in parts by weight: 50-60 parts of degradable plastic masterbatch, 20-25 parts of a polyolefin elastomer, 10-15 parts of a spherical powder of silicone, 10-15 parts of glass fibers, 5-9 parts of activated carbon, 3-7 parts of a plasticizer, 5-9 parts of dried sweet potato residues, 10-14 parts of nano-zinc oxide, 3-8 parts of a dispersant, 3-5 parts of a nano-copper powder antibacterial agent, 3-5 parts of cyclodextrin-modified polyether, 2-4 parts of a photodegradant, 1-3 parts of rose essential oil and 2-4 parts of silicone oil. The fragrant environment-friendly plastic film material provided by the invention is low in cost, and also has excellent flame retardancy and electrical conductivity and relatively high tensile strength; the spherical powder of silicone is added so that a finished product of the film material has characteristics of chemical resistance, stable heat resistance, ultraviolet resistance, weather resistance, improved dispersion processability and the like; and the rose essential oil is added so that a film product has fragrant smell and also has antibacterial and bactericidal effects.

Description

technical field [0001] The invention relates to an energy-saving and environment-friendly material, in particular to a fragrance-friendly and environment-friendly plastic film material. Background technique [0002] Plastic raw material is a kind of synthetic living natural polymer compound, which can be arbitrarily kneaded into various shapes and finally can keep the shape of the material or plastic material products. At present, plastic is closely related to people's daily life. It has the advantages of convenience and durability, but it has the problem of being difficult to degrade, causing environmental pollution. [0003] As the concepts of low-carbon economy and green packaging are gradually recognized by people, environmentally friendly packaging materials have been widely used. At present, there are many kinds of packaging materials on the market, and there are many different types of environmentally friendly packaging materials in the same field. Contents of the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L51/02C08L77/00C08L23/00C08L3/02C08L83/04C08K13/04C08K7/14C08K7/24C08K7/18C08K3/22C08K3/08C08K5/053C08K5/21C08K5/39C08J5/18
CPCC08J5/18C08J2327/06C08J2403/02C08J2423/00C08J2451/02C08J2477/00C08J2483/04C08K5/053C08K5/21C08K5/39C08K7/14C08K7/18C08K7/24C08K13/04C08K2003/085C08K2003/2296C08K2201/011
Inventor 潘杰
Owner 桐城市申科塑业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap