Waste polyester textile recycling method and system

A technology for textiles and polyester, applied in the field of chemical recycling of polyester textiles, can solve the problems of flammable and explosive methanol, complicated process implementation, etc., and achieve the effects of color improvement, simple process and resource saving.

Pending Publication Date: 2018-10-12
SHANGHAI JUYOU CHEM ENG
View PDF0 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the mainstream chemical recycling method in the market is methanol alcoholysis method, which uses methanol to react alcoholysis with PET to generate methyl terephthalate, and then uses ethylene glycol for transesterification to generate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waste polyester textile recycling method and system
  • Waste polyester textile recycling method and system
  • Waste polyester textile recycling method and system

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0030]

[0031] (1) Waste polyester textile recycling system

[0032] like figure 1 As shown, the waste polyester textile recycling system 100 in this embodiment includes: washing equipment, alcoholysis equipment, purification equipment, polycondensation equipment, pelletizing equipment, spinning equipment, auxiliary equipment and recycling equipment.

[0033] Washing equipment, alcoholysis equipment, purification equipment and polycondensation equipment are connected sequentially through pipelines. The washing equipment has a material conveyor belt, an ethylene glycol spray pipe, and an ethylene glycol waste liquid recovery tank. The alcoholysis equipment has an alcoholysis kettle. The purification equipment has a vacuum distillation kettle, a first dilution kettle, a second dilution kettle and a centrifugal dryer connected in sequence. The polycondensation equipment has prepolymerization tanks and final polymerization tanks connected in sequence.

[0034] The auxiliary...

Example Embodiment

[0046]

[0047] The method for recycling waste polyester textiles in this embodiment is also carried out by using the waste polyester textile recycling system 100 in Embodiment 1, including the following steps:

[0048] Step 1, pretreatment section

[0049] Put the waste polyester textiles into the washing equipment, add ethylene glycol and stir for hot washing, the mass ratio of waste polyester textiles to ethylene glycol is 1:2, the mixing time is 30min, the temperature is 130°C, after heating The waste polyester textiles are washed and dried to obtain pretreated textiles.

[0050] Step 2, alcoholysis section

[0051] The pretreated textiles and ethylene glycol are dropped into the alcoholysis kettle according to the mass ratio of 1:1, and then the alcoholysis catalyst zinc acetate is dropped into. The consumption of zinc acetate is 0.2% of the quality of the pretreated textiles, and the reaction temperature is controlled at 190°C, the reaction time is 3h, and the alcoho...

Example Embodiment

[0055]

[0056] The method for recycling waste polyester textiles in this embodiment is also carried out by using the waste polyester textile recycling system 100 in Embodiment 1, including the following steps:

[0057] Step 1, pretreatment section

[0058] Put the waste polyester textiles into the washing equipment, add ethylene glycol and stir for hot washing, the mass ratio of waste polyester textiles to ethylene glycol is 1:4, the mixing time is 30min, the temperature is 100 ℃, after heating The waste polyester textiles are washed and dried to obtain pretreated textiles.

[0059] Step 2, alcoholysis section

[0060] The pretreated textiles and ethylene glycol are dropped into the alcoholysis kettle according to the mass ratio of 1:1, and then the alcoholysis catalyst zinc acetate is dropped into. The consumption of zinc acetate is 0.4% of the quality of the pretreated textiles, and the controlled reaction temperature is 180°C, the reaction time is 3h, and the alcoholys...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Intrinsic viscosityaaaaaaaaaa
Intrinsic viscosityaaaaaaaaaa
Intrinsic viscosityaaaaaaaaaa
Login to view more

Abstract

The invention provides a waste polyester textile recycling method and system. The waste polyester textile recycling method comprises the steps that firstly,ethylene glycol is added into waste polyester textiles for stirring and pretreatment; secondly,the pretreated textiles are placed in an alcoholysis kettle,ethylene glycol is added again for an alcoholysis reaction with zinc acetate as a catalyst,undissolved substances in alcoholysis liquid are filtered out,then the alcoholysis liquid is subjected to reduced pressure distillation,crude polyethylene glycol terephthalate obtained through reduced pressure distillation is purified,and purified polyethylene glycol terephthalate is obtained; thirdly,the purified polyethylene glycol terephthalate is added into a pre-polymerization kettle and subjected to pre-polymerization by adding an catalyst,a prepolymer obtained through the pre-polymerization reaction is put into a final polymerization kettle for final polymerization,discharging is conducted through a melt pump to obtain recycled polyester,and the recycled polyester is sliced.

Description

technical field [0001] The invention relates to the technical field of chemical recycling of polyester textiles, in particular to a method for recycling waste polyester textiles through ethylene glycol alcoholysis and a recycling system thereof. Background technique [0002] With the rapid development of my country's polyester industry, the recycling and reuse of polyester textiles has gradually attracted the attention of the society. Although polyester itself is non-toxic and harmless, it is difficult to degrade in nature. Once it is not handled properly, it may cause pollution to the environment. . Polyethylene terephthalate (PET) is a high polymer obtained by condensation polymerization of ethylene terephthalate (BHET). BHET monomer is obtained by esterifying ethylene glycol with terephthalate. to make. At present, there are two main methods of recycling polyester: physical recycling and chemical recycling. The physical recycling method is to melt and extrude waste text...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08J11/24C08G63/183C08G63/78D01F13/04C08L67/02
CPCD01F13/04C08G63/183C08G63/78C08J11/24C08J2367/02Y02P70/62Y02W30/62
Inventor 甘胜华李红彬吴宝宅何洲丁杨惠勤
Owner SHANGHAI JUYOU CHEM ENG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap