Preparation method of nano-copper-coated aluminum composite fuel

A technology of composite fuel and coated aluminum, applied in nanotechnology, transportation and packaging, metal processing equipment, etc., can solve the problem of low combustion calorific value, achieve uniform distribution, uniform particle size, and simple production equipment

Active Publication Date: 2021-07-20
合肥净龙环保科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the coating materials involved in the research are inert substances, non-solid rocket propellant formulation components, and the combustion calorific value is not high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of nano-copper-coated aluminum composite fuel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Embodiment 1: The steps of preparing nano-copper-coated aluminum composite fuel are as follows:

[0025] (1) Under normal temperature and pressure, prepare a certain concentration of copper sulfate aqueous solution and sodium hydroxide aqueous solution, and mix the copper sulfate aqueous solution and sodium hydroxide aqueous solution at a volume ratio of 1:1 to form a copper hydroxide suspension; The copper oxide suspension is centrifuged, washed with deionized water until the pH is neutral, and copper hydroxide is obtained; wherein, the concentration of the copper sulfate aqueous solution is 0.01mol / L, and the concentration of the sodium hydroxide aqueous solution is 2.1 times the concentration of the copper sulfate water;

[0026] (2) Add the copper hydroxide and aluminum powder obtained in step (1) into water for ultrasonic dispersion with a power of 60 watts to obtain a mixed aqueous phase suspension of copper hydroxide and aluminum powder; wherein, the particle size...

Embodiment 2

[0028] Embodiment 2: The steps of preparing nano-copper-coated aluminum composite fuel are as follows:

[0029] (1) Under normal temperature and pressure, prepare a certain concentration of copper sulfate aqueous solution and sodium hydroxide aqueous solution, and mix the copper sulfate aqueous solution and sodium hydroxide aqueous solution at a volume ratio of 1:1 to form a copper hydroxide suspension; The copper oxide suspension is centrifuged, washed with deionized water until the pH is neutral to obtain copper hydroxide; wherein, the concentration of the copper sulfate aqueous solution is 0.055mol / L, and the concentration of the sodium hydroxide aqueous solution is 2.1 times the concentration of the copper sulfate water;

[0030] (2) Add the copper hydroxide and aluminum powder obtained in step (1) into water for ultrasonic dispersion with a power of 210 watts to obtain a mixed aqueous phase suspension of copper hydroxide and aluminum powder; wherein, the particle size of t...

Embodiment 3

[0032] Embodiment 3: The steps of preparing nano-copper-coated aluminum composite fuel are as follows:

[0033] (1) Under normal temperature and pressure, prepare a certain concentration of copper sulfate aqueous solution and sodium hydroxide aqueous solution, and mix the copper sulfate aqueous solution and sodium hydroxide aqueous solution at a volume ratio of 1:1 to form a copper hydroxide suspension; The copper oxide suspension is centrifuged, washed with deionized water until the pH is neutral, and copper hydroxide is obtained; wherein, the concentration of the copper sulfate aqueous solution is 0.1mol / L, and the concentration of the sodium hydroxide aqueous solution is 2.1 times the concentration of the copper sulfate water;

[0034](2) Add the copper hydroxide and aluminum powder obtained in step (1) into water for ultrasonic dispersion with a power of 360 watts to obtain a mixed aqueous phase suspension of copper hydroxide and aluminum powder; wherein, the particle size ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a nano-copper-coated aluminum composite fuel, which comprises adding a trace amount of copper ion complexing agent trisodium citrate and aluminum ions into the mixed aqueous phase suspension liquid of copper hydroxide and aluminum powder The complexing agent is ammonium fluoride, and the purple-red product obtained by the reaction is centrifuged to obtain a nano-copper-coated aluminum composite fuel. The process of the present invention is carried out at normal temperature and pressure without introducing any surfactant, and the obtained nano-copper is evenly distributed on the surface of the nano-aluminum, and the particle size is uniform; the concentration of the trace copper ion complexing agent can also be adjusted to adjust the obtained nano-copper. The particle size of the copper particles.

Description

technical field [0001] The invention relates to a preparation method of a nano-aluminum composite fuel for a solid propellant, in particular to a preparation method of a nano-copper-coated aluminum composite fuel. Background technique [0002] Due to its high density, low oxygen consumption and high combustion heat, aluminum powder has a significant effect on improving specific impulse, so it is widely used as metal fuel in solid rocket propellants. Compared with traditional micron aluminum fuel, the special small size effect and surface effect of nano aluminum fuel make it have higher reactivity and energy release efficiency. Then, the chemical properties of nano-aluminum are more active than micro-aluminum, and it is easier to interact with external environmental factors (temperature, humidity, atmosphere, etc.), forming a higher content of inert oxide film on its surface, thus losing most of its activity. Therefore, maintaining the activity of nano-aluminum fuel has beco...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22F9/24B22F1/02B22F1/00B82Y40/00
CPCB82Y40/00B22F9/24B22F1/17B22F1/054
Inventor 程志鹏于森博褚效中徐继明仲慧张莉莉戴本林
Owner 合肥净龙环保科技有限公司