Preparing method for antibacterial stainless steel composite workpiece

A technology of antibacterial stainless steel and composite parts, which is applied in the direction of coating, etc., can solve the problems of low composite fastness, affect the use experience, and easy to breed bacteria, etc., and achieve the effect of good integration and strong binding force

Inactive Publication Date: 2018-11-02
FOSHAN GAOMING LIGANG PRECISION CASTING CO LTD
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the actual application process, the composite parts made of stainless steel parts and plastic materials have the problem of low composite fastness. At the same time, in the process of being us

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0020] Example 1

[0021] In this embodiment, a composite material composed of a 12Cr12 steel plate with a length, width and height of 10 cm×8 cm×1 cm and an antibacterial PP plastic is used. The specific preparation method is as follows:

[0022] Step 1. Take the above-mentioned stainless steel plate and first immerse the stainless steel plate in a strengthened corrosive solution, which is a deionized aqueous solution containing 5wt% nitric acid, 5wt% hydrochloric acid, 3wt% hydrofluoric acid and 5wt% ferric chloride, at 60℃ After 15s of corrosion in the enhanced corrosive solution, it is immersed in a circulating 40℃ saturated picric acid deionized water solution for 60s. The saturated picric acid deionized water solution is also added with 2wt% corrosion inhibitor, the corrosion inhibitor is rosin amine polyoxyethylene A mixed additive of ether and thiourea 1:0.8. After taking it out, use spray water to rinse and dry the corrosion surface of stainless steel. The cleaning proce...

Example Embodiment

[0026] Example 2

[0027] In this embodiment, a composite material of 06Cr13 steel plate with length, width and height of 10 cm×8 cm×1 cm and antibacterial PE plastic is used. The specific preparation method is as follows:

[0028] Step 1. Take the above-mentioned stainless steel plate, and first immerse the stainless steel plate in a strengthened corrosive solution, which is a deionized aqueous solution containing 5wt% nitric acid, 5wt% hydrochloric acid, 3wt% hydrofluoric acid and 5wt% ferric chloride at 65°C After 15s of corrosion in the enhanced corrosive solution, it is immersed in a circulating 40℃ saturated picric acid deionized water solution for 60s. The saturated picric acid deionized water solution is also added with 2wt% corrosion inhibitor, the corrosion inhibitor is rosin amine polyoxyethylene A mixed additive of ether and thiourea 1:0.8. After taking it out, use spray water to rinse and dry the corrosion surface of stainless steel. The cleaning process is combined ...

Example Embodiment

[0032] Example 3

[0033] In this embodiment, a composite material composed of 06Cr13 steel plate with length, width and height of 10cm×8cm×1cm and antibacterial PVC plastic is used. The specific preparation method is as follows:

[0034] Step 1. Take the above-mentioned stainless steel plate and first immerse the stainless steel plate in a strengthened corrosive solution, which is a deionized aqueous solution containing 5wt% nitric acid, 5wt% hydrochloric acid, 3wt% hydrofluoric acid and 5wt% ferric chloride, at 60℃ After 15s of corrosion in the enhanced corrosive solution, it is immersed in a circulating 45℃ saturated picric acid deionized aqueous solution for 55s. The saturated picric acid deionized aqueous solution is also added with 5wt% corrosion inhibitor, which is rosin amine polyoxyethylene A mixed additive of ether and thiourea 1:0.8. After taking it out, use spray water to rinse and dry the corrosion surface of stainless steel. The cleaning process is combined with ult...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Surface roughnessaaaaaaaaaa
Surface roughnessaaaaaaaaaa
Surface roughnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparing method for an antibacterial stainless steel composite workpiece. The preparing method comprises the following steps that firstly, a stainless steel material is taken and subjected to corrosion etching treatment, the surface roughness Ra of treated stainless steel is 10-50 microns, and the thickness of the stainless steel material is not lower than 5 mm; and secondly, after a layer of promoting bonding agent is sprayed to the surface of the stainless steel material, temperature rise is conducted to 50-60 DEG C, an antibacterial plastic layer with the thickness being 0.1-2 mm is formed on the surface of the stainless steel through in-mold injection molding under the vacuum condition, and accordingly the antibacterial stainless steel composite workpiece ismanufactured. The stainless steel material prepared through the method and plastic materials are high in binding force and good in integrity, a certain antibacterial function is achieved, and the antibacterial stainless steel composite workpiece is suitable for being applied to products frequently making contact with the human bodies to serve a structure workpiece.

Description

technical field [0001] The invention belongs to the field of stainless steel composite materials, and in particular relates to a preparation method of antibacterial stainless steel composite parts. Background technique [0002] Stainless steel materials are widely used in miniaturized products, especially in the field of 3C electronics. Due to their good formability, high strength, high hardness, and good corrosion resistance, stainless steel materials are widely used in consumer electronics such as mobile phones and computers. product. Consumer electronic products are currently demanding more and more metal material structures. With the development of thinner and smaller consumer electronic products, traditional stainless steel parts have a wide range of raw materials and good formability, but due to their relatively high density It is difficult to meet the requirements of reducing the thickness and quality of components without greatly affecting the structural strength in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B29C45/14C23F1/28
CPCB29C45/14778B29C2045/14868C23F1/28
Inventor 王立峰
Owner FOSHAN GAOMING LIGANG PRECISION CASTING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap