A viscose and construction technology, applied in the field of construction viscose materials, can solve the problems of increasing building load-bearing burden, low construction efficiency, low bonding strength, etc., and achieve the effects of wide application range, material saving and good crack resistance.

Inactive Publication Date: 2018-11-06
淮北卓颂建筑工程有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are two main types of adhesives used in construction: one is the traditional concrete with cement, which is widely used in construction production, but this method is relatively heavy, and it is suitable for lighter buildings or Unsuitable building materials will increase the load-bearing burden of the building, and too many materials are used, and the construction efficiency is not high
The other is an adhesive prepared by mixing 107 glue or other viscose with foamed styrene, but this kind of adhesive often contains toxic and volatile solvents, which are harmful to the human body, and its bonding strength is not high. , the scope of application is narrow

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] The invention provides a construction adhesive material. The raw materials include the following components in weight percent: 4.5% of acrylic resin emulsion, 3.0% of polyvinyl alcohol, 20.0% of polyurethane aqueous dispersion, 8.0% of phenoxyethanol, and Drying oil and wax 2.8%, parabens 10.0%, acrylic acid emulsion 10%, starch 3.0%, propylene glycol 10.0%, glycerin 5.0%, stearic acid 10.0%, stearate Sodium acid is 1.0%, transparent nucleating agent is 5.0%, transparent stabilizer is 9.0%, polyvinylpyrrolidone is 1.5%, preservative is 2.0%, and the balance is deionized water. The sum of the above components is 100%.

[0014] The transparent nucleating agent is a sorbitol-based transparent nucleating agent.

[0015] The polyhydric alcohol is glycerin, propylene glycol and polyethylene glycol 400, and the proportioning ratio is: 0.9~1.1:2:3 in sequence.

[0016] Polyvinylpyrrolidone is any one of pigments, dyes or pigments.

[0017] 0.1-0.3% o-cresolphthalein coloring ...

Embodiment 2

[0019] The invention provides a construction adhesive material. The raw materials include the following components in weight percentage: 3.0% of acrylic resin emulsion, 5.0% of polyvinyl alcohol, 20.0% of polyurethane aqueous dispersion, 7.0% of phenoxyethanol, and Drying oil and wax 5.0%, parabens 15.0%, acrylic acid emulsion 8.0%, starch 6.0%, propylene glycol 8.0%, glycerin 15.0%, stearic acid 6.0%, stearate Sodium acid is 2.0%, transparent nucleating agent is 3.0%, transparent stabilizer is 6.0%, polyvinylpyrrolidone is 1.0%, preservative is 1.0%, and the balance is deionized water. The sum of the above components is 100%.

Embodiment 3

[0021] The invention provides a construction adhesive material. The raw materials include the following components in weight percentage: 0.8% of acrylic resin emulsion, 3.0% of polyvinyl alcohol, 30.0% of polyurethane water dispersion, 5.0% of phenoxyethanol, and Drying oil and wax 2.8%, parabens 10.0%, acrylic acid emulsion 8%, starch 3.0%, propylene glycol 5.0%, glycerin 20.0%, stearic acid 3.0%, stearate Sodium acid is 1.0%, transparent nucleating agent is 2.0%, transparent stabilizer is 9.0%, polyvinylpyrrolidone is 1.5%, preservative is 2.0%, and the balance is deionized water. The sum of the above components is 100%.

[0022] The construction adhesive material provided by the present invention is simple to use, and the adhesive can be applied on the surface of building materials such as tiles, and the tiles can be bonded to the ground or wall. Compared with ordinary concrete, its quality is lighter, It saves more materials, reduces the load-bearing burden of buildings, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a building viscose material. Firstly, a vacuum electric furnace is used for smelting, an alloy ingot is put into a heating furnace with an initial temperature of 600 DEG C orhigher for heating, and finally, a horizontal continuous casting billet is rolled after being cooled. According to the building viscose material provided by the invention, the oxidation resistance ofa welding seam under a high temperature is improved, Si also serves as an excellent deoxidizing agent and can increase the flowability of slag and molten metal, moreover, slag-bonding on the surface of the welding seam is avoided. Therefore, the welding efficiency is improved, and the property of welding deposit metal and the usability are met.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a building adhesive material. Background technique [0002] Adhesives have important applications in the construction industry and demand is growing rapidly. At present, there are two main types of adhesives used in construction: one is the traditional concrete with cement, which is widely used in construction production, but this method is relatively heavy, and it is suitable for lighter buildings or Unsuitable building materials will increase the load-bearing burden of the building, and too many materials are used, and the construction efficiency is not high. The other is an adhesive prepared by mixing 107 glue or other viscose with foamed styrene, but this kind of adhesive often contains toxic and volatile solvents, which are harmful to the human body, and its bonding strength is not high. , the scope of application is narrow. Contents of the invention [0003]...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J175/04C09J133/00C09J103/02C09J129/04C09J11/06C09J11/08
CPCC08K2201/014C08L2205/025C08L2205/035C09J11/06C09J11/08C09J175/04C08L33/00C08L29/04C08L91/00C08L91/06C08L3/02C08K5/00C08K5/09C08K5/053C08K5/098
Inventor 刘芳
Owner 淮北卓颂建筑工程有限公司