A methane reforming multi-core shell hollow nickel-nickel silicate-ceo 2 preparation method

A hollow type, silicate technology, applied in the direction of catalyst activation/preparation, chemical instruments and methods, chemical/physical processes, etc., can solve the problem of losing high specific surface area

Inactive Publication Date: 2020-10-30
GUIZHOU INST OF TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present, these metal silicates are only used as catalyst precursors. After high-temperature reduction, the metal silicates are completely decomposed and lose their advantages of high specific surface area.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A methane reforming multi-core shell hollow nickel-nickel silicate-ceo <sub>2</sub> preparation method
  • A methane reforming multi-core shell hollow nickel-nickel silicate-ceo <sub>2</sub> preparation method
  • A methane reforming multi-core shell hollow nickel-nickel silicate-ceo <sub>2</sub> preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] (1) 200mL ethanol, 100mL water and 40mL orthosilicate methyl ester at 0 o Mix and stir evenly at C, then add urea to adjust the pH to 10. After stirring for 2h, it was separated with a centrifuge and washed with a mixture of methanol and water. Finally, 600nm silica nanoparticles were obtained at 150 o C dried for 24h.

[0025] (2) Take 2g of silicon dioxide and 0.3g of nickel nitrate, add ammonia water, and adjust the pH to 8. Put the mixed solution into the autoclave and heat to 50 o C degree, after reacting for 24h, cool to room temperature. Centrifuge, wash with methanol, ethanol, and water, and place in a 100-degree drying oven. Obtain nickel silicate hollow spheres (such as figure 2 shown), the specific area is 250m 2 g -1 .

[0026] (3) Disperse hollow nickel silicate spheres in a mixed solution of ethanol (10mL) and water (20mL). After stirring for 30 min, cerium nitrate (3 g) and ammonia water (30 mL) were added. Raise the reaction temperature to 40...

Embodiment 2

[0030] (1) 200mL ethanol, 100mL water and 40mL methyl orthosilicate at 35 o C and mix well. Add urea to adjust the pH to 10. After stirring for 2h, it was separated with a centrifuge. Wash with a mixture of methanol and water. Finally, 600nm silica nanoparticles were obtained at 150 o C dried for 24h.

[0031] (2) Take 2g of silicon dioxide and 0.3g of nickel nitrate, add ammonia water, and adjust the pH to 11. Put the mixed solution into the autoclave and heat it to 135 o C degree, after reacting for 24h, cool to room temperature. Centrifuge and wash with methanol, ethanol, water, and then prevent from a 100-degree drying oven. Obtain nickel silicate hollow spheres (such as figure 2 shown), the specific area is 250m 2 g -1 .

[0032] (3) Disperse hollow nickel silicate spheres in a mixed solution of ethanol (10mL) and water (20mL). After stirring for 30 min, cerium nitrate (3 g) and ammonia water (30 mL) were added. Raise the reaction temperature to 95 o C, rea...

Embodiment 3

[0036] (1) 200mL ethanol, 100mL water and 40mL methyl orthosilicate at 70 o C and mix well. Add urea to adjust the pH to 10. After stirring for 2h, it was separated with a centrifuge, and washed with methanol and water. Finally, 600nm silica nanoparticles were obtained at 150 o C dried for 24h.

[0037] (2) Take 2g of silicon dioxide and 0.3g of nickel nitrate, add ammonia water, and adjust the pH to 13. Put the mixed solution into the autoclave and heat to 220 o C degree, after reacting for 24h, cool to room temperature. Centrifuge and wash with methanol, ethanol, water, and then prevent from a 100-degree drying oven. Obtain nickel silicate hollow spheres (such as figure 2 shown), the specific area is 250m 2 g -1 .

[0038] (3) Disperse hollow nickel silicate spheres in a mixed solution of ethanol (10mL) and water (20mL). After stirring for 30 min, cerium nitrate (3 g) and ammonia water (30 mL) were added. Raise the reaction temperature to 150 o C, reacted for 4...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a methane reforming multi-core shell hollow type nickel-nickel silicate-CeO 2 The preparation method includes the steps of (1) first preparing silica nanoparticles; (2) adding nickel precursor to the silica nanoparticles, 50 o C~220 o Under C conditions, nickel silicate hollow spheres are prepared; (3) Disperse the nickel silicate hollow spheres in a mixed solution of ethanol and water, and add CeO 2 of precursors and precipitants at a temperature of 40 o C~150 o React under C conditions to obtain nickel silicate-CeO 2 Core-shell hollow nanospheres; (4) Nickel silicate-CeO 2 Highly dispersed nickel-nickel silicate-CeO prepared by reduction of core-shell hollow nanospheres 2 Multi-core shell hollow catalyst. Multi-core shell hollow type nickel-nickel silicate-CeO prepared by the invention 2 The catalyst has high anti-sintering properties for both nickel and ceria, high oxygen hole concentration, high carbon deposition resistance, high nickel dispersion, and high CeO 2 Dispersion and other advantages, it shows high catalytic activity and high anti-carbon deposition performance in the application of low-temperature methane dry reforming catalytic reaction.

Description

technical field [0001] The invention relates to a methane reforming multi-core shell hollow nickel-nickel silicate-CeO 2 The preparation method belongs to CH 4 The technical field of reforming multi-core-shell hollow catalysts. Background technique [0002] Nickel-based catalysts have been widely studied at home and abroad because of their low price and high catalytic activity for reforming. When they are applied to CH 4 During the dry reforming reaction, carbon deposition on nickel-based catalysts is relatively serious, mainly because the sintering of nickel metal promotes the occurrence of carbon deposition side reactions. especially when CH 4 Dry reforming reaction temperature below 600 o C, the carbon deposition phenomenon is more serious. The present inventor has developed a core-shell structure catalyst, which can effectively prevent metal sintering. However, these core-shell structures generally suffer from low specific surface area and low mass transfer efficie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/83B01J35/08B01J37/03B01J37/10B01J37/18C01B3/40
CPCC01B3/40B01J23/83B01J37/031B01J37/033B01J37/10B01J37/18C01B2203/1241C01B2203/1058C01B2203/0238B01J35/397B01J35/399B01J35/393B01J35/23B01J35/51Y02P20/52
Inventor 李自卫李敏
Owner GUIZHOU INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com