Modified cotton fiber and easy-care fabric prepared therefrom

A technology for modifying cotton and cotton fibers, applied in the field of cotton textiles, can solve problems such as shrinkage and wrinkling, and achieve the effects of memory elimination, good moisture absorption, and good skin-friendliness.

Inactive Publication Date: 2018-11-16
合肥云都棉花有限公司
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, cotton textiles also have their own shortcomings. For example, cotton textiles often shrink after rinsing due to the curling characteristics of the fiber itself. The shrunken cotton textiles need to be ironed. Good, but re-wrinkles after multiple rinses

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A kind of modified cotton fiber, the modification method of cotton fiber comprises the steps:

[0024] (1) Add cotton fibers to 15wt% sodium hydroxide solution, soak for 30 minutes at a temperature of 35°C, centrifuge and dehydrate after impregnation, and then rinse the cotton fibers after centrifugation with deionized water until rinsed The PH value is 7-7.5;

[0025] (2) Continue to centrifuge and dehydrate the rinsed fiber, add it to the bleach solution containing hydrogen peroxide, brightener and sodium bisulfite after dehydration, bleach at 70°C for 30 minutes, and then dehydrate and dry after bleaching;

[0026] (3) Send the cotton fiber from the previous step into a mixed solution of equal mass ratio of absolute ethanol and acetone, wash it with ultrasonic vibration at a temperature of 40°C for 10 minutes, and centrifuge and dehydrate after the treatment is completed;

[0027] (4) According to the mass parts: 15 parts of titanium sulfate, 3 parts of urea, 1 part...

Embodiment 2

[0034] A kind of modified cotton fiber, the modification method of cotton fiber comprises the steps:

[0035] (1) Add cotton fiber to 20wt% sodium hydroxide solution, soak it at 45°C for 40 minutes, centrifuge and dehydrate after impregnation, then rinse the cotton fiber after centrifuge dehydration with deionized water, and rinse to the rinse solution The PH value is 7.5;

[0036] (2) Continue to centrifuge and dehydrate the rinsed fiber, add it to the bleach solution containing hydrogen peroxide, brightener and sodium bisulfite after dehydration, bleach at 80°C for 40 minutes, dehydrate and dry after bleaching;

[0037] (3) Send the cotton fiber from the previous step into a mixed solution of equal mass ratio of absolute ethanol and acetone, wash it with ultrasonic vibration at a temperature of 60°C for 15 minutes, and centrifuge and dehydrate after the treatment is completed;

[0038] (4) According to the mass parts: 20 parts of titanium sulfate, 7 parts of urea, 3 parts o...

Embodiment 3

[0045] A kind of modified cotton fiber, the modification method of cotton fiber comprises the steps:

[0046] (1) Add cotton fiber to 18wt% sodium hydroxide solution, soak it at 40°C for 35 minutes, centrifuge and dehydrate after impregnation, then rinse the cotton fiber after centrifuge dehydration with deionized water, and rinse to the rinse solution The PH value is 7.3;

[0047] (2) Continue to centrifuge and dehydrate the rinsed fiber, add it to the bleach solution containing hydrogen peroxide, brightener and sodium bisulfite after dehydration, bleach at 75°C for 35 minutes, and then dehydrate and dry after bleaching;

[0048] (3) Send the cotton fiber from the previous step into a mixed solution of equal mass ratio of absolute ethanol and acetone, wash it with ultrasonic vibration at a temperature of 50°C for 13 minutes, and centrifuge and dehydrate after the treatment is completed;

[0049] (4) According to the mass parts: 18 parts of titanium sulfate, 5 parts of urea, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of cotton textiles and specifically relates to a modified cotton fiber and easy-care fabric prepared therefrom. A preparation method of the modified cottonfiber comprises the following steps: performing alkaline water dipping on cotton fibers with sodium hydroxide solution, bleaching the cotton fibers, pretreating the treated cotton fibers with organicsolution, and performing modifier treatment and centrifugal purification on the cotton fibers, wherein a cotton fiber modifier comprises titanium sulfate, urea, butyl titanate, sodium hydroxymethyl acrylamide and chitosan. The fabric prepared by mixing the modified cotton fibers, polypropylene fibers and chinlon is good in skin-friendly performance and also has air permeability and anti-wrinkle performance.

Description

technical field [0001] The invention relates to the technical field of cotton textiles, in particular to a modified cotton fiber and a non-ironing cloth prepared therefrom. Background technique [0002] Cotton is a plant that can provide natural plant fiber products. It is a crop with important strategic value. The cotton fiber in cotton has good toughness, high strength, excellent elasticity, chemical stability and moisture absorption performance. It is the best fabric fiber. Clothing made of cotton has good warmth retention, strong air permeability, and has excellent skin-friendly properties, making it very comfortable to wear. [0003] But cotton textiles also have its own shortcomings. For example, cotton textiles often shrink after rinsing due to the curling characteristics of the fiber itself. The shrunken cotton textiles need to be ironed. Nice, but re-wrinkled after multiple rinses. Contents of the invention [0004] Aiming at the problems existing in the prior a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M11/38D06M11/56D06M13/432D06M13/503D06M13/419D06M15/03D06M10/00D06L4/13A41D31/00D06M101/06
CPCA41D31/00D06L4/13D06M10/003D06M11/38D06M11/56D06M13/419D06M13/432D06M13/503D06M15/03D06M2101/06
Inventor 程飞
Owner 合肥云都棉花有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com