A technology of yoga mats and accelerators, which is applied in the field of antibacterial yoga mats, can solve the problems of difficult bacteria cleaning on yoga mats and the limited disinfection power of cleaning solutions, and achieve the effects of reducing human injury, improving killing effect, and buffering external forces

Inactive Publication Date: 2018-11-23
WUHU SAUNAKING ELECTRONICS TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, people usually clean yoga mats by cleaning yoga mats, but the cleaning liquid has limited disinfection power, and it is difficult to completely clean up the bacteria on yoga mats

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial yoga mat

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] An antibacterial yoga mat is made of the following parts by weight: 90 parts by weight of styrene TPE elastomer, 30 parts by weight of polyurethane, 15 parts by weight of nitrile rubber, 25 parts by weight of titanium dioxide, lysine 5 parts by weight, 4 parts by weight of silane coupling agent KH792, 18 parts by weight of copolymerized PP grafted maleic anhydride (grafting rate 1.5-2.0%), 1 part by weight of 2-mercaptobenzothiazole, 2,2, 0.5 parts by weight of 4-trimethyl-1,2-dihydroquinoline polymer, 0.5 parts by weight of antioxidant DLTP, 1 part by weight of di-tert-butyl peroxide cumene, triallyl isocyanuric acid 0.5 parts by weight of ester, 1.5 parts by weight of carbon black (with a particle size of 40 nm to 200 nm), 0.5 parts by weight of ethylene bisstearamide and 0.5 parts by weight of ethylene oxide.

[0023] The preparation method of the antibacterial yoga mat, the steps are as follows:

[0024] (1) Ultrasonically disperse titanium dioxide in absolute etha...

Embodiment 2

[0028] An antibacterial yoga mat is made of the following parts by weight: 100 parts by weight of styrene TPE elastomer, 36 parts by weight of polyurethane, 20 parts by weight of nitrile rubber, 20 parts by weight of titanium dioxide, lysine 4 parts by weight, 5 parts by weight of silane coupling agent KH560, 15 parts by weight of copolymerized PP grafted maleic anhydride (graft rate 1.5-2.0%), 2 parts by weight of tetraethylthiuram disulfide, 4,4' -Dioctyldiphenylamine, N,N'-di(β-naphthyl)-p-phenylenediamine 0.5 parts by weight, antioxidant 168 0.3 parts by weight, dicumyl peroxide 0.5 parts by weight, triallyl iso 0.5 parts by weight of cyanurate, 1.5 parts by weight of carbon black (with a particle size of 300 nm to 500 nm), 0.8 parts by weight of polyethylene wax and 0.5 parts by weight of ethylene oxide.

[0029] The preparation method of the antibacterial yoga mat, the steps are as follows:

[0030] (1) Ultrasonically disperse titanium dioxide in absolute ethanol at 100...

Embodiment 3

[0034] An antibacterial yoga mat is made of the following parts by weight: 80 parts by weight of styrene TPE elastomer, 40 parts by weight of polyurethane, 16 parts by weight of nitrile rubber, 15 parts by weight of titanium dioxide, lysine 5 parts by weight, titanate coupling agent 201 3 parts by weight, 10 parts by weight of copolymerized PP grafted maleic anhydride (grafting rate 1.5-2.0%), 0.5 parts by weight of N-cyclyl-2-benzothiazole sulfenamide Parts by weight, 0.5 parts by weight of 2,2,4-trimethyl-1,2-dihydroquinoline polymer, 0.3 parts by weight of antioxidant 1076, 1 part by weight of di-tert-butyl cumene peroxide, carbon 1.5 parts by weight of black (with a particle diameter of 100 nm to 300 nm), 0.5 parts by weight of polyethylene wax and 0.5 parts by weight of propylene oxide copolymer.

[0035] The preparation method of the antibacterial yoga mat, the steps are as follows:

[0036] (1) Ultrasonically disperse titanium dioxide in absolute ethanol at 200 Hz to o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of fitness equipment, in particular to an antibacterial yoga mat, which is prepared from a composition of the following raw materials in parts by weight: 72-120 parts of styrene TPE elastomer, 30-50 parts of polyurethane, 15-30 parts of nitrile butadiene rubber, 6-25 parts of titanium dioxide, 3-5 parts of lysine, 3-8 parts of a coupling agent, 5-25 parts of a compatilizer, 0.5-2 parts of an accelerator, and 0-5 parts of an auxiliary agent. The antibacterial yoga mat provided by the invention not only has good elasticity and toughness but also has excellent antibacterial performance.

Description

technical field [0001] The invention relates to the technical field of fitness equipment, in particular to an antibacterial yoga mat. Background technique [0002] Nowadays, people are under high pressure of work and life, and more and more people are in a sub-healthy state. Exercise can effectively regulate the nervous system and endocrine system, and improve human health. With the development of the economy and the improvement of people's living standards, The opportunities for people to exercise outdoors are reduced, and they take indoor sports instead. Yoga mats are one of the most commonly used equipment in indoor sports. Yoga mats can effectively reduce the pain caused by the contact between the human body and the ground. In addition to the characteristics of softness and good resilience, it should also have good anti-skid performance, toughness and mechanical properties. At present, most yoga mats are processed from PVC materials, which are mainly mixed with fillers ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L53/02C08L75/04C08L9/02C08L51/06C08K13/06C08K9/06C08K9/04C08K3/22C08K5/20C08K5/14C08K5/47
CPCC08L53/02C08K2003/2241C08L2205/035C08L75/04C08L9/02C08L51/06C08K13/06C08K9/06C08K9/04C08K3/22C08K5/20C08K5/14C08K5/47
Inventor 马西健崔亮
Owner WUHU SAUNAKING ELECTRONICS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap