Gum dipping liquid for improving fiber fabric performance and preparation method thereof
A technology of fiber fabric and dipping solution, applied in the direction of wear-resistant fibers, flame-retardant fibers, etc., to achieve the effects of improving performance, improving flame retardancy and flexibility, and improving flame retardancy
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0020] A dipping solution for improving the performance of fiber fabrics, which is composed of the following ingredients in parts by weight: 15-19 parts of epoxy resin, 6 parts of glycerin glycidyl ether, 1 part of latex, 2 parts of RF resin, and 10 parts of aqueous solution , 30 parts of deionized water, 1 part of formaldehyde, 1 part of resorcinol E, 1 part of curing agent, 1 part of flexible agent, 5 parts of resorcinol, 1 part of adhesive, 1 part of fabric flame retardant.
[0021] The curing agent is specifically diethylenetriamine.
[0022] The latex is styrene-butadiene latex.
[0023] The binder is a binder containing -NCO groups, and its chemical formula is C 19 h 37 NO.
[0024] A kind of preparation method of the dipping liquid that improves fiber fabric performance, its step is as follows,
[0025] C1: According to the formula of dipping solution, add epoxy resin, latex, RF resin, aqueous solution and curing agent into the reaction vessel, then stir evenly at 2...
Embodiment 2
[0031] A dipping solution for improving the performance of fiber fabrics, consisting of the following ingredients in parts by weight: 16 parts of epoxy resin, 7 parts of glycerin glycidyl ether, 1.5 parts of latex, 8 parts of RF resin, 11 parts of aqueous solution, 40 parts of ionized water, 1.5 parts of formaldehyde, 2 parts of resorcinol E, 1.5 parts of curing agent, 1.5 parts of flexible agent, 6 parts of resorcinol, 1.2 parts of adhesive, 1.5 parts of fabric flame retardant.
[0032] The curing agent is specifically a mixture of diethylenetriamine, triethylenetetramine and tetraethylenepentamine.
[0033] The latex is a mixture of styrene-butadiene latex and natural latex.
[0034] The binder is a binder containing -NCO groups, and its chemical formula is C 19 h 37 NO.
[0035] A kind of preparation method of the dipping liquid that improves fiber fabric performance, its steps are as follows:
[0036] C1: According to the formula of dipping solution, add epoxy resin, l...
Embodiment 3
[0042] A dipping solution for improving the performance of fiber fabrics, consisting of the following formula components in parts by weight: 17 parts of epoxy resin, 7.5 parts of glycerin glycidyl ether, 2 parts of latex, RF resin 9 parts, 11.5 parts of aqueous solution, 50 parts of deionized water, 2 parts of formaldehyde, 4 parts of resorcinol E, 2 parts of curing agent, 2 parts of flexible agent, 8 parts of resorcinol, 1.5 parts of adhesive, fabric barrier Fuel agent 2 parts.
[0043] The curing agent is specifically a mixture of diethylenetriamine, triethylenetetramine and tetraethylenepentamine.
[0044] The latex is a mixture of styrene-butadiene latex and natural latex.
[0045] The binder is a binder containing -NCO groups, and its chemical formula is C 19 h 37 NO.
[0046] A kind of preparation method of the dipping liquid that improves fiber fabric performance, its steps are as follows:
[0047] C1: According to the formula of dipping solution, add epoxy resin, ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com