Unlock instant, AI-driven research and patent intelligence for your innovation.

Environment-friendly adhesive formula for badminton production

An adhesive and badminton technology, applied in the directions of polymer adhesive additives, non-polymer adhesive additives, non-polymer organic compound adhesives, etc., can solve the problems of adverse physical and mental health, poor adhesive bonding , can not play protection and other problems, to achieve the effect of not easy to crack and degumming, small shrinkage, and prolong service life

Inactive Publication Date: 2018-11-27
ANHUI HUA LING FEATHER PROD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Adhesives need to be used in many places in the production of badminton, but the existing adhesives are poorly bonded and cannot play a role in protection and strengthening. The experience in use is poor, and the wear and tear is serious. Some use Ingredients that are irritating to the human body are not conducive to people's physical and mental health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0012] An environmentally friendly adhesive formula for badminton production, which consists of the following raw materials in parts by weight: 57 parts of polyvinyl alcohol, 38 parts of epoxy resin, 34 parts of ABS resin, 22 parts of ethylene glycol dimethacrylate, water-based 14 parts of polyvinyl butyral, 13 parts of neoprene rubber, 6 parts of hydroxycumene peroxide, 1.2 parts of polyacrylamide, 0.9 parts of ammonium persulfate, 3 parts of sodium linoleate, 5 parts of methacrylic acid, 4 parts of diol, 3 parts of magnesium chloride, 1 part of highly active zinc oxide, 4 parts of cinnamic acid propyl betaine, 3 parts of talcum powder, 0.8 parts of protease, 3 parts of borax, 4 parts of paraffin wax, 13 parts of rosin resin, 6 parts of mica powder parts, 15 parts of metallic bamboo charcoal solution, 4 parts of thickener, 5 parts of hydrogenated castor oil, and 150 parts of deionized water.

[0013] The metallic bamboo charcoal solution is prepared by mixing metal masterbatc...

specific Embodiment 2

[0014] An environmentally friendly adhesive formula for badminton production, which consists of the following raw materials in parts by weight: 52 parts of polyvinyl alcohol, 35 parts of epoxy resin, 31 parts of ABS resin, 20 parts of ethylene glycol dimethacrylate, water-based 12 parts of polyvinyl butyral, 11 parts of neoprene rubber, 4 parts of hydroxycumene peroxide, 1 part of polyacrylamide, 0.7 parts of ammonium persulfate, 2 parts of sodium linoleate, 3 parts of methacrylic acid, 2 parts of diol, 2 parts of magnesium chloride, 0.9 parts of highly active zinc oxide, 3 parts of cinnamic acid propyl betaine, 2 parts of talcum powder, 0.5 parts of protease, 2 parts of borax, 3 parts of paraffin wax, 10 parts of rosin resin, 5 parts of mica powder parts, 13 parts of metal bamboo charcoal solution, 2 parts of thickener, 4 parts of hydrogenated castor oil, and 133 parts of deionized water.

[0015] The metallic bamboo charcoal solution is prepared by mixing metal masterbatches...

specific Embodiment 3

[0016] An environmentally friendly adhesive formula for badminton production, which consists of the following raw materials in parts by weight: 46 parts of polyvinyl alcohol, 32 parts of epoxy resin, 28 parts of ABS resin, 17 parts of ethylene glycol dimethacrylate, water-based 10 parts of polyvinyl butyral, 9 parts of neoprene rubber, 3 parts of hydroxycumene peroxide, 0.8 parts of polyacrylamide, 0.5 parts of ammonium persulfate, 1 part of sodium linoleate, 2 parts of methacrylic acid, 1 part of diol, 1 part of magnesium chloride, 0.7 parts of highly active zinc oxide, 1 part of cinnamon amidopropyl betaine, 1 part of talcum powder, 0.3 parts of protease, 1 part of borax, 2 parts of paraffin wax, 7 parts of rosin resin, 3 parts of mica powder 10 parts of metal bamboo charcoal solution, 1 part of thickener, 2 parts of hydrogenated castor oil, 114 parts of deionized water.

[0017] The metallic bamboo charcoal solution is prepared by mixing metal masterbatches containing zinc ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environment-friendly adhesive formula for badminton production. The adhesive is prepared from, by weight, 46-61 parts of polyvinyl alcohol, 32-40 parts of epoxy resin, 28-36parts of ABS resin, 17-24 parts of glycol dimethyl acrylic ester, 10-16 parts of waterborne polyvinyl butyral, 9-14 parts of chloroprene rubber, 3-7 parts of cumene hydroperoxide, 0.8-1.5 parts of polyacrylamide, 0.5-1 part of ammonium persulfate, 1-4 parts of sodium linoleate, 2-6 parts of methacrylic acid, 1-6 parts of glycol, 1-4 parts of magnesium chloride, 0.7-1.2 parts of high-activity zincoxide, 1-5 parts of Lauramidopropyl betaine, 1-4 parts of talcum powder, 0.3-1 part of protease, 1-4 parts of borax, 2-5 parts of paraffin, 7-16 parts of abietin, 3-8 parts of mica powder, 10-17 parts of metal bamboo charcoal solution, 1-5 parts of thickening agent, 2-6 parts of hydrogenated castor oil and 114-152 parts of deionized water. The adhesive achieves the protection effect and the effect of enhancing firmness, the hitting resistance of badminton is enhanced, and the service life is prolonged.

Description

technical field [0001] The invention relates to the technical field of shuttlecock processing, in particular to an environment-friendly adhesive formula for shuttlecock production. Background technique [0002] As early as two thousand years ago, a game similar to badminton appeared in China, India and other countries. It is called Shuttlecock in China, Pune in India, and Shuttlecock in Western Europe and other countries. In the 1870s, British soldiers brought back the Pune game learned in India as a recreational activity after dinner and during breaks. [0003] In 1954, a batch of children who served the motherland returned home, brought back advanced badminton technology, and formed a national training team at the same time. Subsequently, our country also established badminton teams in several major cities along the southeast coast, with returned overseas Chinese youth as the backbone. Experience and lessons of badminton and collated technical data, combined with their ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More