Method for comprehensively recycling valuable components in paigeite

A boronite and component technology, applied in the direction of boron halide compounds, chemical instruments and methods, boron halides, etc., can solve problems such as large pollution, low utilization rate of magnesium, and impact on the environment, so as to promote comprehensive utilization and realize comprehensive utilization. The effect of utilization and low production cost

Inactive Publication Date: 2018-11-27
HEBEI UNIV OF ENG +1
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the production of boron ore mainly comes from sedimentary and metamorphic boron-magnesium ores in Liaoning, but this type of ore only accounts for 8.98% of the total boron reserves in the country. After years of development and utilization, the reserves of boron-magnesium ores are less than 2 million tons. Mineral resources are nearly exhausted. With the development of the national economy, the demand for boron is growing rapidly, and the available boron resources cannot meet the needs of all walks of life.
These three schemes can complete the separation of iron and boron in boron iron ore to a certain extent. The former scheme can achieve better iron and boron re

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] Using 1# boronite in a certain place, its chemical composition is TFe:29.23%, Fe 3 o 4 : 26.24%, FeO: 12.87%, B 2 o 3 : 8.03%, MgO: 26.88%, SiO 2 : 12.22%, CaO: 0.35%, other oxides: 13.41%.

[0058] The method for the comprehensive recovery and utilization of valuable components in boron ore comprises the following steps:

[0059] A. Mixing materials: Add mineral powder, low-sulfur coal and calcium oxide into the mixer, the addition of low-sulfur coal is 10% of the total mass of mineral powder, and the addition of calcium oxide is 5% of the total mass of mineral powder. The particle size of mineral powder, low-sulfur coal and calcium oxide is ≤100 mesh, and they are fully mixed.

[0060] B. Reduction of iron oxides: put the mixed powder into a tunnel kiln, heat it to 1200° C. with microwaves, and keep it warm for 0.8 hours to reduce iron oxides to obtain metal sponge iron.

[0061] C. Separation of metal sponge iron: After the reduction, use 1.5T magnetic inductio...

Embodiment 2

[0067] Using 1# boronite in a certain place, its chemical composition is TFe:29.23%, Fe 3 o 4 : 26.24%, FeO: 12.87%, B 2 o 3 : 8.03%, MgO: 26.88%, SiO 2 : 12.22%, CaO: 0.35%, other oxides: 13.41%.

[0068] The method for the comprehensive recovery and utilization of valuable components in boron ore comprises the following steps:

[0069] A. Mixing: Add mineral powder, coke chips, and calcium oxide into the mixer. The amount of coke chips added is 12% of the total mass of mineral powder, and the amount of calcium oxide added is 4% of the total mass of mineral powder. , coke scraps and calcium oxide with a particle size of ≤100 mesh, fully mixed.

[0070] B. Reduction of iron oxides: put the mixed powder into a tunnel kiln, heat it with microwave to 1000°C, and keep it warm for 1 hour to reduce the iron oxides to obtain metal sponge iron.

[0071] C. Separation of metal sponge iron: After the reduction, use 1.2T magnetic induction to separate to obtain metal sponge iron an...

Embodiment 3

[0077] Using 2# boronite in a certain place, its chemical composition is TFe: 26.82%, Fe 3 o 4 : 28.52%, FeO: 6.64%, B 2 o 3 :8.97%, MgO:23.50%, SiO 2 : 18.29%, CaO: 0.72%, other oxides: 13.36%.

[0078] The method for the comprehensive recovery and utilization of valuable components in boron ore comprises the following steps:

[0079] A. Mixing materials: Add mineral powder, low-sulfur coal and calcium oxide into the mixer, the addition of low-sulfur coal is 13% of the total mass of mineral powder, and the addition of calcium oxide is 6% of the total mass of mineral powder. The particle size of mineral powder, low-sulfur coal and calcium oxide is ≤100 mesh, and they are fully mixed.

[0080] B. Reduction of iron oxides: put the mixed powder into a tunnel kiln, heat it with microwave to 1200°C, and keep it warm for 0.5 hours to reduce the iron oxides to obtain metal sponge iron.

[0081] C. Separation of metal sponge iron: After the reduction, use 1.5T magnetic induction...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for comprehensively recycling valuable components in paigeite, and belongs to the field of metallurgy. The method adopts microwave heating, tunnel kiln smelting and chloride separation. According to the method, iron, boron and magnesium elements in the paigeite can be effectively separated, the grade and yield of iron and boron can be improved, high-magnesium tailings can be recycled, utilization of the composite paigeite is promoted, the situation of iron mine, boron mine and magnesium mine resource shortage can be effectively relieved, the ecological featureof resource and energy can be taken into consideration, and comprehensive utilization of paigeite resource can be realized. The method has the advantages of simple process, low production cost, energyconservation, emission reduction and the like.

Description

technical field [0001] The invention relates to the comprehensive utilization of metallurgical slag resources, in particular to a method for treating boron ore, belonging to the field of metallurgy. Background technique [0002] At present, the production of boron ore mainly comes from sedimentary and metamorphic boron-magnesium ores in Liaoning, but this type of ore only accounts for 8.98% of the total boron reserves in the country. After years of development and utilization, the reserves of boron-magnesium ores are less than 2 million tons. Mineral resources are nearly exhausted. With the development of the national economy, the demand for boron is growing rapidly, and the available boron resources cannot meet the needs of all walks of life. However, my country is rich in boron-iron ore resources, and the reserve of boron-iron ore in Liaoning alone reaches 280 million tons, of which B 2 o 3 The estimated reserves are 21.84 million tons. Since boronite mainly includes bor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C21B13/00C01B35/06C22B26/22C01B33/107
CPCC01B33/10721C01B35/061C21B13/00C22B26/22Y02P10/20
Inventor 黄伟军刘亚静
Owner HEBEI UNIV OF ENG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap