Production and preparation method for ceramic steel medical door

A technology of medical doors and ceramic steel, applied in anti-corrosion coatings, epoxy resin coatings, coatings, etc., can solve the problems of inability to isolate radiation, and achieve the effects of strong adjustability, good aesthetics, and comfortable air

Inactive Publication Date: 2018-11-30
安徽省浦菲尔建材有限公司
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to solve the defect that the hospital door cannot isolate radiation in the prior art, and proposes a production and preparation method of a ceramic steel medical door

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A production and preparation method of ceramic steel medical door, comprising the following steps:

[0021] S1. Cut the steel plate into a suitable size door panel according to the installation size;

[0022] S2, the making of antirust coating: take by weighing 32 parts of epoxy resins, 28 parts of acrylic resins, 4 parts of sebacic acid, 4 parts of isopropanolamines, 5 parts of dodecanedioic acids, 5 parts of octanols, titanium dioxide, 23 parts, 3 parts of rosin, 5 parts of cellulose acetate, 5 parts of tetrasodium EDTA, 10 parts of calcium carbonate, 5 parts of mica, 15 parts of magnesium oxide, 18 parts of silica aluminum oxide, 3 parts of zirconia, acetic acid 4 parts of ethylene-ethylene copolymer emulsion, 1 part of polyacrylate and 62 parts of purified water are used as raw materials, which are fully mixed and filtered under the action of ultrasonic waves to obtain an antirust coating;

[0023] S3, the making of anti-radiation film: take by weighing 295 parts o...

Embodiment 2

[0026] A production and preparation method of ceramic steel medical door, comprising the following steps:

[0027] S1. Cut the steel plate into a suitable size door panel according to the installation size;

[0028] S2, the making of antirust paint: take by weighing 33 parts of epoxy resins, 32 parts of acrylic resins, 5 parts of sebacic acid, 5 parts of isopropanolamines, 7 parts of dodecanedioic acids, 7 parts of octanol, toluidine red powder 25 parts, rosin 6 parts, cellulose acetate 7 parts, EDTA tetrasodium salt 6 parts, calcium carbonate 12 parts, mica 6 parts, magnesium oxide 17 parts, silica aluminum oxide 19 parts, zirconia 4 parts, acetic acid 5 parts of ethylene-ethylene copolymer emulsion, 2 parts of polyvinyl butyral and 64 parts of purified water are used as raw materials, which are fully mixed and filtered under the action of ultrasonic waves to obtain an antirust coating;

[0029] S3, the making of anti-radiation film: take by weighing 32 parts of epoxy resins...

Embodiment 3

[0032] A production and preparation method of ceramic steel medical door, comprising the following steps:

[0033] S1. Cut the steel plate into a suitable size door panel according to the installation size;

[0034] S2, the making of antirust coating: take by weighing 35 parts of epoxy resins, 34 parts of acrylic resins, 6 parts of sebacic acid, 6 parts of isopropanolamines, 8 parts of dodecanedioic acids, 8 parts of octanols, titanium dioxide, 27 parts of ultramarine powder, 8 parts of rosin, 9 parts of cellulose acetate, 7 parts of tetrasodium edetate, 16 parts of calcium carbonate, 8 parts of mica, 18 parts of magnesium oxide, 21 parts of silica aluminum oxide, and 5 parts of zirconia , 7 parts of vinyl acetate-ethylene copolymer emulsion, 2 parts of acrylate and 66 parts of purified water are used as raw materials, which are fully mixed and filtered under the action of ultrasonic waves to obtain an antirust coating;

[0035] S3, the making of anti-radiation film: take by ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a production and preparation method for a ceramic steel medical door. The production and preparation method comprises the following steps of C1, cutting a steel plate into a door sheet with proper dimension according to the installation dimension; S2, preparing an anti-rust coating, specifically, weighing raw materials, and mixing the raw materials under the action of ultrasonic waves so as to obtain the anti-rust coating; S3, preparing an anti-radiation thin film, specifically, weighing raw materials, treating powder under a molten state through a tape casting method through an extruding machine so as to obtain the thin film, and carrying out double-roller air drying, traction and reeling on the thin film so as to obtain the anti-radiation thin film; and S4, coating the outer end of the door sheet with a layer of paint, attaching the anti-radiation thin film to the outer layer of the door sheet so as to obtain the ceramic steel medical door. The method has theadvantages that the outer side of a steel door is coated with the anti-rust coating, so that the medical door has the anti-rust characteristic, in addition, the appearance color of the steel door is strong in adjustability, the steel door is more attractive in appearance, uniform mixing is carried out by adopting an ultrasonic method, and the uniform mixing effect is better.

Description

technical field [0001] The invention relates to the technical field of steel door processing, in particular to a production and preparation method of a ceramic steel medical door. Background technique [0002] Due to its particularity, the hospital, especially the dialysis room, ultrasound room, etc., will produce a large amount of infrared rays, ultrasound, etc., which have a strong therapeutic effect on the treatment of patients, but will cause harm to normal people, so they need to be isolated. There can be no leakage. All the doors of the radiology department of the existing hospital are basically ordinary wooden doors or ordinary steel doors. They cannot prevent the leakage of some radioactive sources such as infrared rays and ultrasonic waves, and are easy to cause harm to others. Contents of the invention [0003] The purpose of the present invention is to solve the defect that the hospital door cannot isolate radiation in the prior art, and proposes a production an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D133/00C09D5/08C09D7/61C09D7/63C09D7/65C08L63/00C08L33/00C08L27/18C08K7/24C08J5/18
CPCC08J5/18C08J2363/00C08J2427/18C08J2433/00C08K7/24C08K2003/222C08K2003/2244C08K2003/265C09D5/08C09D7/61C09D7/63C09D7/65C09D163/00C08L33/00C08L93/04C08L1/12C08L31/04C08K13/02C08K5/092C08K5/17C08K3/26C08K3/34C08K3/22C08K3/36
Inventor 段承连陈小军陈林
Owner 安徽省浦菲尔建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap