Metal structure test block for ultrasonic testing and preparation method thereof

A metal structure and ultrasonic testing technology, which is applied in the direction of material analysis, measuring devices, and instruments using sonic/ultrasonic/infrasonic waves. and other problems, to achieve the effect of good internal compactness and scalability, ensuring stability and stress-sensing sensitivity, and improving detection accuracy.

Active Publication Date: 2018-11-30
浙江方圆金属材料检测有限公司 +1
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Non-destructive testing is a common method for detecting internal defects in steel structure products. However, there are currently no ultrasonic testing standards for the characteristics of steel structures, the scarcity of highly skilled testing technicians, and the lack of physical comparison materials for testing. Due to weak testing technology links and Inadequate monitoring of construction and other links leads to the collapse of steel structure buildings from time to time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A metal structure test block for ultrasonic testing, comprising an inner sand core block, a transition composite layer, and an outer metal layer formed by successive pouring. The surface of the inner sand core block is crosswise provided with a number of interconnected channels, and the inner diameter of the channel opening Larger than the inner diameter of the widest part, the inner sand core block consists of the following raw materials: sandstone, soft refractory clay, water glass, the transition composite layer is a composite molten iron containing silicon carbide, and the outer metal layer is a composite molten iron containing no silicon carbide.

[0025] Among them, the channel depth is 1-10mm, the outer metal layer casting thickness is 5-20mm, and the channel longitudinal section is "U"-shaped.

[0026] The inner sand core block also includes rare earth phosphates, wherein the rare earth is selected from any one of lanthanum, cerium, and shirt. The mass percentage of e...

Embodiment 2

[0037] A metal structure test block for ultrasonic testing, comprising an inner sand core block, a transition composite layer, and an outer metal layer formed by successive pouring. The surface of the inner sand core block is crosswise provided with a number of interconnected channels, and the inner diameter of the channel opening Larger than the inner diameter of the widest part, the inner sand core block consists of the following raw materials: sandstone, soft refractory clay, water glass, the transition composite layer is a composite molten iron containing silicon carbide, and the outer metal layer is a composite molten iron containing no silicon carbide.

[0038] Among them, the channel depth is 1-10mm, the outer metal layer casting thickness is 5-20mm, and the channel longitudinal section is "U"-shaped.

[0039] The inner sand core block also includes rare earth phosphates, wherein the rare earth is selected from any one of lanthanum, cerium, and shirt. The mass percentage of e...

Embodiment 3

[0050] A metal structure test block for ultrasonic testing, comprising an inner sand core block, a transition composite layer, and an outer metal layer formed by successive pouring. The surface of the inner sand core block is crosswise provided with a number of interconnected channels, and the inner diameter of the channel opening Larger than the inner diameter of the widest part, the inner sand core block consists of the following raw materials: sandstone, soft refractory clay, water glass, the transition composite layer is a composite molten iron containing silicon carbide, and the outer metal layer is a composite molten iron containing no silicon carbide.

[0051] Among them, the channel depth is 1-10mm, the outer metal layer casting thickness is 5-20mm, and the longitudinal section of the channel is gourd-shaped (the upper half is a semicircle, the lower half is a complete circle, and the inner diameter of the upper half is larger than the lower Half inner diameter).

[0052] T...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
depthaaaaaaaaaa
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a metal structure test block for ultrasonic testing. The metal structure test block comprises an inner sand core block, a transition composite layer and an outer metal layer which are sequentially cast. The surface of the inner sand core block is crossedly provided with a plurality of communicated channels. The inner diameter of the channel opening is larger than the widestinner diameter of the channel. The inner sand core block comprises sandstone, soft refractory clay and water glass. The transition composite layer comprises composite molten iron containing silicon carbide. The outer metal layer comprises composite molten iron without silicon carbide. Through the reasonable structure design and material matching, the test block for ultrasonic testing has stable structural quality. The metal structure test block has good internal compactness and retractable elasticity and low transverse wave and longitudinal wave dampening effects, can be used for an ultrasonictest on the diagonal welding joint and has high detection sensitivity.

Description

Technical field [0001] The invention relates to the technical field of metal test blocks, in particular to a metal structure test block for ultrasonic testing and a preparation process thereof. Background technique [0002] my country's steel structure industry has developed rapidly in the past 10 years and has become the world's largest steel structure country with the largest amount of steel structure, the strongest manufacturing and construction capacity, the largest industrial scale and the largest enterprise scale in the world. The successful construction of major steel structure projects in various places shows that my country's comprehensive technical level of steel structures has reached the international advanced level. However, my country's steel structure industry still lags far behind developed countries in terms of informatization, automation, standardization, and scientific research and innovation. Whether the steel structure industry in our country can make a heal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G01N29/30
CPCG01N29/30G01N2291/0234
Inventor 李述亭林华骆群黄群安振帮傅俊磊丁勇马再生方军胡玥杨恒范志荣肖玮郑勇军
Owner 浙江方圆金属材料检测有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com