Low-carbon low-boron low-chromium alloy steel, and preparation method thereof

A carbon-low-boron, alloy steel technology, applied in the field of low-carbon, low-boron, low-chromium alloy steel and its preparation, can solve the problems of high brittleness, poor toughness, and easy damage of alloy steel, and achieve increased hardness, increased strength, Effect of preventing temper brittleness

Inactive Publication Date: 2018-12-07
LESHAN TAIGANG SUNKOS MACHINERY MFG
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The manufacturing method of the high-strength and high-toughness alloy steel disclosed in this patent document is produced with medium carbon steel. Although the hardness is high, the toughness is poor, and the prepared alloy steel is relatively brittle. When used to beat pebbles, the alloy steel is easily damaged.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-carbon low-boron low-chromium alloy steel, and preparation method thereof
  • Low-carbon low-boron low-chromium alloy steel, and preparation method thereof
  • Low-carbon low-boron low-chromium alloy steel, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Low-carbon, low-boron, low-chromium alloy steel is composed of the following raw materials in weight percentage:

[0032]

Embodiment 2

[0034] Low-carbon, low-boron, low-chromium alloy steel is composed of the following raw materials in weight percentage:

[0035]

[0036]

[0037] The low-carbon, low-boron, low-chromium wear-resistant alloy steel composed of the above components has the best wear resistance and impact toughness.

Embodiment 3

[0039] Low-carbon, low-boron, low-chromium alloy steel is composed of the following raw materials in weight percentage:

[0040]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a low-carbon low-boron low-chromium alloy steel, and a preparation method thereof, and belongs to the technical field of alloy steel manufacturing. According to the preparationmethod, low-carbon low-boron low-chromium materials are combined with cerium rare earth, vanadium, tungsten, copper, tantalum, cobalt, niobium, and the like, technical target value determination, material preparation, melting, sampling adjusting, casting moulding, and heat treatment are carried out so as to obtain the low-carbon low-boron low-chromium alloy steel at last; the hardness is HRC42-52, the impact energy is as high as 11 to 20 joules. The preparation method is capable of guaranteeing the certain hardness of the alloy steel, and at the same time, improving the impact resistance, thetoughness, and the wear resistance greatly.

Description

technical field [0001] The invention relates to the technical field of alloy steel manufacture, in particular to a low-carbon, low-boron, low-chromium alloy steel with high toughness and wear resistance and a preparation method thereof. Background technique [0002] Alloy steel is an iron-carbon alloy formed by adding an appropriate amount of one or more alloying elements to ordinary carbon steel. According to the different elements added and appropriate processing technology, special properties such as high strength, high toughness, wear resistance, corrosion resistance, low temperature resistance, high temperature resistance, and non-magnetic properties can be obtained. According to the content of alloy elements in steel, it can be divided into low alloy steel, medium alloy steel and high alloy steel. The main alloying elements of alloy steel are silicon, manganese, chromium, nickel, molybdenum, tungsten, vanadium, titanium, niobium, zirconium, cobalt, aluminum, copper, b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/44C22C38/46C22C38/42C22C38/48C22C38/50C22C38/52C22C38/54C22C38/02C22C38/04C22C38/06C22C33/04C21D6/00
CPCC22C38/44C21D6/004C21D6/005C21D6/007C21D6/008C22C33/04C22C38/005C22C38/008C22C38/02C22C38/04C22C38/06C22C38/42C22C38/46C22C38/48C22C38/50C22C38/52C22C38/54
Inventor 陈章华陈瑾昱张昌华
Owner LESHAN TAIGANG SUNKOS MACHINERY MFG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com