Black metal water-based antirust agent

A water-based anti-rust agent, ferrous metal technology, applied in the coating process of metal materials, etc., can solve the problems that ferrous metals cannot provide good anti-rust performance, and the effect of anti-rust agent is general

Inactive Publication Date: 2018-12-14
广州市融宽科技有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Corrosion is one of the main forms of damage to metal products. In order to avoid corrosion and reduce losses, people have adopted various methods. Among them, using antirust agents to protect metal products is one of the most common protection methods at present. The antirust agents in the prior art are generally effective and cannot provide good antirust performance for ferrous metals

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A water-based antirust agent for ferrous metals proposed by the present invention comprises the following raw materials in parts by weight: 7 parts of ethanolamine, 1 part of dodecane tribasic acid, 0.5 part of boric acid, 2 parts of sedimentation agent, 0.3 part of anti-hard water agent, corrosion inhibitor 1 part of antifoaming agent, 0.5 part of defoamer, 1 part of trisodium phosphate, 1 part of sodium tripolyphosphate, 2 parts of sodium hydroxide, 0.3 part of sodium molybdate, 2 parts of benzotriazole, 0.5 part of complexing agent, oxidation 2 parts of zinc, 1 part of sodium benzoate, 0.2 parts of dibutyl phthalate.

[0022] Its preparation method comprises the following steps:

[0023] S1, Weigh ethanolamine and dodecane tribasic acid according to the proportion of the parts, divide the ethanolamine into two equal parts, put one part of ethanolamine and dodecane tribasic acid into the reaction kettle, and continue to Stir for 5 hours to make it completely react un...

Embodiment 2

[0028] A water-based antirust agent for ferrous metals proposed by the present invention comprises the following raw materials in parts by weight: 8 parts of ethanolamine, 1.1 parts of dodecane tribasic acid, 0.6 part of boric acid, 2.2 parts of sedimentation agent, 0.4 part of anti-hard water agent, corrosion inhibitor 1.2 parts of antifoaming agent, 0.6 parts of defoaming agent, 1.1 parts of trisodium phosphate, 1.5 parts of sodium tripolyphosphate, 2.5 parts of sodium hydroxide, 0.4 parts of sodium molybdate, 3 parts of benzotriazole, 0.7 parts of complexing agent, oxidation 2.2 parts of zinc, 1.5 parts of sodium benzoate, and 0.4 parts of dibutyl phthalate.

[0029] Its preparation method comprises the following steps:

[0030] S1, Weigh ethanolamine and dodecane tribasic acid according to the proportion of the parts, divide the ethanolamine into the same two parts, put one part of ethanolamine and dodecane tribasic acid into the reaction kettle, and continue at a temperat...

Embodiment 3

[0035] A water-based antirust agent for ferrous metals proposed by the present invention comprises the following raw materials in parts by weight: 9 parts of ethanolamine, 1.3 parts of dodecane tribasic acid, 0.9 part of boric acid, 2.5 parts of sedimentation agent, 0.5 part of anti-hard water agent, corrosion inhibitor 1.5 parts of agent, 0.7 parts of defoamer, 1.3 parts of trisodium phosphate, 2 parts of sodium tripolyphosphate, 3 parts of sodium hydroxide, 0.6 parts of sodium molybdate, 3.5 parts of benzotriazole, 1 part of complexing agent, oxidation 2.5 parts of zinc, 2 parts of sodium benzoate, 0.6 parts of dibutyl phthalate.

[0036] Its preparation method comprises the following steps:

[0037] S1, Weigh ethanolamine and dodecane tribasic acid according to the proportion of the parts, divide the ethanolamine into two identical parts, put one part of ethanolamine and dodecane tribasic acid into the reaction kettle, and continue to Stir for 6 hours to make it completely...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a black metal water-based antirust agent. The black metal water-based antirust agent comprises the following raw materials in parts by weight: 7 to 12 parts of ethanol amine, 1to 1.5 parts of dodecyl tribasic acid, 0.5 to 1.5 parts of boric acid, 2 to 3 parts of a settling agent, 0.3 to 0.7 part of a hard water resistant agent, 1 to 2 parts of a corrosion inhibitor, 0.5 to1 part of a defoaming agent, 1 to 1.5 parts of trisodium phosphate, 1 to 3 parts of sodium tripolyphosphate, 2 to 4 parts of sodium hydroxide, 0.3 to 0.9 part of sodium molybdate, 2 to 5 parts of benzotriazole, 0.5 to 1.5 parts of a complexing agent, 2 to 3 parts of zinc oxide, 1 to 3 parts of sodium benzoate and 0.2 to 1 part of dibutyl phthalate. The black metal water-based antirust agent has agood antirust function, also has a certain cleaning effect and is suitable for popularizing.

Description

technical field [0001] The invention relates to the technical field of antirust agents, in particular to a water-based antirust agent for ferrous metals. Background technique [0002] Metal is a material with luster, good electrical conductivity, thermal conductivity and mechanical properties, and a positive temperature coefficient of resistance. Metals are a big family, and there are 86 kinds of metals in the world. Usually people divide metals into ferrous metals and non-ferrous metals according to their characteristics such as color and properties. Ferrous metals mainly refer to iron, manganese, chromium and their alloys, such as steel, pig iron, ferroalloy, cast iron, etc. [0003] Corrosion is one of the main forms of damage to metal products. In order to avoid corrosion and reduce losses, people have adopted various methods. Among them, using antirust agents to protect metal products is one of the most common protection methods at present. The antirust agents in the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23C22/42
CPCC23C22/42
Inventor 张隽
Owner 广州市融宽科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com