Concrete dyeing and sealing material

A sealing material and concrete technology, applied in the field of building materials, can solve the problems of inability to improve concrete pores, affect the service life of concrete, and single color of ordinary concrete, and achieve the effects of strong tinting strength, easy reaction and good dispersion.

Pending Publication Date: 2018-12-18
傅修丽
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the increasing demand for concrete diversification, people began to gradually pursue durable and beautiful products. Ordinary concrete has a single color, which limits its application in construction engineering to a certain extent.
Today's colored concrete products are developing rapidly, but the current colored concrete can't improve the defects of concrete's own porous holes, and its durability has not been ideal, which affects the service life of concrete, and the durability of color is not good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A concrete dyeing and sealing material is composed of the following raw materials in weight fractions: 2 parts of nano-zinc powder, 0.1 part of suspension stabilizer, 2 parts of sodium lauryl alcohol succinic acid monoester sulfonate, nonylphenol polyoxyethylene (9) ether sulfonate 2 parts of succinate disodium salt, 1 part of alkanolamide succinic acid monoester disodium salt, 40 parts of pigment, 1 part of nano-zircon powder, 0.5 part of tetraethylamine perfluorooctane sulfonate, tetrapotassium pyrophosphate 1 part, the balance is water.

[0020] The suspension stabilizer is propylene glycol alginate.

[0021] The pigment is compounded by organic coloring material and inorganic pigment.

Embodiment 2

[0023] A concrete dyeing sealing material is composed of the following raw materials in weight fractions: 10 parts of nano-zinc powder, 0.01 part of suspension stabilizer, 5 parts of sodium lauryl alcohol succinic acid monoester sulfonate, nonylphenol polyoxyethylene (9) ether sulfonate 1 part of succinate disodium salt, 3 parts of alkanolamide succinic acid monoester disodium salt, 20 parts of pigment, 5 parts of nano-zircon powder, 0.1 part of tetraethylamine perfluorooctane sulfonate, tetrapotassium pyrophosphate 2 parts, the balance being water.

[0024] The particle size of the nanometer zinc powder is 3-5 um.

[0025] The suspension stabilizer is carboxymethyl starch ether.

[0026] The pigment is compounded by azo coloring material and iron oxide.

Embodiment 3

[0028] A concrete dyeing and sealing material is composed of the following raw materials in weight fractions: 8 parts of nano-zinc powder, 0.08 parts of suspension stabilizer, 4 parts of sodium lauryl alcohol succinic acid monoester sulfonate, nonylphenol polyoxyethylene (9) ether sulfonate 1.7 parts of succinate disodium salt, 2 parts of alkanolamide succinic acid monoester disodium salt, 30 parts of pigment, 4 parts of nano-zircon powder, 0.4 part of tetraethylamine perfluorooctane sulfonate, tetrapotassium pyrophosphate 1.2 parts, the balance is water.

[0029] The suspension stabilizer is composed of propylene glycol alginate and guar gum hydroxypropyltrimethylammonium chloride in a weight ratio of 1:1.

[0030] The pigment is compounded by phthalocyanine coloring material and chromium oxide pigment.

[0031] The particle size of the nano-zircon powder is 2-8 um.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Belonging to the technical field of building materials, the invention specifically relates to a concrete dyeing and sealing material, which consists of the following raw materials by weight: 2-10 parts of nano-zinc powder, 0.01-0.1 part of a suspension stabilizer, 2-5 parts of sodium lauryl mono succinate sulfonate, 1-2 parts of disodium nonylphenol polyoxyethylene (9) ether sulfosuccinate, 1-3 parts of disodium alkanolamide mono succinate, 20-40 parts of pigment, 1-5 parts of nano-zircon powder, 0.1-0.5 part of tetraethylammonium perfluorooctanesulfonate, 1-2 parts of tetrapotassium pyrophosphate, and the balance water. The concrete dyeing and sealing material provided by the invention is a novel product integrating concrete dyeing and sealing, and has the characteristics of simple preparation process, easily controllable reaction and convenient use.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a concrete dyed sealing material. Background technique [0002] Concrete is a mixture prepared by adding water to cement, mineral admixtures, sand, stones, admixtures, etc. in an appropriate proportion. It has the advantages of economy, durability, fire resistance, and high compression resistance. It is the most widely used man-made Building materials are widely used in various structural projects. With the increasing demand for concrete diversification, people began to gradually pursue durable and beautiful products. Ordinary concrete has a single color, which limits its application in construction projects to a certain extent. The development of today's colored concrete products is rapid, but the current colored concrete cannot improve the defects of the concrete's own porous holes, and the durability has not been ideal, which affects the service life of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/69
CPCC04B41/515C04B41/69C04B41/5042C04B41/46C04B41/4896C04B41/5015C04B41/4803C04B41/4539C04B41/5036C04B41/5033
Inventor 傅修丽
Owner 傅修丽
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com