Copper-based antibacterial masterbatch and preparation method thereof

An antibacterial masterbatch, copper-based technology, applied in the manufacture of rayon, single-component polyolefin rayon, single-component polyester rayon, etc. It can solve the problems of complex granulation process, etc., to achieve the effect of low cost, difficult to control color and lasting effect.

Active Publication Date: 2018-12-28
晋大纳米科技(厦门)有限公司
View PDF15 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to overcome the complex process and high cost of obtaining antibacterial masterbatch through esterification, and the direct mixing and granulation of copper will cause the color of fiber fabric to be difficult to control, and provide a copper-based antibacterial masterbatch and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] A preparation method of copper-based antibacterial masterbatch, the specific steps are:

[0044] Dissolve 9.9g cuprous chloride in deionized water, add 50g mesoporous zirconium silicate to soak and absorb at room temperature for 1 day, then add 0.2mol sodium thiosulfate solution, the solution is 31.6g sodium thiosulfate and 20.4g Sodium metaphosphate is mixed with water, reacted for 2 hours, and then heated and dried to obtain cuprous-loaded zirconium silicate powder.

[0045] 70 parts by weight of carrier resin PET, 15 parts by weight of dispersant phosphate ester and 10 parts by weight of processing aid chlorinated polyethylene were added in proportion to the high-speed mixer and mixed for 15 minutes, and then added effective copper with a proportion of 5 parts by weight The zirconium silicate powder loaded with cuprous is pelletized by a twin-screw extruder at an extrusion temperature of 130-300°C to obtain copper-based antibacterial master batches. The fiber is made acc...

Embodiment 2

[0047] A preparation method of copper-based antibacterial masterbatch, the specific steps are:

[0048] Dissolve 9.9g cuprous chloride in deionized water, add 50g mesoporous zirconium silicate to soak and absorb at room temperature for 1 day, then add 0.2mol sodium thiosulfate solution, the solution is 31.6g sodium thiosulfate and 20.4g Sodium metaphosphate is mixed with water, reacted for 2 hours, and then heated and dried to obtain cuprous-loaded zirconium silicate powder.

[0049] Add 65 parts by weight of carrier resin PP, 20 parts by weight of dispersant silicate and 10 parts by weight of processing aid MBS (methyl methacrylate, butadiene, styrene terpolymer) into the high-speed mixer in proportion 15min after mixing, add 5 parts by weight of cuprous zirconium silicate powder with effective copper ratio and mix, use twin-screw extruder to pelletize, extrusion temperature 130-220℃, then copper antibacterial masterbatch is obtained . The fiber is made according to the conventi...

Embodiment 3

[0051] A preparation method of copper-based antibacterial masterbatch, the specific steps are:

[0052] Dissolve 22.3g cuprous sulfate in deionized water, add 126g mesoporous zirconium silicate to soak and absorb at room temperature for 2 days, then add 0.5mol sodium thiosulfate solution, which is 79g sodium thiosulfate and 16g sodium metaphosphate It is mixed with water, reacted for 3 hours, and then heated and dried to obtain cuprous-loaded zirconium silicate powder.

[0053] Add 80 parts by weight of carrier resin PBT, 15 parts by weight of dispersant isopropanol and 10 parts by weight of processing aid MBS (methyl methacrylate, butadiene, styrene terpolymer) into a high-speed mixer in proportion After 15 minutes, add cuprous zirconium silicate powder with an effective copper ratio of 10 parts by weight, and pelletize with a twin-screw extruder at an extrusion temperature of 220-300°C to obtain a copper-based antibacterial masterbatch . The fiber is made according to the conve...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
antibacterial rateaaaaaaaaaa
antibacterial rateaaaaaaaaaa
antibacterial rateaaaaaaaaaa
Login to view more

Abstract

The invention relates to a copper-based antibacterial masterbatch and a preparation method thereof. The preparation method comprises the steps of mixing a soluble cuprous salt with water, adding mesoporous zirconium silicate to perform immersion adsorption to obtain a mixture; mixing and adding thiosulfate, metaphosphate and water into the obtained mixture, performing drying after the reaction, and obtaining cuprous ion-loaded zirconium silicate powder; mixing a carrier resin, a dispersing agent, a processing aid and the cuprous ion-loaded zirconium silicate powder and then performing extrusion pelleting, and obtaining the copper-based antibacterial masterbatch. A fiber obtained according to a conventional spinning process by the copper-based antibacterial masterbatch obtained through themethod has excellent antibacterial property and not only has good oxidation resistance, but also has excellent washing resistance, the preparation method is simple and convenient to operate, efficient, low in cost and lasting in effect and has a broad application prospect.

Description

Technical field [0001] The invention relates to the field of preparation of antibacterial masterbatch fibers, in particular to copper-based antibacterial masterbatch and a preparation method thereof. Background technique [0002] Today's social extreme environment, environmental pollution and other ecological environments are seriously deteriorating, and special living micro-environments such as confined spaces have led to an urgent need for functional protective textiles. Taking antibacterial properties as an example, textiles are prone to breeding microorganisms. The microbial communities in nature are widely present in the surrounding environment, and can grow quickly once they encounter suitable humidity, nutrients and temperature. The microorganisms breeding on textiles not only affect the wearability of textiles, but also damage the health of users. Therefore, how to inhibit or kill microorganisms attached to textiles is an urgent problem in the textile industry. Antibac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/92D01F1/10D01F6/46D01F6/54D01F6/90
CPCD01F1/103D01F6/46D01F6/54D01F6/90D01F6/92
Inventor 吴永鑫胡必忠钟元杰康朝晖
Owner 晋大纳米科技(厦门)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap