Enhanced heat-resistant automobile glass

A kind of automotive glass, enhanced technology, applied in the field of glass materials, can solve the problems of poor heat resistance, unbearable human body, harmful to health, etc., to achieve the effect of blocking sunlight, protecting from damage, and long service life

Inactive Publication Date: 2019-01-04
景有超
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the car glass on the market has poor heat resistance effect, especially in summer, when the ultraviolet rays are strong, driving outside for a long time will damage the skin, which is unbearable for the human body and harmful to health.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A reinforced heat-resistant automotive glass, which is prepared from the following components in parts by weight: 3-13 parts of borax, 2-10 parts of sodium hydroxide, 1-7 parts of limestone, 2-8 parts of glass fiber, carbon dioxide 15-25 parts of silicon, 2-10 parts of steel fiber, 3-8 parts of calcium carbonate, 1-2 parts of sodium chloride, 2-8 parts of zinc oxide, 3-13 parts of sodium carbonate, 2-12 parts of curing agent, silicon Calcium acid 5-9 parts.

[0014] Further, the curing agent is polymethyl acrylate resin, polyethyl methacrylate or polybutyl acrylate resin.

[0015] Further, the silica is 1000-1200 mesh silica.

[0016] Further, 2-5 parts of magnesium oxide are also included.

[0017] Further, 2-5 parts of phosphorus pentoxide are also included.

Embodiment 2

[0019] A reinforced heat-resistant automotive glass, prepared from the following components in parts by weight: 13 parts of borax, 10 parts of sodium hydroxide, 7 parts of limestone, 8 parts of glass fiber, 25 parts of silicon dioxide, and 10 parts of steel fiber , 8 parts of calcium carbonate, 2 parts of sodium chloride, 8 parts of zinc oxide, 13 parts of sodium carbonate, 12 parts of curing agent, and 9 parts of calcium silicate.

[0020] Further, the curing agent is polymethyl acrylate resin, polyethyl methacrylate or polybutyl acrylate resin.

[0021] Further, the silica is 1200 mesh silica.

[0022] Further, 5 parts of magnesium oxide are also included.

[0023] Further, 5 parts of phosphorus pentoxide are also included.

Embodiment 3

[0025] A reinforced heat-resistant automotive glass, prepared from the following components in parts by weight: 3 parts of borax, 2 parts of sodium hydroxide, 1 part of limestone, 2 parts of glass fiber, 15 parts of silicon dioxide, and 2 parts of steel fiber , 3 parts of calcium carbonate, 1 part of sodium chloride, 2 parts of zinc oxide, 3 parts of sodium carbonate, 2 parts of curing agent, 5 parts of calcium silicate.

[0026] Further, the curing agent is polymethyl acrylate resin, polyethyl methacrylate or polybutyl acrylate resin.

[0027] Further, the silica is 1000 mesh silica.

[0028] Further, 2 parts of magnesium oxide are also included.

[0029] Further, 2 parts of phosphorus pentoxide are also included.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to enhanced heat-resistant automobile glass, and belongs to the technical field of glass materials. The glass is prepared from, by weight, 3-13 parts of borax, 2-10 parts of sodium hydroxide, 1-7 parts of limestone, 2-8 parts of glass fiber, 15-25 parts of silicon dioxide, 2-10 parts of steel fiber, 3-8 parts of calcium carbonate, 1-2 parts of sodium chloride, 2-8 parts of zinc oxide, 3-13 parts of sodium carbonate, 2-12 parts of curing agent and 5-9 parts of calcium silicate. The prepared automobile glass has the advantages of being high in structural strength, long in service life and the like, the problem that breakage occurs in the using process is avoided, the structural strength of the glass material is enhanced, the service life is prolonged, and the glass hashigh strength and can resist strong impact, effectively prevent sun irradiation and protect skin from being harmed.

Description

technical field [0001] The invention relates to a glass material, in particular to a reinforced heat-resistant automobile glass, which belongs to the technical field of glass materials. Background technique [0002] Automobile glass is indispensable in the accessories of automobile body, and mainly plays a protective role. There are three main types of automotive glass: laminated glass, tempered glass and area tempered glass, which can withstand strong impact. Automobile glass is divided into four types according to its location: front windshield, side window glass, rear windshield glass and sunroof glass. The national mandatory regulations for the front windshield must be laminated glass, the side window glass is tempered glass, and the rear windshield is generally tempered glass with electric heating wire. The current automotive glass on the market has poor heat resistance, especially in summer, when the ultraviolet rays are strong, and driving outside for a long time wi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C14/00C03C6/06C03C4/08
CPCC03C14/002C03C1/00C03C4/085C03C2201/60
Inventor 景有超
Owner 景有超
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com