Concrete material containing active additive

An active additive and concrete technology, which is applied in the field of concrete materials, can solve the problems of insufficient mechanical strength and impermeability, achieve good water blocking effect, enhance impermeability, and improve the effect of cracking and seepage again

Active Publication Date: 2019-01-04
ANHUI POLYTECHNIC UNIV MECHANICAL & ELECTRICAL COLLEGE
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a concrete material containing active additives, which solves the problem of insufficient overall mechanical strength and impermeability of traditional concrete materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Concrete material containing active additive
  • Concrete material containing active additive
  • Concrete material containing active additive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The waterproof material is prepared according to the above preparation method, wherein the concrete material includes the following raw material components by weight: 100 parts of Portland cement, 0.4 parts of active additives, 15 parts of sodium silicate, 50 parts of quartz sand and 110 parts of water The weight ratio of material A, material B and material C is: 0.2:2:10; in material A, the weight ratio of allophane and potassium carbonate is 1:0.11; the weight percent content of each component in the material B are: 10% of tartaric acid, 0.5% of maleic acid, 0.3% of ammonium formate, 40% of calcium metaaluminate, 0.4% of oxalic acid, 4% of sodium tartrate and the balance of calcium chloride; the weight of each component in the material C The percentage content is: sodium silicate 4%, sodium citrate 3%, zinc formate 0.5%, calcium carbonate 2%, potassium carbonate 5%, sodium acetate trihydrate 2%, calcium formate 0.2%, calcium metaaluminate 32% and balance calcium chlor...

Embodiment 2

[0033]The waterproof material is prepared according to the above-mentioned preparation method, wherein the concrete material comprises the following raw material components in parts by weight: 100 parts of Portland cement, 0.6 parts of active additives, 22 parts of sodium silicate, 55 parts of quartz sand and 120 parts of water The weight ratio of material A, material B and material C is: 0.6:4:10; in material A, the weight ratio of allophane and potassium carbonate is 1:0.13; the weight percent content of each component in the material B are: 13% of tartaric acid, 0.7% of maleic acid, 0.5% of ammonium formate, 49% of calcium metaaluminate, 0.6% of oxalic acid, 7% of sodium tartrate and the balance of calcium chloride; the weight of each component in the material C The percentage content is: sodium silicate 7%, sodium citrate 6%, zinc formate 0.7%, calcium carbonate 6%, potassium carbonate 7%, sodium acetate trihydrate 6%, calcium formate 0.5%, calcium metaaluminate 35% and ba...

Embodiment 3

[0035] The waterproof material is prepared according to the above preparation method, wherein the concrete material includes the following raw material components by weight: 100 parts of Portland cement, 0.8 parts of active additives, 30 parts of sodium silicate, 60 parts of quartz sand and 130 parts of water ; The weight ratio of material A, material B and material C is: 0.8:5:10; in material A, the weight ratio of allophane and potassium carbonate is 1:0.14; the weight percent content of each component in the material B It is: 15% of tartaric acid, 0.9% of maleic acid, 0.8% of ammonium formate, 55% of calcium metaaluminate, 0.8% of oxalic acid, 9% of sodium tartrate and the balance of calcium chloride; the weight of each component in the material C The percentage content is: sodium silicate 10%, sodium citrate 8%, zinc formate 0.9%, calcium carbonate 8%, potassium carbonate 9%, sodium acetate trihydrate 8%, calcium formate 0.8%, calcium metaaluminate 38% and balance calcium ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a concrete material containing an active additive. The concrete material comprises Portland cement, the active additive, sodium silicate, quartz sand and water, wherein the active additive comprises material A, material B and material C; the material A is made with allophane and potassium carbonate; the material B is made with tartaric acid, maleic acid, ammonium formate, calcium metaaluminate, oxalic acid, sodium tartrate and calcium chloride; the material C is made with sodium silicate, sodium citrate, zinc formate, calcium carbonate, potassium carbonate, sodium acetate trihydrate, calcium formate, calcium metaaluminate and calcium chloride. The problem that traditional concrete material has insufficient overall mechanical strength and anti-permeability performance is solved.

Description

technical field [0001] The invention relates to the field of concrete materials, in particular to a concrete material containing active additives. Background technique [0002] The waterproof material is the building envelope to prevent the infiltration of rainwater, snow and groundwater; to prevent the erosion of moisture, steam and other harmful gases and liquids in the air; the partition structure to prevent the seepage of water supply and drainage. These materials that are resistant to penetration, leakage and erosion are collectively referred to as. For example, the invention with the patent number CN2017100474779 discloses a cement-based permeable crystalline waterproofing agent, which includes the following components by weight: 570-630 parts of Portland cement; 275-325 parts of quartz sand; 95 parts of fly ash -105 parts; 2-17 parts of water reducing agent; 80-95 parts of osmotic crystallization masterbatch; osmotic crystallization masterbatch includes sodium metasi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B111/27
CPCC04B28/04C04B2111/00293C04B2111/27C04B2201/50C04B12/04C04B14/06C04B14/041C04B22/10C04B24/06C04B24/04C04B24/12C04B22/085C04B22/124C04B14/28
Inventor 赵浩峰张椿英夏俊陈姗姗韩海东岳浩
Owner ANHUI POLYTECHNIC UNIV MECHANICAL & ELECTRICAL COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap