Bathroom floor tile adhesive, preparation method and application in anti-leakage construction

An adhesive, toilet technology, applied in the direction of adhesive type, chitin adhesive, hyaluronic acid adhesive, etc., to achieve the effect of reducing VOC content

Active Publication Date: 2020-06-16
南京嘉怡装饰设计有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, in the prior art, there is hardly any report using hydrogel as a floor tile adhesive, and most of them are still traditional cement mortar adhesives, such as a high-strength hydrogel provided by the Chinese patent of CN 104150849 A. The main component of adhesive is silicate clinker and fly ash; Another example is that the main raw material of the waterproof color caulking adhesive for construction provided by the Chinese patent of CN 100558840 C is also cement and quartz sand

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bathroom floor tile adhesive, preparation method and application in anti-leakage construction
  • Bathroom floor tile adhesive, preparation method and application in anti-leakage construction

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] A bathroom tile adhesive comprising hyaluronic acid and lysine-glycine dipeptide.

[0048] The preparation method of the bathroom floor tile adhesive is as follows:

[0049] (1) prepare 3wt% hyaluronic acid aqueous solution;

[0050] (2) preparing 18wt% lysine-glycine dipeptide aqueous solution;

[0051] (3) mixing an equal volume of hyaluronic acid aqueous solution and lysine-glycine dipeptide aqueous solution to obtain a mixed solution;

[0052] (4) Add methyl o-benzoylbenzoate and irradiate with ultraviolet light for 2 minutes to obtain the adhesive;

[0053] The amount of methyl phthaloylbenzoate added is 0.7% of the mixed solution quality;

[0054] The ultraviolet light irradiation intensity is 6.9mW / cm 2 ;

[0055] The wavelength of the ultraviolet light is 360nm.

[0056] A method for using a toilet floor tile adhesive, that is, a toilet floor anti-leakage construction process, comprising the following steps:

[0057] (1) The ground is poured with cement s...

Embodiment 2

[0072] A bathroom floor tile adhesive comprising hyaluronic acid and glycyl-glycyl-L-leucine.

[0073] The preparation method of described toilet floor tile adhesive is as follows:

[0074] (1) prepare 3wt% hyaluronic acid aqueous solution;

[0075] (2) preparing 18wt% glycyl-glycyl-L-leucine aqueous solution;

[0076] (3) mixing an equal volume of hyaluronic acid aqueous solution and glycyl-glycyl-L-leucine aqueous solution to obtain a mixed solution;

[0077] (4) Add methyl o-benzoylbenzoate and irradiate with ultraviolet light for 2 minutes to obtain the adhesive;

[0078] The amount of methyl phthaloylbenzoate added is 0.7% of the mixed solution quality;

[0079] The ultraviolet light irradiation intensity is 6.9mW / cm 2 ;

[0080] The wavelength of the ultraviolet light is 360nm.

[0081] The using method of described bathroom floor tile adhesive is identical with embodiment 1.

Embodiment 3

[0083] A bathroom floor tile adhesive comprising hyaluronic acid and glycyl-glycyl-L-leucine.

[0084] The preparation method of described toilet floor tile adhesive is as follows:

[0085] (1) prepare 3wt% hyaluronic acid aqueous solution;

[0086] (2) preparing 18wt% glycyl-glycyl-L-leucine aqueous solution;

[0087] (3) mixing an equal volume of hyaluronic acid aqueous solution and glycyl-glycyl-L-leucine aqueous solution to obtain a mixed solution;

[0088] (4) Add benzoin ethyl ether and irradiate with ultraviolet light for 2 minutes to obtain the adhesive;

[0089] The amount of added benzoin ethyl ether is 0.7% of the mixed solution quality;

[0090] The ultraviolet light irradiation intensity is 6.9mW / cm 2 ;

[0091] The wavelength of the ultraviolet light is 360nm.

[0092] The using method of described bathroom floor tile adhesive is identical with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
wavelengthaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention relates to a toilet floor tile adhesive, and belongs to the field of adhesive. The toilet floor tile adhesive comprises hyaluronic acid and a peptide compound, and the preparation methodcomprises the steps: (1) preparing a 2-4 wt% hyaluronic acid aqueous solution; (2) preparing a 10-30 wt% peptide compound aqueous solution; (3) mixing the hyaluronic acid aqueous solution and the peptide compound aqueous solution with equal volume to obtain a mixed solution; and (4) adding a photoinitiator and irradiating with ultraviolet light for 2-5 min, and thus obtaining the adhesive. The photoinitiator is preferred to be benzophenone compounds or benzoin derivatives. The toilet floor tile adhesive provided by the invention has good bonding strength, the original strength is as high as 1.57 MPa, and the strength can be improved to 1.75 MPa to a certain extent after the adhesive is soaked in water.

Description

technical field [0001] The invention belongs to the field of adhesives, in particular to an adhesive for bathroom floor tiles. Background technique [0002] In daily life, the bathroom is a place with a large water consumption and high water frequency, and water seepage in the bathroom is relatively common. The common problem of toilet leakage has become the main object of homeowners’ complaints about housing quality, seriously affecting the normal life of residents, not only easily causing neighborhood disputes, but also causing the safety of building structures to be returned and shortening the service life of buildings. [0003] In the anti-leakage construction process of the bathroom, the most important thing is the choice of waterproof coating and tile adhesive. Both of them use materials with better performance, which can not only waterproof but also have high tile adhesion As time goes by or the humidity of the environment changes, the degree of adhesion is reduced a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J105/08C09J11/06C09J11/00C09D183/04C09D7/63C09D7/62C09J125/14C09J11/08E04F15/02E04F15/18
CPCC09D7/62C09D7/63C09D183/04C09J11/00C09J11/06C09J11/08C09J105/08C09J125/14E04F15/0215E04F15/182E04F2290/04C08K5/175C08K5/5425C08K9/04C08K3/36C08L33/02C08K5/42C08K5/32
Inventor 曾兵
Owner 南京嘉怡装饰设计有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional