A kind of preparation method of conductive reinforced finger glove

A technology of gloves and conductive carbon black, which is applied in the field of preparation of conductive reinforced finger gloves, can solve the problems of stiff conductive gloves, easy hand fatigue, poor flex resistance, etc., achieve excellent protection performance and wear resistance, and feel Comfortable and soft, the effect of improving softness

Active Publication Date: 2021-04-02
SHANDONG XINGYU GLOVES
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the above-mentioned problems in the prior art, the present invention provides a method for preparing conductive reinforced finger gloves, which can effectively solve the problems of existing conductive gloves such as stiffness, poor flex resistance, and easy hand fatigue

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] Step 1. Conductive carbon black is prepared into conductive carbon black dispersion liquid, and its raw materials are mixed and stirred evenly according to the following proportions by mass: conductive carbon black: 100 parts, dispersant sodium methylene dinaphthalene sulfonate: 4 parts , titanate coupling agent TMC-311w: 5 parts, potassium hydroxide: 1.5 parts, water: 650 parts;

[0052] Step 2, prepare the latex dispersion liquid composite mucilage with pre-vulcanized latex and auxiliary materials, the mass parts of each component: 100 parts of natural latex, 2 parts of anti-frost emulsified paraffin, 2 parts of anti-sticking agent zinc stearate , 2 parts of potassium oleate, 1.5 parts of sodium polyacrylate, stop stirring when the stirring and foaming volume is 1.3 times, and the measured viscosity is 2000mpa s;

[0053] Step 3. Mix the above-mentioned conductive carbon black dispersion with latex to prepare a second-pass latex-conductive dispersion composite mucilag...

Embodiment 2

[0058] Step 1. Prepare the conductive carbon black into a conductive carbon black dispersion, and prepare the following raw materials according to the following mass parts, conductive carbon black: 100 parts, 2 parts of dispersant sodium dibutylnaphthalene sulfonate, titanate coupling agent TMC -101: 5 parts, 5 parts of potassium hydroxide, 600 parts of water; mix and stir evenly to obtain conductive carbon black dispersion;

[0059] Step 2, prepare a latex dispersion composite mucilage with pre-vulcanized nitrile and auxiliary materials, the mass parts of each component: 100 parts of nitrile latex, 2 parts of sodium polyacrylate, viscosity 2200mpa s;

[0060] Step 3, mixing the conductive carbon black dispersion obtained in step 1 with butyronitrile to prepare a second latex-conductive dispersion composite mucilage, the mass parts of each component: nitrile latex: 100 parts, conductive carbon black dispersion: 30 parts, 2% hydroxymethyl ethyl cellulose: 10 parts, the viscosit...

Embodiment 3

[0067] Step 1, prepare conductive carbon black into conductive carbon black dispersion, prepare the following raw materials according to the following mass parts, conductive carbon black: 90 parts, dispersant is sodium methylene dinaphthalene sulfonate and sodium dibutyl naphthalene sulfonate Mix according to the mass ratio of 1:1: 5 parts, titanate coupling agent TMC-201: 5 parts, water: 700 parts; mix and stir evenly to obtain the conductive carbon black dispersion;

[0068] Step 2, prepare the latex dispersion composite mucilage with pre-vulcanized neoprene latex and auxiliary materials, the mass parts of each component: 100 parts of neoprene latex, 3 parts of calcium stearate, 2 parts of carboxymethyl cellulose , viscosity 1800mpa·s;

[0069] Step 3, mix the conductive carbon black dispersion obtained in step 1 with neoprene latex to prepare a second-pass latex-conductive dispersion composite mucilage, the mass parts of each component: neoprene latex: 100 parts, conductive...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle size (mesh)aaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing an electrically conductive reinforced finger glove. The method comprises the following steps: firstly, preparing a conductive carbon black dispersion liquid, carrying out one-pass latex dispersion composite liquid slurry, and then mixing the conductive carbon black dispersion liquid with a presulfurized latex to prepare a two-pass latex dispersion composite liquid slurry, after a glove base is soaked in a coagulator, soaking in the one-pass latex dispersion composite liquid slurry, and then, a finger part soaking in the two-pass latex dispersioncomposite liquid slurry, then, performing prevulcanization and high-temperature vulcanization to obtain the conductive reinforced finger glove. The gloves provided by the invention can effectively reduce the production cost. And the gloves are soft and comfortable in use and flexible in fingers. At that same time, the insulation at the palm of the hand is also achieved, such as nitrile rubber gloves. When the thickness of the palm of the hand is 0.2 mm, the instantaneous breakdown voltage is 1.5 KV.

Description

technical field [0001] The invention relates to a preparation method of conductive reinforced finger gloves, which belongs to the technical field of labor protection products preparation. Background technique [0002] At present, there are two main types of conductive gloves on the market; one is to add conductive wire to the glove embryo to increase its conductivity; the other is to add conductive powder to the glue to increase conductivity; but both conductive gloves have Its disadvantage is that it is expensive to add conductive thread to the glove embryo, and the price is increased by 1.2 yuan / pay compared with ordinary gloves; if conductive powder is added to the rubber material, its price can be reduced, but the addition of conductive powder will make the glove stiff. The bending resistance is very poor, and the hands are prone to fatigue. Contents of the invention [0003] (1) Technical problems to be solved [0004] In order to solve the above-mentioned problems ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A41D19/04A41D19/015D06B3/30D06B23/04C08J5/02C08L7/02C08L9/04C08L11/02C08L9/08C08K3/04
CPCA41D19/015A41D19/04C08J5/02C08J2307/02C08J2309/04C08J2309/08C08J2311/02C08K3/04D06B3/30D06B23/04
Inventor 周星余孙永峰
Owner SHANDONG XINGYU GLOVES