Preparation method of high softening point pitch suitable for use as pitch-based spherical activated carbon raw material

A technology of high softening point asphalt and spherical activated carbon, which is applied in the direction of chemical processing of tar pitch/petroleum pitch/natural asphalt, etc., which can solve the long service life and the limitation of stirring motor power, which affects the development of asphalt-based spherical activated carbon, and the price is high No inferior problems, achieve the effect of shortening the oxidation reaction time, reducing the activation reaction time, and realizing continuous production

Active Publication Date: 2021-04-20
湖南曦威新材料有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this regard, the existing research or industry is to reduce the influence of the temperature field gradient distribution of the batch reactor by reducing the inner diameter of the reactor and extending the length of the reactor, but the length of the reactor will be affected by the length of the stirring rod, Service life and limitation of stirring motor power
Therefore, in order to realize the batch production of coal tar pitch with high softening point, multiple sets of batch reactors are used for parallel production, which takes up a large area, requires large equipment investment, low production capacity, and high labor costs, which eventually lead to high softening point coal tar pitch The price remains high, which affects the development of pitch-based spherical activated carbon

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Using rock asphalt with a softening point of 220°C as the raw material, other physical and chemical properties of the raw material are as follows: n-heptane soluble matter is 31.6%, toluene soluble matter is 53.3%, quinoline insoluble matter is 23.9%, pyridine insoluble matter is 14.4% %, ash is 4.5%. Use a roller crusher to crush 2000Kg rock asphalt into rock asphalt particles with a diameter of 0.6-2mm. A vacuum feeding system is used to transport 2000Kg of asphalt granules to the hopper of the twin-screw extruder, and the feeding speed of the loss-in-weight scale is adjusted to 200Kg / h. The temperature of the 10 heating temperature zones of the twin-screw extruder is set sequentially from the feed inlet: 200°C, 300°C, 330°C, 330°C, 330°C, 330°C, 330°C, 300°C, 250°C, 235°C; The temperature of the head of the twin-screw extruder is set to 230°C; a vacuum port is set at every 2 heating temperature zones, and all 4 vacuum ports are closed; the end of the twin-screw extr...

Embodiment 2

[0033] Set the temperature of the 10 temperature zones of the twin-screw extruder in [Example 1] from the feed inlet to: 200°C, 360°C, 360°C, 360°C, 360°C, 360°C, 360°C, 300°C, 280°C, 255°C; the head temperature of the twin-screw extruder is set at 250°C; all other process parameters remain unchanged. The properties of the prepared high softening point pitch are as follows: the yield is 91.3%, the softening point is 258°C, the n-heptane soluble matter is 8.6%, the toluene soluble matter is 25.7%, the quinoline insoluble matter is 38.1%, and the pyridine insoluble matter is 38.1%. Matter 29.2%, ash 6.1%.

Embodiment 3

[0035]Set the temperature of the 10 temperature zones of the twin-screw extruder in [Example 1] from the feed inlet to: 200°C, 360°C, 360°C, 360°C, 360°C, 360°C, 360°C, 300°C, 270°C, 265°C; the head temperature of the twin-screw extruder is set to 260°C; all 4 vacuum ports are opened, and the gauge pressure of the 4 vacuum devices is adjusted to -0.03MPa; all other process parameters remain unchanged. The properties of the prepared high softening point pitch are as follows: the yield is 84.3%, the softening point is 266°C, the soluble matter in n-heptane is 4.9%, the soluble matter in toluene is 22.3%, the insoluble matter in quinoline is 42.5%, and the pyridine insoluble matter is 42.5%. Matter 32.4%, ash 6.6%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing high-softening-point asphalt suitable for use as a raw material for asphalt-based spherical activated carbon. The invention uses special asphalt with a softening point of 130-220°C as a raw material, and utilizes the synergistic effect of negative pressure extraction-thermal polymerization reaction , adopt a twin-screw extruder with a certain number of vacuum ports and adjust the high softening point coal by adjusting the temperature of each temperature zone of the twin-screw extruder, the extrusion speed, the number and setting position of the vacuum ports, and the degree of vacuum Physical and chemical properties such as molecular weight distribution, softening point, and family composition of asphalt. The softening point of the prepared high softening point pitch is 240-280°C, the n-heptane soluble matter is less than 10%, the toluene soluble matter is lower than 30%, the quinoline insoluble matter is higher than 35%, and the pyridine insoluble matter is higher than 20%. %, ash content of 0.02 to 8%. The invention has great significance for promoting the recycling of special asphalt and the development of pitch-based spherical activated carbon and related materials (such as pitch-based foam carbon).

Description

technical field [0001] The invention relates to a low-cost preparation method of high softening point asphalt suitable for use as a pitch-based spherical activated carbon raw material, and belongs to a preparation method of high softening point asphalt with a softening point of 240-280°C. Background technique [0002] Military-civilian integration and ecological civilization construction have become national strategies, and there is an urgent demand for special adsorption materials in key national defense projects, high-tech weapons and equipment, medicine, electronics, air and water purification. [0003] Pitch-based spherical activated carbon is a kind of adsorption material, but its unique spherical structure and spherical diameter (0.2-1.5mm) make it better than ordinary granular activated carbon and columnar activated carbon in terms of packing density, mechanical strength, and adsorption and desorption methods. 1. Powder activated carbon has incomparable performance ad...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C10C3/02
CPCC10C3/02
Inventor 詹亮李国俊李才毅罗浩
Owner 湖南曦威新材料有限公司