A technology for synthetic rubber and stabilizer, applied in the field of synthetic rubber additive preparation, can solve the problems of easy volatility, low toxicity, non-volatile, high toxicity, etc., and achieves the effects of good stability, elimination of harm to the human body, and reduction of production costs.

Pending Publication Date: 2019-02-12
福建凯基高分子材料股份有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the deficiencies of the prior art, the present invention provides a stabilizer for synthetic rubber and a preparation method thereof, which has the advantages of low toxicity and low volatility in the production process, and solves the problem of high toxicity and high volatility in the production process of synthetic rubber at present.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The present invention proposes a method for preparing a stabilizer for synthetic rubber, comprising the steps of: taking a 500ml beaker, mixing 45g resin, 15g sodium polyacrylate, 7g polymer compound fat, 13g sodium linoleate, 7g sodium stearate, Mix 3g of hydrotalcite powder and 4g of muscovite powder, heat it, heat it at 85°C for 3min, and cut it with a high-speed shear for 3min at a speed of 1250 rpm. Add 6g of additives to it at a constant temperature, the plasticizer in the additive is dioctyl phthalate o, the blowing agent is hydrogenated chlorofluorocarbon blowing agent, and the crosslinking agent is dicumyl peroxide , the accelerator is dibenzothiazole disulfide, the antioxidant is butyl hydroxyanisole, and then it is stirred for 3 minutes, and naturally cooled to room temperature to obtain an emulsion-like stabilizer. Test results: the average particle size is 1.32μm, and the viscosity is 870CPS.

Embodiment 2

[0025] The present invention proposes a method for preparing a stabilizer for synthetic rubber, comprising the steps of: taking a 500ml beaker, mixing 50g resin, 10g sodium polyacrylate, 5g polymer compound fat, 15g sodium linoleate, 10g sodium stearate, Mix 3g of hydrotalcite powder and 4g of muscovite powder, heat it, heat it at 93°C for 3min, use a high-speed shearing machine for 3min at a speed of 1350 rpm, and heat it at 70°C The additive of 3g is added in it under the constant temperature, plasticizer is dioctyl phthalate in its additive, and foaming agent is hydrogenated chlorofluorocarbon foaming agent, and described linking agent is di-tert-butyl peroxide, The accelerator is thiuram monosulfide, the antioxidant is dibutylhydroxytoluene, and then it is stirred for 3 minutes, and naturally cooled to room temperature to obtain an emulsion-like stabilizer. Test results: the average particle size is 1.24μm, and the viscosity is 827CPS.

[0026] In summary, the synthetic r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
Viscosityaaaaaaaaaa
The average particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of preparation methods for synthetic rubber additives, and discloses a stabilizer for synthetic rubber. The stabilizer, with the total mass of 100%, is prepared from the following raw materials in parts by weight: 40-50% of resin, 10-20% of sodium polyacrylate, 5-10% of high-molecular complex liped, 10-15% of sodium linoleate, 5-10% of sodium stearate,3-5% of hydrotalcite powder, 4-6% of white mica powder and the balance an additive, wherein the additive, with the total weight of 100 g, is prepared from the following raw materials in parts by weight: 40 g of a plasticizer, 20 g of a foaming agent, 10 g of a cross-linking agent, 15 g of an accelerant and 15 g of an antioxidant, the plasticizer is any one of dioctyl phthalate I and dioctyl phthalate II, the foaming agent is any one of a hydrogenated chlorofluorocarbon foaming agent I and a hydrogenated chlorofluorocarbon foaming agent II, and the cross-linking agent is any one of dicumyl peroxide and di-tert-butyl peroxide. The stabilizer for the synthetic rubber has the advantage that the problems that synthetic rubber is large in toxicity and easy to volatilize in the existing syntheticrubber production process can be solved.

Description

technical field [0001] The invention relates to the technical field of preparation methods of synthetic rubber additives, in particular to a synthetic rubber stabilizer and a preparation method thereof. Background technique [0002] Generally speaking, rubber stabilizer generally refers to the vulcanization catalyst of rubber. Because natural rubber is soft and difficult to be molded and used, it needs to be vulcanized or plasticized. The role of this stabilizer is to promote rubber vulcanization and increase The degree of vulcanization, PVC resin is a polar non-crystalline high polymer, there is a strong force between molecules, it is a hard and brittle material. PVC resin (PVC) is one of the important organic synthetic materials. English name: Polyvinyl Chloride, chemical structural formula: (CH2-CHCL)n, its products have good physical and chemical properties, and are widely used in industry, construction, agriculture, daily life, packaging, electric power, public utiliti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L101/00C08L33/02C08K13/02C08K5/098C08K3/26C08K3/34C08L21/00C08J9/14
CPCC08J9/0023C08J9/0061C08J9/0066C08J9/0095C08J9/144C08J2321/00C08J2400/00C08J2433/02C08L21/00C08L101/00C08L33/02C08K13/02C08K5/098C08K3/26C08K3/34
Inventor 张文俊张文显于清林
Owner 福建凯基高分子材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap