Continuous nanometer TiO2 surface treatment method

A surface treatment and nanotechnology, applied in the field of continuous nano-TiO2 surface treatment, can solve the problems of poor compatibility and limited application of nano-TiO2, and achieve the effects of reducing agglomeration, excellent photostability, and good hydrophobicity

Inactive Publication Date: 2019-02-12
江苏河海纳米科技股份有限公司
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Through inorganic coating (generally using soluble inorganic salts and ions themselves on nano-TiO 2 The flocculation and agglomeration have a certain influence) to solve the problem of photoactivity and agglomeration; through organic modification to solve the disadvantages of poor compatibility in the organic phase; and they are often viewed in isolation, and there are few organic combinations of them up to study
For example: Chinese patent CN1454939A will nano-TiO 2 The slurry is maintained at a certain temperature at a certain pH value, and at the same time, sodium aluminate solution and sulfuric acid solution are added dropwise to coat alumina on its surface, without involving nano-TiO 2 organic surface treatment
And Chinese patent CN1982349A uses tetrabutyl titanate to nano-TiO 2 Surface pretreatment followed by surface polymerization with methyl methacrylate, although improved nano-TiO 2 Dispersion and stability in the organic phase, but due to the lack of inorganic surface treatment, resulting in nano-TiO 2 The field of application is very limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] 1 kg of freeze-dried nano-TiO 2 Add ethanol and water with a mass ratio of 1:1 to the powder, a total of 5 kg, raise the temperature to 55 °C, and adjust the pH of the system to 8. Then add 0.535 kg containing 0.05kg SiO 2 Aqueous ethanol solution of ethyl orthosilicate, stirred evenly, and kept at this temperature and pH for 5.5 h. Filtration, washing, drying, and crushing to obtain nano-TiO with inorganic silicon surface treatment 2 powder.

Embodiment 2

[0026] 1 kg of freeze-dried nano-TiO 2 Add 5 kg of ethanol and water with a mass ratio of 1:1 to the powder, raise the temperature to 55 °C, and adjust the pH of the system to 8. Then add 0.535 kg containing 0.05kg SiO 2 Tetraethyl orthosilicate ethanol aqueous solution, stirred evenly, and kept at this temperature and pH for 5.5 h. Then add 1.2 kg of ethanol aqueous solution containing 0.06 kg of polydimethylsiloxane, stir evenly, and keep the reaction at the temperature and pH for 0.5 h. After the reaction, filter, wash, dry, and pulverize to obtain inorganically modified and organic surface treated nano-TiO 2 powder.

Embodiment 3

[0028] 1 kg of freeze-dried nano-TiO 2 Add 10 kg of isopropanol and water with a mass ratio of 1:2 to the powder, raise the temperature to 75°C, and adjust the pH of the system to 6. Then add 1.07 kg containing 0.1kg SiO 2 Propyl orthosilicate isopropanol aqueous solution, stirred evenly, and kept at this temperature and pH for 1.5 h. Then add 0.4 kg of isopropanol aqueous solution containing 0.02 kg of octyltriethoxysilane, stir evenly, and keep the reaction at the temperature and pH for 2 h. After the reaction, filter, wash, dry, and pulverize to obtain inorganically modified and organic surface treated nano-TiO 2 powder.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a continuous nanometer TiO2 surface treatment method. Nanometer TiO2 is obtained through technologies of freeze drying, silicon or aluminium coating, organosilane or long-chainfatty acid modification and the like. According to the continuous nanometer TiO2 surface treatment method, inorganic surface treatment and organic surface treatment of the nanometer TiO2 are organically combined, the continuous nanometer TiO2 surface treatment method has the characters that a technology process is short, operation is continuous and convenient, and control is easy; the nanometer TiO2 is suitable for industrial production; meanwhile, prepared nanometer TiO2 powder not only has good hydrophobicity, but also has excellent photostability, and the application fields of a product are further expanded.

Description

technical field [0001] The invention belongs to the field of preparation and modification of nano functional materials, in particular to a continuous nano TiO 2 The method of surface treatment. Background technique [0002] Nano titanium oxide (TiO 2 ) is a new type of inorganic UV shielding material, which is widely used in sunscreen cosmetics, coatings, plastics and chemical fibers. Due to its small particle size and high specific surface energy, it is easy to agglomerate and cannot fully utilize many properties of the nanomaterial; at the same time, TiO 2 It has strong photochemical activity, and it is easy to cause discoloration and degradation of organic matter in the system under sunlight irradiation; moreover, its surface is hydrophilic and oleophobic, and is suitable for use in polar systems, such as aqueous solutions and alcohol systems, etc. . If it is added to organic application systems such as rubber, chemical fibers, plastics, inks, solvent-based coatings, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09C1/36C09C3/04C09C3/06C09C3/08C09C3/12B82Y30/00
CPCB82Y30/00C01P2006/22C01P2006/90C09C1/363C09C1/3661C09C1/3669C09C1/3684C09C1/3692
Inventor 徐斌海成庆堂吴卫星陈美陈爱娣徐新前顾冬兰
Owner 江苏河海纳米科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products