Honeycomb-like fabric and manufacturing technology thereof

A manufacturing process, honeycomb technology, applied in biochemical fiber treatment, fiber type, textiles and papermaking, etc., can solve the problems of poor wrinkle resistance and shape retention, ineffective water and oil absorption, and loose surface of fabrics, etc., to achieve oil absorption Good air permeability, good air permeability, fast moisture absorption effect

Inactive Publication Date: 2019-02-15
迦南(福建)新材料科技有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The object of the present invention is to provide a kind of honeycomb fabric and its manufacturing process, to solve the problem that the fabrics currently used to make all kinds of knitted garments are not compact and have multiple surfaces due to the lack of structure. It has a smooth structure, poor wrinkle resistance and shape retention, poor dimensional stability, poor hand feeling, and ineffective water and oil absorption.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A honeycomb fabric, comprising the following materials by weight:

[0028] 13.5 parts by weight of nylon high elastic silk fiber, 15.9 parts by weight of cotton fiber, 15.6 parts by weight of polypropylene fiber, 0.3 part by weight of deodorant, 0.7 part by weight of antibacterial agent, and 40 parts by weight of water.

[0029] A kind of honeycomb fabric as described in claim 1 and its manufacturing process, the specific production process steps are as follows:

[0030] Step 1: material preparation: take by weight nylon high elastic fiber, cotton fiber and polypropylene fiber, antibacterial agent, deodorant and water as raw materials;

[0031] Step 2: Spinning: Spinning different fiber materials in Step 1 by a spinning machine to prepare roving and spun yarn;

[0032] Step 3: Prepare the solution: add water to the dyeing vat and add deodorant and antibacterial agent, stir and mix evenly;

[0033] Step 4: Dipping the spun yarn: put the spun yarn in Step 2 into the sol...

Embodiment 2

[0043] A honeycomb fabric, comprising the following materials by weight:

[0044] 19.48 parts by weight of nylon high elastic silk fiber, 18.98 parts by weight of cotton fiber, 17.5 parts by weight of polypropylene fiber, 0.5 part by weight of deodorant, 0.95 part by weight of antibacterial agent, and 42.5 parts by weight of water.

[0045] A kind of honeycomb fabric as described in claim 1 and its manufacturing process, the specific production process steps are as follows:

[0046] Step 1: material preparation: take by weight nylon high elastic fiber, cotton fiber and polypropylene fiber, antibacterial agent, deodorant and water as raw materials;

[0047] Step 2: Spinning: Spinning different fiber materials in Step 1 by a spinning machine to prepare roving and spun yarn;

[0048] Step 3: Prepare the solution: add water to the dyeing vat and add deodorant and antibacterial agent, stir and mix evenly;

[0049] Step 4: Dipping the spun yarn: put the spun yarn in Step 2 into th...

Embodiment 3

[0059] A honeycomb fabric, comprising the following materials by weight:

[0060] 16.49 parts by weight of nylon high elastic silk fiber, 17.44 parts by weight of cotton fiber, 33.1 parts by weight of polypropylene fiber, 0.4 part by weight of deodorant, 0.83 part by weight of antibacterial agent, and 41.25 parts by weight of water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a manufacturing process of a honeycomb-like fabric. The process specifically includes the following steps that 1, materials are prepared, wherein nylon high elastic fiber, all-cotton fiber, polypropylene fiber, an antimicrobial agent, a deodorant and water as raw materials are weighed according to the corresponding weight parts; 2, spinning is performed, wherein the different fiber materials in the step 1 are spun through a spinning machine to prepare roving and spun yarn; 3, a solution is prepared, wherein the clean water, the antimicrobial agent and the deodorant areadded in a dyeing cylinder, and the mixture is stirred and mixed evenly; 4, the roving and the spun yarn are immersed, wherein the roving and the spun yarn in the step 2 are put in the solution prepared in the step 3 for immersion for 30-45 min; 5, drying, wherein the roving and the spun yarn in the step 4 are taken out and placed in a drying box for drying. According to the production process ofthe honeycomb-like fabric with good water absorption and oil absorption properties, polypropylene is processed into fiber, the oil absorption property is good, and the fiber can be specifically used for absorbing petroleum hydrocarbons, hydrocarbons and the like. The energy consumption is small, the operation is simple, the practicability is high, and the fabric is suitable for wide popularization.

Description

technical field [0001] The invention belongs to the technical field of fabric production, and in particular relates to a honeycomb fabric and a manufacturing process thereof. Background technique [0002] Weft knitting is one of knitting, in which one or more yarns are sequentially formed into loops by knitting needles along the transverse direction of the fabric, and are interlaced longitudinally to form a weft knitted fabric. Weft knitting can be divided into single-sided and double-sided. In weft knitting, the yarn is reciprocated laterally (or circularly) from one side of the machine to the other side, and a new knitting loop can be formed with the movement of the knitting needle. Insufficient surface of the fabric leads to less compact surface, mostly smooth structure, poor wrinkle resistance and shape retention performance, poor dimensional stability, poor hand feeling, and not obvious water and oil absorption effect. Contents of the invention [0003] The object o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D04B1/10D04B1/18D06M15/03D06M11/79D06M13/144D06M101/34D06M101/06D06M101/20
CPCD04B1/102D04B1/18D06M11/79D06M13/144D06M15/03D06M16/00D06M2101/06D06M2101/20D06M2101/34D10B2201/02D10B2321/022D10B2331/02D10B2401/061
Inventor 蔡奕文许恩典蔡奕武赵艳娜许锰镑许四川韩庆华周端硕邱明明
Owner 迦南(福建)新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products