Preparation method for wood capable of releasing negative oxygen ions

A negative oxygen ion and wood technology, applied in wood treatment, wood impregnation, wood impregnation, etc., can solve problems such as dyspnea, loss of activity, discomfort, etc., and achieve the effect of solving the feeling of oppression, good ventilation function, and good application prospects

Inactive Publication Date: 2019-02-19
安瑞康养生科技(苏州)有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In densely populated metropolises, industrially polluted areas, and airtight air-conditioned rooms, the pollutants produced and the liquids, solids, and aerosols formed by various organisms and air combine a large number of small air ions into large ions. The sedimentation and loss of activity will red...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A preparation method of wood capable of releasing negative oxygen ions, comprising the following steps:

[0023] Step 1: Prepare a negative oxygen ion solution, weigh a certain amount of ionized water, isopropylamine, phenol, inorganic nano-silicon, tea polyphenols, procyanidins, nano-titanium dioxide, bactericidal materials and radiation protection raw materials, and mix them to obtain negative oxygen ions solution;

[0024] Step 2: Select high-quality wood with high temperature resistance, place the wood in an environment of 50-60°C, soak it with the negative oxygen ion solution obtained in Step 1, and remove it after soaking for 1-3 hours;

[0025] Step 3: Continue to spray the negative oxygen ion solution evenly in an environment of 50-60°C for the wood soaked in the negative oxygen ion solution obtained in step 2, and the spraying time is 2-5 hours;

[0026] Step 4: continue to place the wood obtained in step 3 in an environment of 50-60°C for drying treatment unt...

Embodiment 2

[0033] Embodiment 2: be the preferred embodiment of embodiment 1

[0034] Step 1: Prepare a negative oxygen ion solution, weigh a certain amount of ionized water, isopropylamine, phenol, inorganic nano-silicon, tea polyphenols, procyanidins, nano-titanium dioxide, bactericidal materials and radiation protection raw materials, and mix them to obtain negative oxygen ions solution;

[0035] Step 2: Select high-quality wood with high temperature resistance, place the wood in an environment of 50-60°C, soak it with the negative oxygen ion solution obtained in Step 1, and remove it after soaking for 1-3 hours;

[0036] Step 3: Continue to spray the negative oxygen ion solution evenly in an environment of 50-60°C for the wood soaked in the negative oxygen ion solution obtained in step 2, and the spraying time is 2-5 hours;

[0037] Step 4: continue to place the wood obtained in step 3 in an environment of 50-60°C for drying treatment until the wood is completely dried and cooled;

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method for wood capable of releasing negative oxygen ions. The preparation method comprises the following steps that 1, ionized water, isopropylamine, phenol, inorganic nanometer silicon, tea polyphenol, proanthocyanidins, nanometer titania, a sterilization material and a radiation protection raw material are quantitatively weighed and mixed, and a negative oxygen ion solution is obtained; 2, high-temperature-resistant high-quality wood is selected and put in the environment with the temperature being 50-60 DEG C to be soaked in the obtained negative oxygen ion solution for 1-3 h, and then, the wood is taken out; 3, the negative oxygen ion solution is uniformly sprayed onto the wood soaked by the negative oxygen ion solution in the 50-60 DEG C environment for 2-5 h; 4, the wood obtained in the step 3 is subjected to drying treatment and cooled in the 50-60 DEG C environment; and 5, the wood obtained in the step 4 is heated to 30-45 DEG C through electromagnetic waves, and 10000-50000 negative oxygen ions per cubic centimeter are released. Through the preparation method, the wood capable of releasing the negative oxygen ions can be obtained, inaddition, the wood has the formaldehyde removal function, and the good air exchange function is achieved.

Description

technical field [0001] The invention relates to the technical field of environmental protection wood processing, in particular to a preparation method of wood capable of releasing negative oxygen ions. Background technique [0002] Air negative oxygen ion is a kind of negatively charged air particles. Like vitamins in food, it has a very important impact on human life activities, so some people call it "air vitamin", and some even think that air negative oxygen Ions are related to longevity, and it is called "longevity element". High concentration of small air negative ions make the air fresh and refreshing. In densely populated metropolises, industrially polluted areas, and airtight air-conditioned rooms, the pollutants produced and the liquids, solids, and aerosols formed by various organisms and air combine a large number of small air ions into large ions. The sedimentation and loss of activity will reduce the concentration of small air negative ions, and a state of imb...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B27K3/02B27K5/04B27K5/00B27K3/52B27K3/00
CPCB27K3/007B27K3/02B27K3/0228B27K3/52B27K5/003B27K5/04
Inventor 花丹
Owner 安瑞康养生科技(苏州)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap