A delayed coking process for preparing coal-based needle coke

A delayed coking and needle coke technology, which is applied in the multi-tower delayed coking process field, can solve the problems of solvent coking, difficult long-term stable operation of the process flow, and small proportion of petroleum-based raw materials, and achieves the effect of avoiding coking and clogging.

Active Publication Date: 2020-09-08
山西中科化美科技有限责任公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the large difference in the molecular structure and composition of coal tar pitch and petroleum-based raw materials, the proportion of petroleum-based raw materials added is relatively small, and the mesophase formation and coking reaction conditions of the two raw materials are different, so the delayed coking process conditions need Adjust according to different raw materials, it is difficult to run stably for a long period of time
[0005] The above-mentioned existing technologies have problems such as the inability to control the reaction process of coal-based needle coke raw materials in the delayed coking process, coking of solvents in heating furnace tubes, feed pipes, etc., and difficulty in long-term stable operation of the process flow.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A delayed coking process for preparing coal-based needle coke
  • A delayed coking process for preparing coal-based needle coke

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] like Figure 1-2 As shown, a delayed coking process for preparing coal-based needle coke, the specific steps are as follows:

[0026] 1. The medium-temperature coal tar pitch is the refined raw material after solvent pretreatment. The content of quinoline insolubles in the refined raw material is 0.08%. The refined raw material is heated to 395°C by the low-temperature heating furnace 1 and then sent to the thermal polymerization tower 2. In a nitrogen atmosphere, Under the conditions of reaction temperature 390°C and reaction pressure 0.1MPa, stir for 3h;

[0027] 2. When the mesophase content of the material reaches 35%, the material containing the mesophase obtained in the thermal polymerization kettle and diesel oil are sent into the high-temperature heating furnace 3 together;

[0028] 3. Raise the temperature of the mixed material in the high-temperature heating furnace 3 to 486°C, and send the mixed material into the coke tower;

[0029] 4. Control the temperat...

Embodiment 2

[0033] A delayed coking process for preparing coal-based needle coke, the specific steps are as follows:

[0034] 1. The refined raw material of high-temperature coal tar after solvent pretreatment, the content of quinoline insolubles in the refined raw material is 0.03%, and the refined raw material is heated to 386 °C by the low-temperature heating furnace 1 and then sent to the thermal polymerization tower 2, in a nitrogen atmosphere, Under the conditions of reaction temperature 380°C and reaction pressure 0.2MPa, stir for 1.5h;

[0035] Two, when the mesophase content of the material reaches 32%, the mixture of the material containing the mesophase obtained in the thermal polymerization kettle and tetralin and diesel oil is jointly sent into the high-temperature heating furnace 3;

[0036] 3. Raise the temperature of the mixed material in the high-temperature heating furnace 3 to 486°C, and send the mixed material into the coke tower;

[0037] 4. Control the temperature i...

Embodiment 3

[0041] A delayed coking process for preparing coal-based needle coke, the specific steps are as follows:

[0042] 1. The medium-temperature coal tar pitch is a refined raw material after solvent pretreatment. The content of quinoline insolubles in the refined raw material is 0.05%. The refined raw material is heated to 430°C by a low-temperature heating furnace 1 and sent to a thermal polymerization tower 2. In a nitrogen atmosphere, Under the conditions of reaction temperature 425°C and reaction pressure 0.4MPa, stir for 2h;

[0043] 2. When the mesophase content of the material reaches 40%, the material containing the mesophase obtained in the thermal polymerization kettle and the diesel oil are jointly sent into the high-temperature heating furnace 3;

[0044] 3. Raise the temperature of the mixed material in the high-temperature heating furnace 3 to 505°C, and send the mixed material into the coke tower;

[0045]4. Control the temperature in the coke tower to 470°C, the c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of needle coke preparation, and relates to a delayed coking process for preparing coal-based needle coke, in particular to a multi-tower delayed coking process with a heat polycondensation tower and a coking tower. The technical scheme includes that the coking process includes the steps: pretreating coal tar, coal pitch, modified pitch and the like to obtain finished raw materials; heating the finished raw materials, and enabling the heated raw material to enter a heat polymerization tower; polymerizing the raw materials to generate an intermediatephase in the inertness or reduction atmosphere; rapidly heating materials containing the intermediate phase and inert oil when the content of the intermediate phase of the materials reaches 30-60%; conveying the heated mixture into the coking tower to generate coke, and calcining the coke to obtain the needle coke. High-temperature oil and gas of the coking tower is divided into fuel gas and coking oil by a fractionating tower, the coking tower serves as a product output system, the process can accurately control coking reaction degree of coal-based needle coke raw materials, coking and jamming of a device pipeline are avoided, and long-period stable operation of coal-based needle coke production is achieved.

Description

technical field [0001] The invention belongs to the technical field of needle coke preparation, and relates to a delayed coking process for preparing coal-based needle coke, in particular to a multi-tower delayed coking process with thermal shrinkage towers and coking towers. Background technique [0002] Needle coke is a high-quality carbon material with the advantages of low ash, low thermal expansion, high conductivity, and high anisotropy. It is widely used in many fields such as high-power / ultra-high-power graphite electrodes, lithium battery negative electrode materials, and special graphite materials. . According to different raw materials, it can be divided into coal-based needle coke and oil-based needle coke. Coal-based needle coke raw materials are represented by coal tar pitch, etc. Compared with oil-based needle coke raw materials such as residual oil and catalytic oil slurry, it is characterized by high polycyclic aromatic hydrocarbon content, low alkane conte...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C10G55/04C10B55/00C10B57/00
CPCC10B55/00C10B57/005C10G55/04C10G2300/10
Inventor 康荷菲郭少青
Owner 山西中科化美科技有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com