Reflective insulation coating for oil tank and preparation method thereof

A technology for reflective thermal insulation coatings and oil tanks, applied in reflective/signal coatings, anti-corrosion coatings, fire-retardant coatings, etc. Thermal performance, the effect of improving the performance of the paint film

Inactive Publication Date: 2019-03-01
广西南宁维一防腐科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are many researches on heat insulation coatings for storage tanks in China, but the heat insulation effects are different, good and bad are mixed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] A reflective heat-insulating coating for oil tanks, the coating is composed of component A and component B, including the following raw materials in parts by weight:

[0054] Component A: 50 parts of acrylic resin; 25 parts of titanium dioxide; 8 parts of heat reflective powder; 8 parts of xylene; 5 parts of butyl acetate; 0.5 parts of anti-settling agent; 1.5 parts of dispersant;

[0055] Component B: 70 parts of biuret; 0.1 part of auxiliary agent;

[0056] The preparation method of the heat reflective powder comprises the following steps:

[0057] (1) Nano-titanium oxide, nano-vanadium oxide, nano-rectorite powder, nano-manganese oxide and nano-copper oxide are made into nano-titanium oxide: nano-vanadium oxide: nano-rectorite powder: nano-manganese oxide: nano-copper oxide = 1:1:1:0.5:0.5 put into the mixer and mix and stir for 0.5 hours to obtain mixture A;

[0058] (2) Prepare 0.05mol / L nitric acid solution, dissolve aluminum isopropoxide in 0.05mol / L nitric aci...

Embodiment 2

[0068] A reflective heat-insulating coating for oil tanks, the coating is composed of component A and component B, including the following raw materials in parts by weight:

[0069] Component A: 60 parts of acrylic resin; 35 parts of titanium dioxide; 10 parts of heat reflective powder; 10 parts of xylene; 8 parts of butyl acetate; 1 part of anti-settling agent; 3.0 parts of dispersant; 1.0 part of defoamer;

[0070] Component B: 75 parts of biuret; 2.0 parts of auxiliary agent;

[0071] The preparation method of the heat reflective powder comprises the following steps:

[0072] (1) Nano-titanium oxide, nano-vanadium oxide, nano-rectorite powder, nano-manganese oxide and nano-copper oxide are made into nano-titanium oxide: nano-vanadium oxide: nano-rectorite powder: nano-manganese oxide: nano-copper oxide = 1:1:1:0.5:0.5 put into the mixer and mix for 1 hour to obtain mixture A;

[0073] (2) Prepare 0.05mol / L nitric acid solution, dissolve aluminum isopropoxide in 0.05mol / L ...

Embodiment 3

[0083] A reflective heat-insulating coating for oil tanks, the coating is composed of component A and component B, including the following raw materials in parts by weight:

[0084] Component A: 55 parts of acrylic resin; 30 parts of titanium dioxide; 9 parts of heat reflective powder; 9 parts of xylene; 6 parts of butyl acetate; 0.7 parts of anti-settling agent; 2.0 parts of dispersant; 0.7 parts of defoamer;

[0085] Component B: 73 parts of biuret; 1.0 part of auxiliary agent;

[0086] The preparation method of the heat reflective powder comprises the following steps:

[0087] (1) Nano-titanium oxide, nano-vanadium oxide, nano-rectorite powder, nano-manganese oxide and nano-copper oxide are made into nano-titanium oxide: nano-vanadium oxide: nano-rectorite powder: nano-manganese oxide: nano-copper oxide = 1:1:1:0.5:0.5 was put into the mixer and mixed for 0.7 hours to obtain mixture A;

[0088] (2) Prepare 0.05mol / L nitric acid solution, dissolve aluminum isopropoxide in ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
refractive indexaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of coatings and specifically relates to a reflective insulation coating for an oil tank and a preparation method thereof. The reflective insulation coating is composed of a component A and a component B; the component A comprises the following raw materials: 50-60 parts of acrylic resin, 25-35 parts of titanium dioxide, 8-10 parts of heat reflection powder, 8-10parts of xylene, 5-8 parts of n-butyl acetate, 0.5-1 part of anti-settling agent, 1.5-3.0 parts of dispersing agent and 0.5-1.0 part of de-foaming agent; the component B comprises the following raw materials: 70-75 parts of biuret and 0.1-0.2 part of auxiliaries. The reflective insulation coating is capable of excellently shielding ultraviolet rays, infrared rays, and the like, is characterized bymulti-reflection and low heat absorption, is capable of effectively obstructing heat transfer and has an excellent reflecting heat-insulation effect.

Description

technical field [0001] The invention relates to the field of coatings, in particular to a reflective heat-insulating coating for oil tanks and a preparation method thereof. Background technique [0002] The earth is irradiated by the sun all the time, and the sun has about 1765×1017J of energy per second to reach the earth. The huge energy provides the necessary conditions for human survival and life. But the intense radiation of the sun brings inconvenience to people's life. At noon in hot summer, the solar radiation energy on the surface can be as high as about 1000w / m 2 . Crude oil and refined oil storage tanks and light liquid chemical product storage tanks in petrochemical enterprises will continue to accumulate energy due to solar radiation heat, causing the surface and interior of the storage tank to heat up rapidly. The solar radiation energy irradiated on the roof of a 5000m3 vaulted tank at noon in summer can be as high as 400kW, which increases the evaporation ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D5/33C09D5/08C09D7/61C09D7/63C09D7/65
CPCC08K2003/2241C08K2003/2248C08K2003/2262C08K2201/011C08L2201/08C09D5/004C09D5/08C09D5/18C09D7/61C09D7/63C09D7/65C09D133/00C08L75/04C08K13/06C08K9/10C08K3/22C08K3/346C08K3/34
Inventor 李金庆李常勇王全忠
Owner 广西南宁维一防腐科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com