A kind of graphene thermal storage pad and preparation method thereof

A graphene and heat storage technology, applied in the field of thermal insulation materials, can solve the problems of inability to store and release heat, occupy a large space, and inconvenient construction, and achieve the effects of reducing material and labor costs, stable structure, and convenient installation.

Active Publication Date: 2020-12-11
牛墨石墨烯应用科技有限公司
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Therefore, aiming at the above content, the present invention provides a graphene heat storage mat and its preparation method, which solves the problems of poor waterproofness, inconvenient construction, large space occupation, and inability to store heat and release heat in the prior art.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A graphene heat storage pad, comprising a bottom moisture-proof layer and a heat storage layer on the top layer, the heat storage layer is attached to the upper surface of the moisture-proof layer, and the moisture-proof layer is made of radiation cross-linked polyethylene foam material The thermal storage layer is made of graphene / organic composite phase change material, and a layer of aluminum foil is pasted on the bottom of the moisture-proof layer.

[0027] The preparation steps of graphene thermal storage pad are as follows:

[0028] (1) Preparation of moisture-proof layer:

[0029] After plasticizing the polyethylene resin at 120°C with a double-roll mill, add foaming agent and other additives in turn, mix well, pull out and cool, then pelletize with a pelletizer, and extrude Extruded into sheets by machine, irradiated through the irradiation transmission device, and finally foamed on the foaming device, and the obtained radiation cross-linked polyethylene foam m...

Embodiment 2

[0035] A graphene thermal storage pad, its structure is consistent with embodiment one, and the preparation method of described graphene thermal storage pad is as follows:

[0036] (1) Make the moisture-proof layer with radiation cross-linked polyethylene foam material, the preparation method is consistent with embodiment one;

[0037] (2) The heat storage layer is made of graphene / organic composite phase change material, and the preparation process of graphene / organic composite phase change material is as follows:

[0038] Step1: 30 parts by weight of ethanol and 30 parts by weight of acetone are made into a mixed solution, and 5 parts by weight of graphene, 12 parts by weight of carbon black, 3 parts by weight of carbon nanotube powder, and 0.8 parts by weight of 3-glycidyl propylene are added to the mixed solution Base (dimethoxy) methyl silane, carry out ultrasonic dispersion 6h, then add 35 parts by weight of polyvinyl formal resin, 2 parts by weight of polychlorotrifluor...

Embodiment 3

[0042] A graphene thermal storage pad, its structure is consistent with embodiment one, and the preparation method of described graphene thermal storage pad is as follows:

[0043] (1) Make the moisture-proof layer with radiation cross-linked polyethylene foam material, the preparation method is consistent with embodiment one;

[0044] (2) The heat storage layer is made of graphene / organic composite phase change material, and the preparation process of graphene / organic composite phase change material is as follows:

[0045]Step1: 40 parts by weight of ethanol and 35 parts by weight of acetone are made into a mixed solution, and 6 parts by weight of graphene, 15 parts by weight of carbon black, 4 parts by weight of carbon nanotube powder, and 1 part by weight of 3-glycidyl propylene are added to the mixed solution Base (dimethoxy)methylsilane, ultrasonic dispersion for 7h, and then add 50 parts by weight of polyvinyl formal resin, 3 parts by weight of polychlorotrifluoroethylen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of heat preservation materials, and provides a graphene heat accumulation pad and a preparing method thereof. The graphene heat accumulation pad comprises a damp-proof layer at the bottom and a heat accumulation layer on the top, the heat accumulation layer fits the upper surface of the damp-proof layer, the damp-proof layer is made from a radiation crosslinkingpolyethylene foaming material, the heat accumulation layer is prepared from a graphene / organic compound phase-change material, and a layer of aluminum foil fits the bottom face of the damp-proof layer. The invention provides a novel thin film material with the functions of heat preservation, heat accumulation and damp proofing, and the novel thin film material is suitable for thermal insulation materials of various floors and floor heating systems.

Description

technical field [0001] The invention relates to the field of thermal insulation materials, in particular to a graphene heat storage pad and a preparation method thereof. Background technique [0002] When installing general building floors, heating floors, heating membranes, heating panels, etc., thermal insulation materials need to be installed. Traditional thermal insulation materials are mainly to increase the gas phase void ratio and reduce the thermal conductivity and conductivity. In order to increase convective heat transfer and radiation heat transfer in the use environment, fiber-based thermal insulation materials must have a thicker coating; while profile-based inorganic thermal insulation materials need to be assembled and constructed, there are many seams, which damage the appearance and waterproof. Poor performance, short service life and other defects. [0003] The invention of authorized notification number CN106489050B discloses a vacuum heat insulation mate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B32B15/20B32B15/085B32B27/32B32B5/18B32B9/00B32B9/04B32B7/08B32B33/00B32B37/10B32B37/06E04B1/78C08L29/14C08L27/12C08K13/06C08K9/06C08K9/00C08K3/04C08K5/053C08K3/26C08K3/36C08K7/14C08K5/09C08K5/07C09K5/06
CPCB32B7/08B32B9/007B32B9/046B32B15/046B32B15/20B32B33/00B32B37/06B32B37/10B32B2266/025B32B2307/21B32B2307/212B32B2307/3065B32B2307/31B32B2307/7265B32B2419/00C08K2003/265C08K2201/011C08L29/14C08L2201/02C08L2205/03C09K5/06E04B1/78C08L27/12C08K13/06C08K9/06C08K9/00C08K3/041C08K3/042C08K3/04C08K5/053C08K3/26C08K3/36C08K7/14C08K5/09C08K5/07
Inventor 陈心军孟建武杨跃仁张雷
Owner 牛墨石墨烯应用科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap