A colored dispersion liquid, a colored photosensitive resin composition, a pattern layer, a color filter and a display device

A photosensitive resin and dispersing resin technology, applied in optics, instruments, filters, etc., can solve the problems of insufficient improvement in solvent resistance and storage stability, and achieve excellent storage stability, reliability, and elasticity. The effect of the response rate

Active Publication Date: 2019-04-30
DONGWOO FINE CHEM CO LTD
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, improvements in solvent resistance and storage stability are still insufficient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A colored dispersion liquid, a colored photosensitive resin composition, a pattern layer, a color filter and a display device
  • A colored dispersion liquid, a colored photosensitive resin composition, a pattern layer, a color filter and a display device
  • A colored dispersion liquid, a colored photosensitive resin composition, a pattern layer, a color filter and a display device

Examples

Experimental program
Comparison scheme
Effect test

manufacture example 1

[0177] Production Example 1. Production of Dispersion Resin A1

[0178] 277 g of methoxybutyl acetate was injected|thrown-in to the separation-type flask of internal volume 1L equipped with the stirrer, thermometer, reflux condenser, dropping funnel, and nitrogen introduction tube, and it heated to 80 degreeC. Next, prepare 3,4-epoxytricyclo[5.2.1.0,2,6]decane-9-yl acrylate and 3,4-epoxytricyclo[5.2.1.0,2,6] A mixture obtained by dissolving 301 g of decan-8-yl acrylate in a molar ratio of 50:50, 49 g of methacrylic acid, and 23 g of azobisdimethylvaleronitrile in 350 g of methoxybutyl acetate mixture. The said mixed solution was dripped in the flask over 5 hours using the dropping funnel, and it reacted for 3 hours, and dispersion resin A1 [solid content (NV) 35.0 weight%] was manufactured. The acid value (dry) of the dispersed resin A1 produced above was 69.8 KOH mg / g, the weight average molecular weight (Mw) was 12,300, and the degree of dispersion (Mw / Mn) was 2.1.

manufacture example 2

[0179] Production Example 2. Production of Dispersion Resin A2

[0180] Prepare a flask equipped with a stirrer, thermometer, reflux condenser, dropping funnel, and nitrogen inlet. As a monomer dropping funnel, 14.4 parts by weight (0.2 moles) of acrylic acid, 140.8 parts by weight (0.8 moles) of benzyl methacrylate, 2.0 parts by weight of tert-butyl peroxy-2-ethylhexanoate, propylene glycol monomethyl 40.0 parts by weight of ether acetate (PGMEA) were mixed and prepared. As a chain transfer agent dropping tank, 3.0 parts by weight of n-dodecanemercaptan and 24.0 parts by weight of PGMEA were mixed and prepared. After that, 395 parts by weight of PGMEA was added to the flask, and the atmosphere in the flask was replaced with nitrogen from air, and then the temperature of the flask was raised to 90° C. while stirring. Next, the monomer and the chain transfer agent were added dropwise from the dropping funnel. The dropwise addition was performed for 4 hours each while maintai...

manufacture example 3

[0181] Production Example 3. Production of Dispersion Resin A3

[0182] Prepare a flask equipped with a stirrer, thermometer, reflux condenser, dropping funnel, and nitrogen inlet. As a monomer dropping funnel, 52.1 parts by weight (0.25 moles) of 2-phenylthioethyl acrylate, 44.0 parts by weight (0.25 moles) of benzyl methacrylate, 12.9 parts by weight (0.15 moles) of methacrylic acid, ethylene 41.3 parts by weight (0.35 mol) of methyl toluene, 4.0 parts by weight of tert-butyl peroxy-2-ethylhexanoate, and 40.0 parts by weight of PGMEA were prepared by mixing. As a chain transfer agent dropping tank, 6.0 parts by weight of n-dodecanemercaptan and 24.0 parts by weight of PGMEA were mixed and prepared. After that, 395 parts by weight of PGMEA was added to the flask, and the atmosphere in the flask was replaced with nitrogen from air, and then the temperature of the flask was raised to 90° C. while stirring. Next, the monomer and the chain transfer agent were added dropwise f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
dispersityaaaaaaaaaa
dispersityaaaaaaaaaa
Login to View More

Abstract

The invention provides a colored photosensitive resin composition, a pattern layer manufactured by using the colored photosensitive resin composition, a color filter including the pattern layer, and adisplay device including the color filter. The colored photosensitive resin composition comprises a colored dispersion liquid, an alkali-soluble resin, a photopolymerizable compound, a photopolymerization initiator and a solvent. The colored dispersion liquid comprises a colorant containing an organic black pigment, a blue pigment, a purple pigment and carbon black, a dispersion resin containinga copolymer of the following chemical formula 1, and a solvent, wherein in the chemical formula 1, R1 and R2 are each independently hydrogen or a methyl group, and the molar ratio of a monomer a to amonomer b is 1: 20 to 20: 1.

Description

technical field [0001] The present invention relates to a colored dispersion liquid, a colored photosensitive resin composition containing the above colored dispersion liquid, a pattern layer produced using the above resin composition, a color filter containing the above pattern layer, and a display device containing the above color filter. Background technique [0002] Color filters are widely used in various display devices such as imaging elements and liquid crystal displays (LCDs), and the range of applications thereof is rapidly expanding. The above-mentioned color filters used in imaging elements, liquid crystal display devices, etc. are formed of coloring patterns of three colors of red (Red), green (Green) and blue (Blue), or are formed of yellow (Yellow), magenta ( Magenta) and blue-green (Cyan) coloring patterns are formed. [0003] Each colored pattern of the above-mentioned color filter is generally formed using a colored photosensitive resin composition contain...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G03F7/004G03F7/027G02B5/22
CPCG03F7/004G03F7/027G02B5/223C09B67/0084G03F7/105G03F7/028G03F7/0007G02B5/20G02F1/133514
Inventor 权宁竖权玟廷曺升铉
Owner DONGWOO FINE CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com