A kind of high simulation antibacterial ceramic tile and preparation method thereof

A ceramic tile and green body technology, which is applied in the field of high simulation antibacterial tiles and its preparation, can solve the problems of low fidelity, unsatisfactory antibacterial performance, poor three-dimensional effect, etc., and achieve the effect of avoiding texture distortion

Active Publication Date: 2021-12-31
FOSHAN SHI WAN YING BRAND CERAMICS CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the problems of unsatisfactory antibacterial properties of ceramic tiles, poor three-dimensional effect and low fidelity, the present invention aims to provide a highly simulated ceramic tile and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A preparation method of highly simulated antibacterial tiles, said method comprising the steps of:

[0036] 1) Preparing the green body: Ball mill the mud and powder of the green body to the required particle size, spray dry them, arrange them in the mold according to the texture requirements, and press them into shape;

[0037] 2) Carry out a firing treatment at 850° C. for the green body of step 1);

[0038] 3) Apply a base glaze to the fired body in step 2), the components of the base glaze include acrylic resin 8%, SiO2 60%, Al3O2 10%, Fe2O3 0.05%, K2O 1.5%, Na2O 2%, MgO 2 %, the thickness of the bottom glaze is 2mm;

[0039] 4) Fire the green body after applying the primer at 680°C;

[0040] 5) Ink-jet treatment is carried out to the green body obtained in step 4), the ink used in the ink-jet treatment comprises the following components by weight: nano silicon dioxide 5%, polymethyl acrylate 4%, propylene glycol methyl ether 14%, Porous copper oxide loaded nano-si...

Embodiment 2

[0047] A preparation method of highly simulated antibacterial tiles, said method comprising the steps of:

[0048] 1) Preparing the green body: Ball mill the mud and powder of the green body to the required particle size, spray dry them, arrange them in the mold according to the texture requirements, and press them into shape;

[0049] 2) Carrying out a firing treatment on the green body in step 1) at 1000° C.;

[0050] 3) Applying a primer to the body after firing in step 2), the primer includes epoxy resin 12%, SiO2 55%, Al3O2 12%, Fe2O3 0.1%, K2O2.8%, Na2O 3%, MgO 3.6% , the thickness of the bottom glaze is 1.8mm;

[0051] 4) Carry out secondary firing treatment at 800°C for the green body after applying the bottom glaze;

[0052] 5) Ink-jet treatment is carried out to the green body obtained in step 4), the ink used in the ink-jet treatment comprises the following components by weight: nano silicon dioxide 5%, polymethyl acrylate 4%, propylene glycol methyl ether 14%, P...

Embodiment 3

[0060] A preparation method of highly simulated antibacterial tiles, said method comprising the steps of:

[0061] 1) Preparing the green body: Ball mill the mud and powder of the green body to the required particle size, spray dry them, arrange them in the mold according to the texture requirements, and press them into shape;

[0062] 2) Carrying out a firing treatment on the green body in step 1) at 1000° C.;

[0063] 3) Apply a primer to the body after firing in step 2), the thickness of the primer is 2mm, and the primer includes 14% epoxy resin, SiO2 65%, Al3O2 15%, Fe2O3 0.1%, K2O 1.5% , Na2O2%, MgO 2%;

[0064] 4) Carry out secondary firing treatment at 800°C for the green body after applying the bottom glaze;

[0065] 5) Inkjet treatment is carried out to the green body obtained in step 4), and the ink used in the inkjet treatment comprises the following components by weight: 6% of silicon dioxide, 8% of polymethyl acrylate, 15% of propylene glycol methyl ether, porou...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The present invention provides a highly simulated antibacterial ceramic tile and a preparation method thereof. The method comprises the following steps: 1) Preparing a green body: ball-milling the mud and powder of the green body to the required particle size, spraying and drying them in a mold according to The texture is required to be paved and pressed; 2) the green body in step 1) is fired once at 850‑1000°C; 3) the base glaze is applied to the fired body in step 2), and the base glaze The components include 8-14% of organic binder; 4) firing the green body after applying the primer; 5) performing inkjet treatment on the green body obtained in step 4); 7) sintering the green body above 1200°C; 8) pickling the sintered tiles; 9) polishing the pickled tiles, the ceramic tiles prepared by the present invention have the following characteristics: High fidelity, strong three-dimensional sense and antibacterial function.

Description

technical field [0001] The invention relates to a tile and a preparation method thereof, in particular to a highly simulated antibacterial tile and a preparation method thereof. Background technique [0002] Natural marble has always been sought after by people as a stone decoration material because of its noble and elegant appearance. However, as a non-renewable resource, the cost of mining and production of natural marble is getting higher and higher. In order to meet people's growing demand for natural marble, reasonable control In terms of production costs, more and more artificial marbles are appearing on the market. However, due to poor technology, the imitation degree and three-dimensional effect of the prepared artificial marble are not ideal, which greatly affects the fidelity of the marble, and with the gradual improvement of people's living standards, the requirements for the living environment are also getting higher and higher. In the current unsatisfactory env...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/89C03C8/00C09D11/38C09D11/30
Inventor 范新晖吴则昌林金宏程贵生吴柏惠
Owner FOSHAN SHI WAN YING BRAND CERAMICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More