A kind of roll material for AGV vehicle environment and preparation method thereof

A coiled material and environment technology, applied in chemical instruments and methods, epoxy resin glue, synthetic resin layered products, etc. Effect

Active Publication Date: 2022-04-26
浙江港流高分子科技股份有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Although the above-mentioned coatings or floors have certain performance advantages, other performances need to be improved when used in the AGV environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of roll material for AGV vehicle environment and preparation method thereof
  • A kind of roll material for AGV vehicle environment and preparation method thereof
  • A kind of roll material for AGV vehicle environment and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0090] 1. Preparation of surface coating

[0091] Preparation of component A, 64.5 parts of phenolic epoxy vinyl ester resin DERAKANE 470; 33 parts of wear-resistant and anti-skid filler; 0.8 parts of viscosity reducer BYK-P 2710; 0.2 parts of defoamer BYK066N; 1.5 parts of accelerator naphthene cobalt acid; after stirring evenly, filter to obtain component A of surface coating;

[0092] Among them, the wear-resistant anti-skid filler is composed of: 20 parts of glass fiber powder, 35 parts of chopped glass fiber, 40 parts of TPU powder, and 5 parts of ternary vinyl chloride resin powder.

[0093] B component is curing agent methyl ethyl ketone peroxide;

[0094] AB components are mixed according to 100:2, and stirred evenly to prepare the top coat;

[0095] 2. Preparation of viscous coating

[0096] Preparation of component A: 67 parts of epoxy resin NPEF-128; 18 parts of polyurethane epoxy resin KTM832; 5 parts of diluent benzyl alcohol; 6 parts of thickener hydrophilic f...

Embodiment 2

[0113] 1. Preparation of surface coating

[0114] Preparation of component A, 67.8 parts of bisphenol A type epoxy vinyl ester resin is DERAKANE411; 30 parts of wear-resistant and anti-skid filler; 1 part of viscosity reducer S-3201; 0.2 parts of defoamer BYK066N; 1 part of accelerator ring Cobalt alkanoate; after stirring evenly, filter to obtain component A of the surface coating;

[0115] Among them, the wear-resistant anti-slip filler is composed of: 20 parts of glass fiber powder, 30 parts of chopped glass fiber, 40 parts of TPU powder, and 10 parts of ternary vinyl chloride resin powder.

[0116] Component B is the curing agent dibenzoyl peroxide;

[0117] AB components are mixed according to 100:2.5, and stirred evenly to prepare the surface coating;

[0118] 2. Preparation of viscous coating

[0119] Preparation of component A: 70 parts of epoxy resin NPEF-70; 15 parts of polyurethane epoxy resin KTM832; 6 parts of diluent propylene oxide butyl ether; 5 parts of thi...

Embodiment 3

[0136] This embodiment is identical with embodiment 1 except that the type of surface layer resin adopted in the surface layer coating is different, that is, the bisphenol-A epoxy vinyl resin MFE-2 of Huachang brand is used.

[0137] After testing: surface hardness 4H; coefficient of friction 0.75; wear resistance 0.003g; surface roughness Ra 0.012; flexibility φ32mm (but the test pass rate of flexibility is about 50%); residual sag of compression resistance 0mm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Basis weightaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a roll material for an AGV vehicle environment and a preparation method thereof. The roll material has a layered structure, and sequentially includes a stitch-bonded felt reinforcement layer, a fiber cloth reinforcement layer, a two-dimensional code printing layer and a transparent surface layer from bottom to top The reinforcement layer of the stitched mat is formed by coating high-permeability paint on the stitch-bonded mat and curing; the fiber cloth reinforcement layer is formed by coating the high-permeability paint on the fiber cloth and curing; the fiber cloth reinforcement layer and the stitch-bonded mat reinforcement layer The two-dimensional code printing layer is formed by printing the adhesive paint on the fiber cloth reinforcement layer and curing; the transparent surface layer is formed by coating the surface coating on the two-dimensional code printing layer and curing. In the present invention, through the structural design of a transparent surface layer, a two-dimensional code printing layer, and a double-layer reinforcement layer, as well as the use of surface coatings, high-permeability coatings and viscous coatings, a coiled material for the AGV vehicle environment is obtained. The characteristics of abrasiveness, high skid resistance and high pressure resistance can meet the needs of AGV vehicles on the ground.

Description

technical field [0001] The invention relates to the technical field of automatic storage ground materials, in particular to a coil material for an AGV vehicle environment and a preparation method thereof. Background technique [0002] With the advent of the industry 4.0 era, the automation of production systems, storage systems, and transportation systems in the industrial manufacturing process is getting higher and higher. In particular, AGV handling automatic systems are more and more commonly used in factory production, warehousing, and logistics. AGV vehicles are on the ground. The material damage is extremely strong, not only the extremely high pressure of the wheels on the ground causes damage to the ground materials, but also the movement route of the AGV vehicle is relatively fixed, and the wheels rotate in situ. Therefore, the ground material is required to have high compressive resistance, high wear resistance, anti-skid, dust-free and other properties. [0003] H...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B17/02B32B17/06B32B9/00B32B9/04B32B17/10B32B27/02B32B27/34B32B38/14B32B37/12C09J163/00C09J175/04C09J11/04D06N3/00D06N3/14
Inventor 张朝设
Owner 浙江港流高分子科技股份有限公司