Preparation method for carrollite spinel and application thereof
A technology of sulfur-copper-cobalt ore and spinel, applied in chemical instruments and methods, water pollutants, physical/chemical process catalysts, etc., can solve problems such as large dosage, instability and easy dissolution of single metal sulfide , to achieve the effects of fast reaction speed, stable structure and high catalytic efficiency
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0030] Specific embodiment one: The preparation method of sulphur-copper-cobalt ore spinel of this embodiment is carried out according to the following steps: dissolving cobalt ion salt and copper ion salt in ultrapure water, stirring until a clear solution is obtained, and slowly adding to the clear solution Thiourea is then vigorously stirred until thiourea is completely dissolved and a transparent and uniform solution is obtained; after adding excess ethylenediamine to the transparent and uniform solution, a dark brown liquid is obtained. The dark brown liquid is heated at high temperature for hydrothermal reaction. After the reaction is completed, the obtained solid product is cooled to room temperature, and then the solid product is washed several times with ultrapure water and ethanol in sequence, and finally dried to obtain the sulphur copper cobalt ore spinel.
[0031] 1. The specific reaction mechanism of this embodiment is that the sulphur-copper-cobalt ore spinel acts a...
Example Embodiment
[0042] Specific embodiment two: this embodiment is different from specific embodiment one in that: the cobalt ion salt is cobalt nitrate, cobalt sulfate or cobalt acetate; the copper ion salt is copper nitrate, copper sulfate or copper acetate. The other steps and parameters are the same as in the first embodiment.
Example Embodiment
[0043] Specific embodiment three: This embodiment is different from specific embodiment one or two in that the concentration of cobalt ion in the clear solution is 0.4-0.8 mmol / L. The other steps and parameters are the same as in the first or second embodiment.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap