Preparation technology of novel modified triethanolamine

A technology of triethanolamine and preparation process, which is applied in the direction of petroleum industry, additives, lubricating compositions, etc., can solve the problems affecting the bonding strength of triethanolamine and steel plate, copper powder layer, and does not consider the application, so as to achieve low friction coefficient and not easy to fall off , to avoid the effect of the accumulation of frictional heat

Inactive Publication Date: 2019-05-21
安靖茹
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

National patent (application) Nos. 00106171.2, 99123812.5, 03151026.4, 200510126587.1, 200610022223.3 and other patents have announced some methods for improving the friction and wear properties of triethanolamine, but they are all based on the modification of the triethanolamine materia

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] 9.3 kg of pre-dried triethanolamine, 0.5 kg of flake zinc powder, and 0.2 kg of molybdenum disulfide were mixed in a plastic mixer for 1 minute and discharged. The mixed materials were blended and granulated in a twin-screw extruder, and the temperature of the extruder was set at 160° C. to prepare a modified triethanolamine material for a three-layer composite material.

Embodiment 2

[0027] 6.4 kg of pre-dried triethanolamine, 3.0 kg of flake copper powder, and 0.6 kg of polytetrafluoroethylene were mixed in a plastic mixer for 1 minute and discharged. The mixed material was blended and granulated in a twin-screw extruder, and the temperature of the extruder was set at 170° C. to prepare a modified triethanolamine material for a three-layer composite material.

Embodiment 3

[0029] 8.5 kg of pre-dried triethanolamine, 0.5 kg of flake copper powder, 0.5 kg of flake zinc powder, 0.2 kg of molybdenum disulfide, and 0.3 kg of graphite were mixed in a plastic mixer for 2 minutes and discharged. The mixed materials were blended and granulated in a twin-screw extruder, and the temperature of the extruder was set at 185° C. to prepare a modified triethanolamine material for a three-layer composite material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a preparation technology of novel modified triethanolamine. A material is prepared from the following ingredients in percentage by weight content: 64 to 93% of triethanolamine, 5 to 30% of alloyed powder and 2 to 6% of tetrafluoroethylene, wherein the alloyed powder is flaky single powder of copper powder, copper alloy powder or zinc powder or a mixture of the copper powder, the copper alloy powder or the zinc powder; and the tetrafluoroethylene is prepared from single powder of polytetrafluoroethylene, molybdenum disulfide or graphite or a mixture of the polytetrafluoroethylene, the molybdenum disulfide or the graphite. The composite material can be prepared by a plastic processing conventional twin-screw extruder through extrusion and granulation. Compared with the prior art, a three-layer composite material bearing prepared by the invention has the advantages of good heat conductivity, bearing capacity, abrasion resistance and the like.

Description

technical field [0001] The invention belongs to the field of new materials, and in particular relates to a preparation process of novel modified triethanolamine. Background technique [0002] Triethanolamine has good self-lubricating property and low coefficient of friction because of its molecular chain has a smooth profile. And because it is a linear high-crystalline polymer with flexible chains, high crystallinity and large bond energy, it is not easy to transfer to the opposite grinding surface, and it has inherent good wear resistance and high strength. It is a resin whose specific strength is closer to that of metal among all plastics. One of the varieties, it is widely used in the manufacture of various parts in the fields of machinery, automobiles, electronic appliances, etc. [0003] However, when common triethanolamine is used as a friction part under the condition of high relative speed and heavy load, due to insufficient lubrication, the heat generated by fricti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10M161/00C10N30/06
Inventor 安靖茹
Owner 安靖茹
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap