Composite water-lubricated bearing material and preparation method thereof
A water-lubricated bearing and composite technology, applied in the field of composite materials, can solve the problems of low elastic modulus, aging, and large friction coefficient of rubber, and achieve the effect of simple process, excellent friction resistance and good impact resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0041] The invention also provides a method for preparing the composite water-lubricated bearing material, which includes the following steps:
[0042] Step 1. Weigh each raw material according to the above weight parts;
[0043] Step 2: Heat and blend the polyurethane prepolymer and polyethylene oxide sodium at 150-160°C to obtain the first component;
[0044] Step 3. Add polyoxyethylene polyoxypropanolamine ether to the first component to obtain the second component;
[0045] Step 3. Mixing polytetrafluoroethylene, glass fiber, boron carbide and lead powder to obtain the third component;
[0046] Step 4. Add the third component to the second component and mix evenly to obtain the fourth component;
[0047] Step 5. Add 4, 4 to the fourth component / -Methylene bis(3-chloro-2,6-diethylaniline), stir well;
[0048] Step 6. Put the mixed raw materials obtained in step 5 into a mold, and obtain the composite water-lubricated bearing material after demolding and shaping.
[0049] Preferably, t...
Example Embodiment
[0050] Example 1
[0051] The present invention provides a composite water-lubricating bearing material, which is composed of the following raw materials by weight: 100 parts of polyurethane prepolymer; 10 parts of sodium oxide polyethylene; 1.5 parts of polyoxyethylene polyoxypropanolamine ether; 4,4 / -20 parts of methylene bis(3-chloro-2,6-diethyl aniline); 2.5 parts of polytetrafluoroethylene; 3 parts of glass fiber; 8 parts of boron carbide; 8 parts of lead powder. The polyurethane prepolymer is prepared from polytetrahydrofuran polyol and 2,4-toluene diisocyanate (prepared according to a method commonly used in the art), the molar ratio of the polytetrahydrofuran polyol and 2,4-toluene diisocyanate The ratio is 2:1, and the molecular weight of the polytetrahydrofuran polyol is 1000-2000.
[0052] The invention also provides a method for preparing the composite water-lubricated bearing material, which includes the following steps:
[0053] Step 1. Weigh each raw material accord...
Example Embodiment
[0060] Example 2
[0061] The present invention provides a composite water-lubricated bearing material, which is composed of the following parts by weight of raw materials: 100 parts of polyurethane prepolymer; 20 parts of sodium oxide polyethylene; 1.8 parts of polyoxyethylene polyoxypropanolamine ether; 4,4 / -30 parts of methylene bis(3-chloro-2,6-diethyl aniline); 3 parts of polytetrafluoroethylene; 4 parts of glass fiber; 10 parts of boron carbide; 10 parts of lead powder. The polyurethane prepolymer is prepared from polytetrahydrofuran polyol and 2,4-toluene diisocyanate (prepared according to a method commonly used in the art), the molar ratio of the polytetrahydrofuran polyol and 2,4-toluene diisocyanate The ratio is 2:1, and the molecular weight of the polytetrahydrofuran polyol is 1000-2000.
[0062] Step 1. Weigh each raw material according to the above weight parts;
[0063] Step 2. Heat and blend the polyurethane prepolymer and polyethylene oxide sodium at 160°C to obta...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap