Mesoporous silica nanoribbon material and production method thereof

A technology of mesoporous silica and nanobelts, applied in the direction of silica, silica, nanotechnology, etc., to achieve the effects of mild conditions, controllable morphology, and simple synthesis methods

Active Publication Date: 2019-06-11
SHANGHAI UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, as far as we know, the current research focuses on the use of chiral surfactants to prepare chiral mesoporous silica nanobelts, while conventional cationic / anionic surfactants are used as co-templates to prepare mesoporous silica Nanoribbons have rarely been reported

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mesoporous silica nanoribbon material and production method thereof
  • Mesoporous silica nanoribbon material and production method thereof
  • Mesoporous silica nanoribbon material and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] a. Dissolve 0.1 g of cetyltrimethylammonium bromide (CTAB) in 137 mL of deionized water until the solution is clear, then add 1.32 mL of ethyl acetate (EA) and continue to stir evenly;

[0022] b. Add 0.08 g of sodium dodecyl sulfate (SDS) to the above solution, with a molar ratio of 1 to CTAB, and stir well, then add 2.7 mL of ammonia (25-28 wt.%) and continue to stir evenly;

[0023] c. Finally, add 275 µL of tetraethylorthosilicate (TEOS) as the silicon source and continue the reaction for 20 hours. After the reaction is completed, the reactants are centrifuged, washed with deionized water and dried repeatedly, and the white powder obtained is It is a mesoporous silica nanobelt.

[0024] The physical properties of the obtained product were characterized, and some of the results are shown in the attached drawings. The obtained mesoporous silica product has a length between 1 µm and 1.5 µm, a width of about 45 nm, and a ribbon-like structure with curled edges. At the same t...

Embodiment 2

[0026] The preparation process and steps of this embodiment are basically the same as those of embodiment 1, except for step b:

[0027] The amount of sodium dodecyl sulfate (SDS) is 0.04 g.

[0028] The results obtained are significantly different from those of Example 1 in terms of morphology and structure. The product obtained partially presents a closed ring structure, which is mainly composed of nanorods with a length of about 400 nm and a diameter of about 43 nm, and has good properties. The channel characteristics.

Embodiment 3

[0030] The preparation process and steps of this embodiment are basically the same as those of embodiment 1, except for step a:

[0031] The amount of ethyl acetate (EA) is 0.5 mL.

[0032] The results obtained are significantly different from those of Example 1. The obtained product has a layered structure with slight curls on the edges, but is relatively thick and has poor dispersion.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a mesoporous silica nanoribbon material and a production method thereof. A mesoporous silica nanoribbon has relatively-ordered mesoporous channels, the length is 1-1.5 mum, and the width is 45-50 nm. From an SEM picture, the fact that the obtained mesoporous silica nano material is of a unique curly structure can be seen. A TEM result shows that light and shade of edges and the interior of the material are clear, which proves that the edges of the material crimp, and obvious mesoporous channel structures can be observed. The produced ribbon-shaped mesoporous silica nano material has wide application prospects in the fields of environmental catalysis and adsorption, biomedicine and the like due to the fact that the ribbon-shaped mesoporous silica nano material has the unique structure with both inner and outer surfaces capable of being subjected to functional modification.

Description

Technical field [0001] The invention relates to a mesoporous silicon oxide nanobelt material and a preparation method thereof. Background technique [0002] Mesoporous silica nanomaterials have outstanding advantages due to their high specific area, adjustable pore diameter and diversified morphology and structure. Since MCM-41 was first reported by Mobil Corporation in 1992, it has been popular among the materials industry and chemists. Widely concerned about its morphology control, structure control and growth mechanism exploration. The reason why mesoporous silica nanomaterials exhibit many excellent physical and chemical properties is not only related to the unique mesoporous channels of the material, but also related to the macroscopic and microscopic morphology of the material itself. In recent years, scientists have paid more and more attention to the rich appearance and morphology of mesoporous silica while working to control the internal pore structure of mesoporous sil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B33/18B82Y30/00B82Y40/00
Inventor 张海娇宋亭亭
Owner SHANGHAI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com