High-temperature-resistant plastic and production method thereof

A technology of high temperature resistance and plastics, applied in the field of plastics production, can solve the problems that affect the normal use of plastics, plastics are easy to be melted by heat, and the production process is unreasonable, so as to achieve the effect of suitable promotion, superior plastic performance and good use effect

Inactive Publication Date: 2019-06-11
安徽新利清洁用品有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the formula composition and production process of plastics are relatively unreasonable, resulting in the poor high temperature resistance of the obtained plastics. When the external temperature is high, the plastics are easy to be heated and melted, thus affecting the normal use of plastics.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A high temperature resistant plastic, said plastic is made of the following raw materials in parts by weight: 36 parts of polyethylene resin, 22 parts of polyurethane, 12 parts of citric acid ester, 1 part of chlordane anhydride, 9 parts of pentaerythritol phosphate, 7 parts of triazine , 13 parts of magnesium borate, 11 parts of zinc borate, 10 parts of antimony trioxide, 8 parts of mica powder, 4 parts of crosslinking agent, 3 parts of plasticizer, and 2 parts of defoamer.

[0026] Wherein, the crosslinking agent is N-methylolacrylamide, 1,4-butanediol diglycidyl ether, tetramethyl-1,2-ethylenediamine and hexamethylenetetramine One or more; the plasticizer is one or more of butyl benzyl phthalate, dioctyl sebacate, tris (2-carboxyethyl) phosphine and dicyclohexyl phthalate Various; the defoamer is one or more of emulsified silicone oil, polyoxyethylene polyoxypropanolamine ether and polyoxypropylene glyceryl ether.

[0027] A preparation method of high temperature re...

Embodiment 2

[0035] A high temperature resistant plastic, said plastic is made of the following raw materials in parts by weight: 38 parts of polyethylene resin, 24 parts of polyurethane, 13 parts of citric acid ester, 2 parts of chlordane anhydride, 10 parts of pentaerythritol phosphate, and 8 parts of triazine , 14 parts of magnesium borate, 12 parts of zinc borate, 11 parts of antimony trioxide, 9 parts of mica powder, 5 parts of crosslinking agent, 4 parts of plasticizer, and 3 parts of defoamer.

[0036] Wherein, the crosslinking agent is N-methylolacrylamide, 1,4-butanediol diglycidyl ether, tetramethyl-1,2-ethylenediamine and hexamethylenetetramine One or more; the plasticizer is one or more of butyl benzyl phthalate, dioctyl sebacate, tris (2-carboxyethyl) phosphine and dicyclohexyl phthalate Various; the defoamer is one or more of emulsified silicone oil, polyoxyethylene polyoxypropanolamine ether and polyoxypropylene glyceryl ether.

[0037] A preparation method of high temperat...

Embodiment 3

[0045] A high temperature resistant plastic, said plastic is made of the following raw materials in parts by weight: 40 parts of polyethylene resin, 26 parts of polyurethane, 14 parts of citric acid ester, 3 parts of chlordane anhydride, 11 parts of pentaerythritol phosphate, and 9 parts of triazine , 15 parts of magnesium borate, 13 parts of zinc borate, 12 parts of antimony trioxide, 10 parts of mica powder, 6 parts of crosslinking agent, 5 parts of plasticizer, and 4 parts of defoamer.

[0046] Wherein, the crosslinking agent is N-methylolacrylamide, 1,4-butanediol diglycidyl ether, tetramethyl-1,2-ethylenediamine and hexamethylenetetramine One or more; the plasticizer is one or more of butyl benzyl phthalate, dioctyl sebacate, tris (2-carboxyethyl) phosphine and dicyclohexyl phthalate Various; the defoamer is one or more of emulsified silicone oil, polyoxyethylene polyoxypropanolamine ether and polyoxypropylene glyceryl ether.

[0047] A preparation method of high tempera...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides high-temperature-resistant plastic and a production method thereof, and relates to the technical field of plastic production. The plastic is produced from the following raw materials of, in parts by weight, 36-40 parts of polyethylene resin, 22-26 parts of polyurethane, 12-14 parts of citrate, 1-3 parts of chlordane anhydride, 9-11 parts of pentaerythritol octahydrogen tetraphosphate, 7-9 parts of triazine, 13-15 parts of magnesium borate, 11-13 parts of zinc borate, 10-12 parts of antimonous oxide, 8-10 parts of mica powder, 4-6 parts of cross-linking agent, 3-5 parts of plasticizer and 2-4 parts of defoaming agent. According to the plastic, the defects of the prior art are overcome, the high-temperature-resistant performance of the plastic can be effectively improved, the situation that the plastic is heated and melts due to high external temperature to affect normal use of the plastic is prevented, then the quality of the plastic is improved, the plastic is good in the high-temperature-resistant performance, and has a good use effect, meanwhile, the components in the plastic have a synergistic effect, and the plastic is excellent in overall performance andsuitable for popularization.

Description

technical field [0001] The invention relates to the technical field of plastic production, in particular to a high-temperature-resistant plastic and a preparation method thereof. Background technique [0002] Plastic is a kind of synthetic or natural high molecular polymer, which can be kneaded into various shapes and finally can keep the same shape. It has the advantages of light weight, low noise, corrosion resistance and good processing performance. . With the development of the times, the plastics industry, one of the pillar industries of my country's light industry, has maintained a growth rate of more than 10% in recent years. While maintaining a relatively fast development speed, the economic benefits have also improved. The total output value of enterprises above designated size in the plastic products industry ranks third among the 19 major industries of light industry, achieving a product sales rate of 97.8%, which is higher than the average level of the light ind...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L75/04C08K13/06C08K9/04C08K5/11C08K5/521C08K3/38C08K3/22C08K3/34
Inventor 蔡丰富
Owner 安徽新利清洁用品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap