A kind of toughening type phenolic resin and preparation method thereof

The technology of phenolic resin and boron phenolic resin is applied in the field of toughened phenolic resin and its preparation, which can solve the problems of undiminished ablation resistance and interface debonding, and achieves improved ablation resistance, increased interface area, The effect of high surface energy

Active Publication Date: 2022-02-22
AEROSPACE INST OF ADVANCED MATERIALS & PROCESSING TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The present invention adopts fillers such as carboxyl-terminated nitrile rubber and zirconium diboride to synergistically modify the phenolic resin, and solves the problem of resin-based composite materials and metal cabins under the premise that the ablation resistance of the toughened phenolic resin is not reduced. Interface debonding problem after one-piece molding

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of toughening type phenolic resin and preparation method thereof
  • A kind of toughening type phenolic resin and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0036] The present invention provides the preparation method of the toughening type phenolic resin described in the first aspect of the present invention in the second aspect, described method comprises the steps:

[0037] (1) Disperse 0.3 to 0.8 parts (such as 0.3, 0.4, 0.5, 0.6, 0.7 or 0.8 parts) of dispersant in a solvent to obtain a dispersion;

[0038] (2) 100 parts of phenolic resin, 30 to 90 parts (such as 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85 or 90 parts) carboxyl-terminated nitrile rubber and 15 to 90 parts 45 parts (such as 15, 20, 25, 30, 35, 40 or 45 parts) of zirconium diboride are mixed uniformly to obtain a mixture;

[0039] (3) Divide (for example, equally divide) the mixture obtained in step (2) into multiple parts (two parts and more than two parts), and then add multiple parts of the mixture into the dispersion liquid obtained in step (1) and stir Disperse evenly to obtain toughened phenolic resin.

[0040] In particular, "parts" in the present in...

Embodiment 1

[0052] ① Weigh 1 kg of absolute ethanol in a container, add 2.5 g of dispersant in the absolute ethanol solvent and disperse and dissolve with ultrasonic waves to obtain a dispersion.

[0053] ② Weigh 500g of boron phenolic resin powder, 150g of carboxy-terminated nitrile rubber powder, and 75g of zirconium diboride powder in another container, and use a stirring paddle to stir and pre-mix for 0.5h to ensure uniform stirring to obtain a mixture; wherein, the The carboxyl-terminated nitrile rubber powder is selected from nano carboxyl-terminated nitrile rubber powder with an average particle diameter of 50-100 nm.

[0054] ③ Divide the well-mixed mixture into 4 equal parts, add them to the dispersion liquid obtained in ① one by one, stir and ultrasonically disperse for 15 minutes each time, until finally all the mixture is added, and the resin composition is stirred evenly to obtain Toughened phenolic resin.

[0055] After the toughened phenolic resin in this example is cured,...

Embodiment 2

[0057] ① Weigh 1 kg of absolute ethanol in a container, add 2.5 g of dispersant in the absolute ethanol solvent and disperse and dissolve with ultrasonic waves to obtain a dispersion.

[0058] ② Weigh 500g of boron phenolic resin powder, 250g of carboxyl-terminated nitrile rubber powder, and 125g of zirconium diboride powder in another container, and use a stirring paddle to stir and pre-mix for 0.5h to ensure uniform stirring to obtain a mixture; wherein, the The carboxyl-terminated nitrile rubber powder is selected from nano carboxyl-terminated nitrile rubber powder with an average particle diameter of 50-100 nm.

[0059]③ Divide the well-mixed mixture into 4 parts, and add them to the dispersion liquid obtained in ① one by one, stir and ultrasonically disperse for 15 minutes each time, until finally all the mixture is added, and the resin composition is stirred evenly to obtain Toughened phenolic resin.

[0060] After the toughened phenolic resin in this example is cured, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
shear strengthaaaaaaaaaa
particle diameteraaaaaaaaaa
shear strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a toughened phenolic resin and a preparation method thereof. The toughened phenolic resin comprises 100 parts by weight of phenolic resin, 30-90 parts of carboxy-terminated nitrile rubber, 15-45 parts of zirconium diboride and 0.3-0.8 parts of dispersant. The preparation method is as follows: dispersing 0.3-0.8 parts of dispersant in a solvent to obtain a dispersion liquid; uniformly mixing 100 parts of phenolic resin, 30-90 parts of carboxy-terminated nitrile rubber and 15-45 parts of zirconium diboride to obtain Mixed material: Divide the obtained mixed material into multiple parts, then add the multiple parts of the mixed material into the obtained dispersion liquid in sequence, stir and disperse evenly, and obtain a toughened phenolic resin. The present invention adopts fillers such as carboxyl-terminated nitrile rubber and zirconium diboride to modify the phenolic resin. On the premise of ensuring that the ablation resistance of the toughened phenolic resin is not reduced, it solves the problem of the integrated molding of the resin-based composite material and the metal cabin. Interface debonding problem.

Description

technical field [0001] The invention belongs to the technical field of polymer modification, in particular to a toughened phenolic resin and a preparation method thereof. Background technique [0002] With the development of aerospace technology, space has become the "commanding height" for safeguarding national security and interests, and various countries are paying more and more attention to the development of aircraft. The problem of heat protection is one of the most critical factors that determine the safety of the aircraft and the successful completion of various tasks, and ablation heat protection has always been popular for its simplicity and reliability, so it has always been the focus of space agencies and experts from various countries hot spot. [0003] The ablation material is a special material used on the outer surface of the missile head, the spacecraft re-entry cabin, and the inner surface of the rocket engine. It decomposes, melts, evaporates, sublimates ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L61/14C08L13/00C08K3/38
CPCC08L61/14C08L2201/08
Inventor 谢永旺许孔力郝春功许学伟李峥
Owner AEROSPACE INST OF ADVANCED MATERIALS & PROCESSING TECH