Antibacterial wear-resistant color masterbatch and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of color masterbatch and antibacterial agent, which is applied in the field of antibacterial and wear-resistant color masterbatch and its preparation, can solve the problems of poor antibacterial and wear-resistant effects, improve antibacterial and wear resistance, and alleviate the formation of water mist on the surface The effect of whitening and avoiding decomposition
Inactive Publication Date: 2019-07-12
ANHUI JIHONG MATERIAL TECH
View PDF3 Cites 13 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
The existing method for preparing color masterbatch has poor antibacterial and wear-resistant effect
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0024] An antibacterial and wear-resistant color masterbatch, composed of the following mass ratios, specifically as follows:
[0025] 50 parts of polyvinyl chloride;
[0026] 6 parts of calcium zinc heat stabilizer;
[0027] 20 parts of filler calcium carbonate;
[0028] 20 parts of chlorinated polyethylene;
[0029] 2 parts colorant;
[0030] 1 part lubricant;
[0031] Antioxidant phosphite 1 part;
[0032] 1 part polyethylene wax;
[0033] 20 parts of environmentally friendly plasticizers;
[0034] 1 part of ultraviolet absorber UV-P;
[0035] 15 parts of antibacterial agent;
[0036] 5 parts of anti-wear agent.
Embodiment 2
[0038] An antibacterial and wear-resistant color masterbatch, composed of the following mass ratios, specifically as follows:
[0039] 80 parts of polyvinyl chloride;
[0040] 10 parts of calcium zinc heat stabilizer;
[0041] 30 parts of filler calcium carbonate;
[0042] 30 parts of chlorinated polyethylene;
[0043] 5 parts of colorant;
[0044] 3 parts lubricant;
[0045] Antioxidant phosphite 2 parts;
[0046] 2 parts polyethylene wax;
[0047] 30 parts of environmentally friendly plasticizers;
[0048] 2 parts of ultraviolet absorber UV-P;
[0049] 20 parts of antibacterial agent;
[0050] 10 parts of anti-wear agent.
Embodiment 3
[0052] An antibacterial and wear-resistant color masterbatch, composed of the following mass ratios, specifically as follows:
[0053] 60 parts of polyvinyl chloride;
[0054] 7 parts of calcium zinc heat stabilizer;
[0055] 22 parts of filler calcium carbonate;
[0056] 22 parts of chlorinated polyethylene;
[0057] 3 parts coloring agent;
[0058] 2 parts lubricant;
[0059] Antioxidant phosphite 2 parts;
[0060] 1 part polyethylene wax;
[0061] 24 parts of environmentally friendly plasticizers;
[0062] 1 part of ultraviolet absorber UV-P;
[0063] 17 parts of antibacterial agent;
[0064] 7 parts of anti-wear agent.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
degree of polymerization
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses an antibacterial wear-resistant color masterbatch. The color masterbatch comprises the following components: 50 to 80 parts of polyvinyl chloride, 6 to 10 parts of a calcium zinc heat stabilizer, 20 to 30 parts of filler calcium carbonate, 20 to 30 parts of chlorinated polyethylene, 2 to 5 parts of a colorant, 1 to 3 parts of a lubricant, 1 to 2 parts of antioxidant phosphite ester, 1 to 2 parts of polyethylene wax, 20 to 30 parts of an environment-friendly plasticizer, 1 to 2 part of an ultraviolet absorber, 15 to 20 parts of an antibacterial agent, and 5 to 10 parts of a wear-resistant agent. A preparation method of the antibacterial wear-resistant color masterbatch comprises the following steps: (1), adding the polyvinyl chloride and the chlorinated polyethyleneinto a high-speed mixer according to certain mass parts, so as to perform high-speed mixing; (2), reducing the temperature to room temperature after the plasticizer is sufficiently absorbed by the polyvinyl chloride and the chlorinated polyethylene; (3), adding the blended materials into a double-screw extruder. The formed antibacterial wear-resistant color masterbatch can improve the antibacterial and wear-resistant effect of a polyvinyl chloride product, and has the advantages of stable performance, high coloring power, good dispersibility, high safety in use, high environmental protection property and high nontoxicity.
Description
technical field [0001] The invention relates to the technical field of color masterbatch application, in particular to an antibacterial and wear-resistant color masterbatch and a preparation method thereof. Background technique [0002] A plastic colorant that is well dispersed with a high proportion of pigments or additives and thermoplastic resins. The selected resin has a good wetting and dispersing effect on the colorant, and has good compatibility with the material to be colored. That is: pigment + carrier + additive = masterbatch. Material The natural color resin and colorant are mixed, kneaded, and granulated into colored plastics, which are used in the molding process. Dry powder coloring: the powder colorant is evenly mixed with the natural color resin and used directly to make plastic products. Masterbatch coloring is the most commonly used plastic coloring method today. In the existing method for preparing color masterbatch, the obtained product has poor antiba...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more