A kind of lanthanum modified high hardness alloy and casting method thereof

A high-hardness, alloy technology, applied in the preparation of wear-resistant and corrosion-resistant cast iron, and the manufacture of mechanical wear-resistant parts, can solve the problems of low strength index, insufficient impact toughness, low bending strength, etc.

Active Publication Date: 2022-03-11
CENT SOUTH UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The hardness of this type of alloy is high, but the impact toughness is insufficient, the strength index is low, and the bending strength is low, in the range of 346-477MPa, which limits the application of this alloy to some occasions where the external load is large and impact resistance is required.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of lanthanum modified high hardness alloy and casting method thereof
  • A kind of lanthanum modified high hardness alloy and casting method thereof
  • A kind of lanthanum modified high hardness alloy and casting method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] Embodiment 1. adopt iron powder and La 2 o 3 After the powder is evenly mixed, it is molded into a powder briquette. La 2 o 3 The mass ratio of iron powder to iron powder is roughly 1:4, that is, Fe-La of Fe-17.05wt.%La is formed 2 o 3 Mixed briquettes. As a carrier for the modification of rare earth La.

[0054] Select high-carbon ferrochrome, micro-carbon ferrochrome, ferroboron, ferro-niobium, ferro-vanadium, industrial pure iron and the above-mentioned Fe-La 2 o 3 Mixed briquettes are used as raw materials, and the composition range is as follows: Cr: 10.0wt.%; B: 2.9wt.%; C: 0.7wt.%; Nb: 0.4wt.%; V: 0.2wt.%; La: 0.5wt.% %; See Table 2 for the control of impurity elements. Small amounts of impurities such as Al, Mn, N, etc. do not cause fundamental changes in alloy properties and are therefore not listed in Table 2. After weighing the corresponding raw materials according to the composition requirements, induction melting and sand mold casting are adopted....

Embodiment 2

[0057] Embodiment 2. adopt iron powder and La 2 o 3 After the powder is evenly mixed, it is molded into a powder briquette. La 2 o 3The mass ratio of iron powder to iron powder is roughly 1:20, that is, Fe-La of Fe-4.06wt.%La is formed 2 o 3 Mixed briquettes. As a carrier for the modification of rare earth La.

[0058] Select high-carbon ferrochrome, metal chromium, ferroboron, ferroniobium, industrial pure iron and the above-mentioned Fe-La 2 o 3 Mixed briquettes are used as raw materials, and the composition range is as follows: Cr: 10.0wt.%; B: 2.7wt.%; C: 0.7wt.%; Nb: 0.5wt.%; La: 0.05wt.%; control of impurity elements is shown in the table 2. Small amounts of impurities such as Al, Mn, N, etc. do not cause fundamental changes in alloy properties and are therefore not listed in Table 2. After weighing the corresponding raw materials according to the composition requirements, the vacuum induction furnace can be used for melting and water-cooled iron mold casting. ...

Embodiment 3

[0060] Embodiment 3. adopt iron powder and La 2 o 3 After the powder is evenly mixed, it is molded into a powder briquette. La 2 o 3 The mass ratio of iron powder to iron powder is roughly 1:10, that is, Fe-La of Fe-7.75wt.%La is formed 2 o 3 Mixed briquettes. As a carrier for the modification of rare earth La.

[0061] Select high-carbon ferrochrome, micro-carbon ferrochrome, ferroboron, ferroniobium, industrial pure iron and the above-mentioned Fe-La 2 o 3 Mixed briquettes are used as raw materials, and the composition range is as follows: Cr: 10.0wt.%; B: 2.7wt.%; C: 0.8wt.%; Nb: 0.6wt.%; La: 0.3wt.%. The control of impurity elements is shown in the table 2. Small amounts of impurities such as Al, Mn, N, etc. do not cause fundamental changes in alloy properties and are therefore not listed in Table 2. After weighing the corresponding raw materials according to the composition requirements, induction melting and investment casting are adopted. The specific steps ar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flexural strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

A lanthanum-modified high-hardness alloy and its casting method, the content of each element of the alloy is Cr: 9.0-13.0, B: 2.6-2.9, C: 0.7-0.9, Nb: 0.4-0.8, V: 0.4-0.8, Mn The content is less than 0.3, La: 0.03-0.7, the balance is Fe, the total amount of C and B is 3.3-3.6; the C / Cr content ratio: 0.06-0.08; the total amount of Nb and V is 0.5-1.0, first prepare Fe ‑La 2 o 3 , Fe-lanthanum carbonate or Fe-lanthanum nitrate powder briquette, alloy ingredients, smelting and modification treatment, and casting alloy, the casting temperature range is 1250 ~ 1320 ℃. The alloy of the present invention has HRC66.2~71.0, and the impact toughness reaches 8.6~14.6J / cm 2 , the bending strength reaches 800~1345MPa.

Description

technical field [0001] The invention belongs to the field of high-hardness wear-resistant cast iron, and relates to a preparation method of wear-resistant and corrosion-resistant cast iron composed of fine hard phases modified by rare earth lanthanum, supersaturated solid solution and martensitic matrix phase, which can be widely used in machinery, chemical industry, Manufacture of mechanical wear-resistant parts in electric power, metallurgy, and other industries. [0002] technical background [0003] Fe-Cr-B-C wear-resistant casting alloy is mainly composed of Fe 2 B or M 2 B is a hard phase, which has good toughness, high hardness, high corrosion resistance, good smelting-casting processability, and has very broad application prospects. [0004] Modification treatment is one of the effective methods to improve the microstructure and mechanical properties of Fe-Cr-B-C alloy. Modifiers can be divided into strong carbon, nitrogen, and sulfide forming elements according to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/32C22C38/04C22C38/26C22C38/24C22C33/06
CPCC22C38/32C22C38/005C22C38/04C22C38/26C22C38/24C22C33/06C22C33/006
Inventor 罗丰华卢静王冠刘浪飞吴卫文王哲
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com