14K corrosion-resistant brittleness-resistant alloy with Spangold effect and process thereof

A corrosion-resistant, alloying technology, applied in the field of alloys, can solve the problems of limiting product share, affecting market sales and user experience, and achieving the effect of corrosion resistance and stability

Inactive Publication Date: 2019-07-26
杭州辰卓科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The problems in the Span alloy industry have not been resolved for a long time, which not only affects the market sales and user experience of this type of product, but also seriously limits the share of this type of product in the international market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A 14K corrosion-resistant and brittle-fracture-resistant gold alloy with the Spank effect and its technology. In terms of weight percentage, the composition of the alloy is: In: 4.2wt.%, Ni: 5.0wt.%, Y: 0.4wt.%, Ta: 0.2wt.%, Re: 2.1wt.%, Ge: 0.1wt. %, Cr: 0.5wt.%, Au: 58.0wt.%, and the balance is silver.

[0018] The method for preparing and using the above-mentioned 14K corrosion-resistant and brittle-fracture-resistant gold alloy with the Spank effect includes the following steps: (a) batching: weighing the raw materials according to the above mass percentage; (b) smelting: using argon Melting is carried out in a non-vacuum induction melting furnace protected by gas, in which the crucible is a graphite crucible; the alloy melt is fully stirred at 1160 degrees for 10 minutes and fully stirred by electromagnetic stirring, and then cast in an iron mold, and rapidly cooled by water cooling; (c ) Subsequent pressure processing and heat treatment: the obtained ingot is rol...

Embodiment 2

[0021] A 14K corrosion-resistant and brittle-fracture-resistant gold alloy with the Spank effect and its technology. In terms of weight percentage, the composition of the alloy is: In: 5.0wt.%, Ni: 6.2wt.%, Y: 0.4wt.%, Ta: 0.5wt.%, Re: 2.0wt.%, Ge: 0.2wt. %, Cr: 0.7wt.%, Au: 59.0wt.%, and the balance is silver.

[0022]The method for preparing and using the above-mentioned 14K corrosion-resistant and brittle-fracture-resistant gold alloy with the Spank effect includes the following steps: (a) batching: weighing the raw materials according to the above mass percentage; (b) smelting: using argon Melting is carried out in a non-vacuum induction melting furnace protected by gas, in which the crucible is a graphite crucible; the alloy melt is fully stirred at 1160 degrees for 10 minutes and fully stirred by electromagnetic stirring, and then cast in an iron mold, and rapidly cooled by water cooling; (c ) Subsequent pressure processing and heat treatment: the obtained ingot is roll...

Embodiment 3

[0025] A 14K corrosion-resistant and brittle-fracture-resistant gold alloy with the Spank effect and its technology. In terms of weight percentage, the composition of the alloy is: In: 4.8wt.%, Ni: 6.0wt.%, Y: 0.5wt.%, Ta: 0.3wt.%, Re: 2.4wt.%, Ge: 0.1wt. %, Cr: 0.5wt.%, Au: 58.0wt.%, and the balance is silver.

[0026] The method for preparing and using the above-mentioned 14K corrosion-resistant and brittle-fracture-resistant gold alloy with the Spank effect includes the following steps: (a) batching: weighing the raw materials according to the above mass percentage; (b) smelting: using argon Melting is carried out in a non-vacuum induction melting furnace protected by gas, in which the crucible is a graphite crucible; the alloy melt is fully stirred at 1160 degrees for 10 minutes and fully stirred by electromagnetic stirring, and then cast in an iron mold, and rapidly cooled by water cooling; (c ) Subsequent pressure processing and heat treatment: the obtained ingot is rol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a 14K corrosion-resistant brittleness-resistant alloy with a Spangold effect and a process thereof. The 14K corrosion-resistant brittleness-resistant alloy with the Spangold effect comprises, by weight, 4.0%-6.0% of In, 5.0%-8.0% of Ni, 0.2%-0.6% of Y, 0.2%-0.5% of Ta, 2.0%-2.5% of Re, 0.1%-0.2% of Ge, 0.4%-0.8% of Cr, 58.0%-59.0% of Au, and the balance sliver. The 14K corrosion-resistant brittleness-resistant alloy has the Spangold effect and is applied to jewelry, and gold jewelry prepared from the 14K corrosion-resistant brittleness-resistant alloy has a bright colorof pearl spots. The jewelry prepared from the 14K corrosion-resistant brittleness-resistant alloy has an outstanding surface impression, the smelting and processing technique is simple, and thus, the14K corrosion-resistant brittleness-resistant alloy with the Spangold effect has great economic value while meeting the urgent demands of domestic and foreign markets in the jewelry industry.

Description

technical field [0001] The invention relates to the technical field of alloys, in particular to a gold-based alloy. Background technique [0002] Pure gold has a very beautiful yellow luster and is chemically stable. It is not easy to change color when heated, that is, it has excellent anti-oxidation properties. Throughout history and consumer markets at home and abroad, gold has always been used as a jewelry material and is favored by people. With the improvement of modern consumption awareness, the patterns of jewelry made of gold are constantly being refurbished. In the past, single gold jewelry was gradually replaced by beautiful and various gold alloys. In addition to being used for jewelry, these gold alloys are also mostly used for watch cases, watch straps, spectacle frames and various handicrafts. In addition to having different colors (commonly white, yellow, red and pink), these gold alloys have good chemical stability, good surface anti-tarnish performance, a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C5/02C22C1/02C22F1/14C22F1/02
CPCC22C1/02C22C5/02C22F1/002C22F1/02C22F1/14
Inventor 刘亚军
Owner 杭州辰卓科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com