Uncoated digital ink jet transfer printing base paper and production method thereof

A technology of transfer printing base paper and digital inkjet, applied in the field of papermaking, can solve the problems of loss of energy saving and insufficient drying ability in digital technology

Pending Publication Date: 2019-08-06
ZHEJIANG UNIVERSITY OF SCIENCE AND TECHNOLOGY
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] When printing on a multi-nozzle printer, the ink drying ability of the transfer paper is severely challenged. If the drying ability is insufficient, it is necessary to add a high-power oven lamp for heating and drying.
And the high-power baking lamp makes the digital technology lose the feature of energy saving

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] An uncoated digital inkjet transfer printing base paper, made of the following components in weight percentage: 50 parts of bleached chemical hardwood pulp fiber, 50 parts of bleached machine bamboo pulp fiber, 5 parts of inorganic filler, 0.2 parts of chemical auxiliary parts, 6.0 parts of dipping treatment solution.

[0024] The inorganic fillers are titanium dioxide and precipitated calcium carbonate, the particle size of the inorganic fillers ranges from 0.2 to 0.6 μm, and the chemical additives are wet strength agents and internal sizing agents in a weight ratio of 1:2.0; among them, the wet strength agent is PAE; the internal sizing agent The agent is a mixture of alkyl ketene dimer (AKD) and cationic starch in a weight ratio of 5:1.

[0025] The impregnation treatment liquid is a mixture of rod-shaped nano-silica, cationic starch and modified chitosan, the weight ratio is 8: 2: 1, the mass concentration of the mixture is controlled at 4%, and the rod-shaped nano-...

Embodiment 2

[0034] An uncoated digital ink-jet transfer printing base paper is made of the following components in weight percentage: 80 parts of bleached chemical hardwood pulp fibers, 20 parts of bleached machine bamboo pulp fibers, 15 parts of inorganic fillers, and 1.0 parts of chemical additives parts, 1.5 parts of dipping treatment solution.

[0035] The inorganic fillers are titanium dioxide, precipitated calcium carbonate and china clay, the particle size of the inorganic fillers ranges from 0.2 to 0.6 μm, the chemical additives are wet strength agents and internal sizing agents in a weight ratio of 1:5.0, the wet strength agents are PAE, and internal sizing agents The agent is a mixture of alkyl ketene dimer (AKD) and cationic starch in a weight ratio of 10:1.

[0036] The impregnation treatment solution is a mixture of rod-shaped nano-silica, cationic starch and modified chitosan, with a weight ratio of 10: 2: 1, and the mass concentration of the mixture is controlled at 8%. The...

Embodiment 3

[0045] An uncoated digital ink-jet transfer printing base paper is made of the following components in weight percentage: 65 parts of bleached chemical hardwood pulp fibers, 35 parts of bleached machine bamboo pulp fibers, 10 parts of inorganic fillers, and 0.6 parts of chemical additives parts, 3.0 parts of dipping treatment solution.

[0046] The inorganic fillers are titanium dioxide and china clay, the particle size of the inorganic fillers ranges from 0.2 to 0.6 μm, and the chemical additives are wet strength agents and internal sizing agents in a weight ratio of 1:3.5, wherein the wet strength agent is PAE; the internal sizing agent is A mixture of alkyl ketene dimer (AKD) and cationic starch in a weight ratio of 7.5:1.

[0047] The impregnation treatment liquid is a mixture of rod-shaped nano-silica, cationic starch and modified chitosan, the weight ratio is 9: 2: 1, the mass concentration of the mixture is controlled at 6%, and the rod-shaped nano-silica in the impregn...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides uncoated digital ink jet transfer printing base paper and a production method thereof. The uncoated digital ink jet transfer printing base paper comprises plant fiber and an inorganic filler, wherein an impregnation treatment agent is filled between the plant fiber and the inorganic filler. The invention also discloses the preparation method of the uncoated ink jet transferprinting base paper, and the preparation method comprises the following steps: base paper is prepared by pulping, blending pulp, forming, squeezing and drying; the base paper is further subjected to impregnation treatment; an impregnation liquid penetrates into the base paper and wraps the surfaces of the plant fiber and the inorganic filler on the surface layer of the base paper; and the uncoatedink jet transfer printing base paper can be obtained after subsequent drying and calendering. The uncoated digital ink jet transfer printing base paper has the advantages that the paper surface is flat without warping, ink on the paper surface is easy to dry, the gloss of the ink is not reduced, and the transfer printing is uniform.

Description

technical field [0001] The invention relates to the technical field of papermaking, in particular to a transfer printing base paper and a production method thereof. Background technique [0002] Transfer printing is one of the more popular printing methods today. Its advantages are artistic patterns, fine outlines, clear layers, lifelike shapes, relatively simple processing, and no pollution, less investment, energy saving, and small equipment footprints. Transfer printing is to print the dye on the transfer printing paper first, and then transfer the dye from the transfer printing paper to the textile through heat treatment, so as to form the desired pattern on the textile. [0003] The preparation of digital inkjet sublimation transfer paper is generally to coat a layer of ink-absorbing ink layer or barrier layer on the base paper. On the one hand, it can absorb ink, and on the other hand, it can prevent the disperse dyes in the ink from penetrating In the paper fiber, it...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D21H11/12D21H11/02D21H17/67D21H17/00D21H17/68D21H17/29D21H17/24D21H21/20D21H21/16D21F11/02
CPCD21F11/02D21H11/02D21H11/12D21H17/24D21H17/29D21H17/675D21H17/68D21H17/74D21H21/16D21H21/20
Inventor 胡志军张诚骆华英许银超翟睿金光范
Owner ZHEJIANG UNIVERSITY OF SCIENCE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap