Metal surface dewaxing agent

A metal surface and wax remover technology, applied in the field of metal surface treatment, can solve the problems of low wax removal efficiency and workpiece corrosion, and achieve the effect of improving wax removal efficiency, softening wax layer, and increasing dissolution

Inactive Publication Date: 2019-08-23
梁生
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The technical problem to be solved by the present invention is to provide a metal surface wax remover for the problems of low wax removal efficiency and easy corrosion of workpieces in current wax removers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0024] The preparation method of solubilizing additive is:

[0025] (1) Take Span-80, add alkanolamide and 6# solvent oil according to the mass ratio of 2~5:1~3:10~20, pass through nitrogen protection, stir and mix for 30~50min to obtain a mixed solution, and then add to mix Azobisisobutyronitrile with a liquid mass of 1~3% is kept at 50~60°C for 60~90min to obtain a mixed solution a;

[0026] (2) In parts by mass, take 5~8 parts of acrylamide, 3~6 parts of 2-acrylamido-2-methylpropanesulfonic acid, 3~7 parts of hexadecyl allyl ammonium chloride, 0.1~0.4 parts of ammonium persulfate, 80~100 parts of water, stirred and mixed at 30~40°C for 30~40 minutes to obtain mixed solution b, take mixed solution b and add mixed solution a according to the mass ratio of 3~5:10~15, and pass Into nitrogen protection, add sodium bisulfite with 4-8% mass of mixed liquid b, heat up to 60-70°C for 3-5h, cool to room temperature, and obtain the solubilizing additive.

[0027] The oleic acid addi...

Embodiment 1

[0036] The preparation method of solubilizing additive is:

[0037] (1) Take Span-80, add alkanolamide and 6# solvent oil at a mass ratio of 2:1:10, pass through nitrogen protection, stir and mix for 30 minutes to obtain a mixed solution, and then add azodicarbonate with 1% mass of the mixed solution Isobutyronitrile, heat preservation at 50°C for 60 minutes to obtain the mixed solution a;

[0038] (2) In parts by mass, take 5 parts of acrylamide, 3 parts of 2-acrylamido-2-methylpropanesulfonic acid, 3 parts of hexadecyl allyl ammonium chloride, 0.1 part of ammonium persulfate, Stir and mix 80 parts of water at 30°C for 30 minutes to obtain mixed solution b. Take mixed solution b and add mixed solution a at a mass ratio of 3:10, pass through nitrogen protection, add 4% sodium bisulfite by mass of mixed solution b, and heat up Keep warm at 60°C for 3 hours, and cool to room temperature to obtain the solubilizing additive.

[0039] The oleic acid additive is as follows: in par...

Embodiment 2

[0048] The preparation method of solubilizing additive is:

[0049] (1) Take Span-80 and add alkanolamide and 6# solvent oil according to the mass ratio of 4:2:15, pass through nitrogen protection, stir and mix for 40 minutes to obtain a mixed solution, and then add azobis Isobutyronitrile, heat preservation at 55°C for 70 minutes to obtain a mixture a;

[0050] (2) In parts by mass, take 3 parts of acrylamide, 5 parts of 2-acrylamido-2-methylpropanesulfonic acid, 5 parts of hexadecyl allyl ammonium chloride, 0.3 parts of ammonium persulfate, Stir and mix 90 parts of water at 35°C for 35 minutes to obtain mixed solution b. Take mixed solution b and add mixed solution a according to the mass ratio of 4:13, pass through nitrogen protection, add 6% sodium bisulfite by mass of mixed solution b, and heat up Insulate at 65°C for 4 hours, and cool to room temperature to obtain the solubilizing additive.

[0051] The oleic acid additive is as follows: in parts by mass, 15 parts of t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a metal surface dewaxing agent, and belongs to the field of metal surface treatment. A prepared solubilizing additive is a polymer with amphiprotic hydrophobic association prepared by emulsifying through the compounding of Span-80 and alkanolamide, and the grafted-copolymerization of acrylamide and 2-acryloylamino-2-methallyl sulfonate, and has high stability, corrosion resistance and an anti-static performance; an adhered waxy molecule is quickly dispersed in water by utilizing a hydrophilic group, so that the dewaxing efficiency is improved; a prepared adsorption corrosion-inhibition protection agent is added with benzyl chloride and epoxy chloropropane so as to carry out quaterisation, and a film can be quickly formed on ta metal surface by utilizing a good micelle assembling performance, so that a workpiece protection performance is improved; and an added dewaxing cleaning active agent is compounded by fatty alcohol polyoxyethylene ether and the like, and the solvent is used for solubilizing so as to accelerate the stripping speed, so that the dewaxing efficiency is improved, and a workpiece is protected. The metal surface dewaxing agent provided by theinvention solves the problems that a current dewaxing agent is low in dewaxing efficiency and easy to corrode the workpiece.

Description

technical field [0001] The invention belongs to the field of metal surface treatment, in particular to a metal surface wax remover. Background technique [0002] In recent years, with the continuous improvement of people's living standards and industrial technology, various metal products, electronics, precision industry and other products have been widely used in industrial production and people's daily life, and the market demand is also relatively large; various metal and Metal alloys have excellent physical and chemical properties and surface treatment characteristics, and are widely used. In order to improve their comprehensive performance, surface finish and decorative effect, surface finishing treatment must be carried out. Among them, mechanical polishing with special polishing wax is the first step in surface finishing treatment. Effective surface polishing process; for example, car glazing wax and polishing agent are used to protect, clean and polish the outer surf...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23G5/06
CPCC23G5/06
Inventor 梁生
Owner 梁生
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com