Preparation method of resin substituting home decoration material

A technology for resin and home improvement, applied in the field of resin replacement for home improvement materials, can solve the problems of wood being easily corroded, air pollution, frequent natural disasters, etc., to reduce wood loss, improve overall performance, and prevent natural disasters.

Active Publication Date: 2019-08-30
天津岐塑科技有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, wood is used in large quantities, which has caused a large number of trees to be cut down by humans, resulting in serious soil erosion, climate warming, serious air pollution, and frequent natural disasters; wood is also easily corroded and insect-eaten; It is easy to deform when soaked in water; and the current artificial wood board contains a large amount of formaldehyde, which is very harmful to the human body
The ceramic floor tiles or wall tiles used for home decoration are relatively bulky, which puts a lot of load on the house or the floor, and the ceramics are fragile, which makes logistics very difficult

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of resin substituting home decoration material
  • Preparation method of resin substituting home decoration material
  • Preparation method of resin substituting home decoration material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A preparation method of resin substitute home decoration material, comprising the steps of:

[0039] Step 1: The first resin is ABS. First, dry the ABS. Dry the ABS at 80°C for 2 hours to reduce the moisture content to 0.13%, so as to prevent the moisture from being heated and evaporated during the molding process, which will cause the resin to crack. Bubbles, expansion, and problems such as silver threads, bubbles, poor transparency, and paste spots on the product, and then heat the dried ABS at 180°C, and then fill the heated ABS into the double-shot resin In the A barrel of the molding machine, the temperature of the A barrel of the two-shot resin molding machine is equal to the ABS heating temperature;

[0040] Step 2: Use PMMA as the second resin. First, dry the PMMA. Dry the PMMA at 80°C for more than 3 hours to reduce the moisture content to 0.13%. Then heat the dried PMMA. The PMMA heating temperature is 160°C. Then add fluorescent powder and pigment into the h...

Embodiment 2

[0048] A preparation method of resin substitute home decoration material, comprising the steps of:

[0049] Step 1: The first resin is made of PP, which is very stable to water, and its water absorption rate in water is only 0.01%, so there is no need to dry it, and then heat the PP at 220°C, and then fill the heated PP Into the A barrel of the two-shot resin molding machine, the temperature of the A barrel of the two-shot resin molding machine is equal to the PP heating temperature;

[0050] Step 2: Use PC as the second resin. First, dry the PC at 120°C for more than 18 hours to reduce the water content to 0.03%. Then heat the dried PC at 330°C. Add fluorescent powder and pigment into the heated PC, stir evenly, then fill the stirred PC into the B barrel of the double-shot resin molding machine, the temperature of the B barrel of the double-shot resin molding machine is equal to the PC heating temperature ;

[0051] Step 3: Use three-dimensional numerical control technology...

Embodiment 3

[0058] A preparation method of resin substitute home decoration material, comprising the steps of:

[0059] Step 1: The first resin is PC+ABS resin. PC+ABS resin is a copolymer blended with 30% ABS and 70% PC, and has the comprehensive characteristics of both PC and ABS. For example, the easy processing characteristics of ABS and the excellent mechanical properties and thermal stability of PC, the ratio of the two will affect the thermal stability of PC+ABS resin, and the mixed material of PC+ABS resin also shows excellent flow characteristics. First, PC +ABS resin for drying treatment, dry the PC+ABS resin at 100°C for 3 hours to reduce the moisture to 0.04%, then heat the PC+ABS resin, the heating temperature of the PC+ABS resin is 240°C, and then heat the The final PC+ABS resin is filled into the A barrel of the two-shot resin molding machine, and the temperature of the A barrel of the two-shot resin molding machine is equal to the heating temperature of the PC+ABS resin; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of a resin substituting home decoration material. First resin and second resin are used, in-mold decoration adding injection molding is carried out, a resinproduct with a tile effect or a wood board effect can be produced, and inlaying, installing and inserting can be conveniently carried out on to-be-decorated surfaces of furniture and walls as the product is thin. The mass of the resin substituting home decoration material is smaller than wood and ceramics, and the bearing force of a building can be reduced in the aspect of carrying; the resin substituting home decoration material can replace the wood, the wood loss can be reduced, and a contribution is made to governing global warming and air pollution and preventing natural disasters of a country; the resin substituting home decoration material is not prone to being corroded and damaged by worms; the water seepage resistance is better; and the resin substituting home decoration materialdoes not contain formaldehyde and other substances harmful to the bodies. The resin substituting home decoration material is formed by an injection mold, has the high production efficiency and low production cost, and is more suitable for meeting the needs of users.

Description

technical field [0001] The invention relates to the field of making decorative boards, in particular to a method for preparing a resin substitute home decoration material. Background technique [0002] Today, with the rapid development of the country and the continuous improvement of people's living standards, the requirements for home decoration and furniture are getting higher and higher, and various artistic styles appear, such as European style and rural style. The home improvement materials are basically wood and ceramics, and the main material of furniture is wood. However, wood is used in large quantities, which has caused a large number of trees to be cut down by humans, resulting in serious soil erosion, climate warming, serious air pollution, and frequent natural disasters; wood is also easily corroded and insect-eaten; It is easy to deform when soaked in water; and the current artificial wood board contains a large amount of formaldehyde, which is very harmful to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B29C45/26B29C45/77B29C45/78B29C33/42B29B13/06
CPCB29B13/022B29C45/263B29C45/77B29C45/78B29C2945/76498B29C2945/76531
Inventor 张旭
Owner 天津岐塑科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com