A high-performance fiberboard

A high-performance fiber and basalt fiber technology, applied in the field of fiberboard, can solve problems such as limited application and insufficient mechanical properties, and achieve the effects of promoting interaction, improving mechanical properties, and superior impact resistance

Active Publication Date: 2021-07-16
阜阳大可新材料股份有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing fiberboard has limited its wider application due to its insufficient mechanical properties.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A high-performance fiberboard

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A high-performance fiberboard, which is formed by bonding and pressing the upper surface layer, the middle layer and the lower surface layer through adhesives from top to bottom, wherein the upper surface layer and the lower surface layer are solid wood sheets, and the middle layer is modified filler particles. The particles are made of the following raw materials in parts by weight: modified wood powder 40, modified basalt fiber 10, polymethacrylate powder 5, polytetrafluoroethylene powder 4, polyethylene powder 10, aluminum oxide 3.

[0015] Further, the preparation method of the modified filler particles is as follows: put the modified wood powder and the modified basalt fiber into a mixer, mix them at a speed of 200 rpm for 20 minutes, and then add polymethacrylate powder, polytetrafluoroethylene Powder, polyethylene powder, and alumina, continue to mix and heat to 93°C, then stir for 30 minutes, granulate, and cool to obtain modified filler particles.

[0016] Furt...

Embodiment 2

[0021] A high-performance fiberboard, which is formed by bonding and pressing the upper surface layer, the middle layer and the lower surface layer through adhesives from top to bottom, wherein the upper surface layer and the lower surface layer are solid wood sheets, and the middle layer is modified filler particles. The particles are made of the following raw materials in parts by weight: modified wood powder 50, modified basalt fiber 15, polymethacrylate powder 7, polytetrafluoroethylene powder 5, polyethylene powder 15, aluminum oxide 5.

[0022] Further, the preparation method of the modified filler particles is as follows: put the modified wood powder and the modified basalt fiber into a mixer, mix them at a speed of 250 rpm for 25 minutes, and then add polymethacrylate powder, polytetrafluoroethylene powder, polyethylene powder, and alumina, continue to mix and heat to 94°C, then stir for 35 minutes, granulate, and cool to obtain modified filler particles.

[0023] Furt...

Embodiment 3

[0028] A high-performance fiberboard, which is formed by bonding and pressing the upper surface layer, the middle layer and the lower surface layer through adhesives from top to bottom, wherein the upper surface layer and the lower surface layer are solid wood sheets, and the middle layer is modified filler particles. The particles are made of the following raw materials in parts by weight: modified wood powder 60, modified basalt fiber 20, polymethacrylate powder 10, polytetrafluoroethylene powder 6, polyethylene powder 20, aluminum oxide 6.

[0029] Further, the preparation method of the modified filler particles is as follows: put the modified wood flour and the modified basalt fiber into a mixer, mix them at a speed of 300 rpm for 30 minutes, and then add polymethacrylate powder, polytetrafluoroethylene Powder, polyethylene powder, alumina, continue to mix and heat to 95°C, then stir for 40 minutes, granulate, cool to obtain modified filler particles.

[0030] Further, the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-performance fiberboard, and the prepared board has excellent bending performance and impact performance, and good mechanical performance. Use camphor wood powder, birch wood powder and maple powder to make a reasonable compound, so that the size density of the fiberboard is uniform and the coordination is good, and the wood powder is modified with glucuronolactone, acetaminophen and polyvinyl alcohol treatment, so that it contains a variety of active groups, which is conducive to the glueing with the adhesive components, and at the same time promotes its compatibility with the modified basalt fiber, and improves the mechanical properties of the obtained board; The fiber is modified to form a porous interface on the surface of the basalt, which promotes the interaction of the basalt fiber with the wood fiber and the adhesive, thereby playing a role as a frame, and significantly improving the bending strength and impact toughness of the obtained board.

Description

technical field [0001] The invention belongs to the technical field of fiberboards, in particular to a high-performance fiberboard. Background technique [0002] Fiberboard is a wood-based panel made by interweaving lignocellulosic fibers and utilizing its inherent adhesive properties. It is a wood-based panel made of wood fiber or other vegetable fibers, which are glued under heat and pressure after applying an adhesive. As a new type of high-grade and environmentally friendly base material, fiberboard has been widely adopted by furniture manufacturers in European and American countries, and the domestic high-end panel furniture market has also begun to use this kind of board in large areas. However, the existing fiberboard has limited its wider application due to its insufficient mechanical properties. Contents of the invention [0003] In view of the above problems, the present invention aims to provide a high-performance fiberboard. [0004] The present invention is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B21/02B32B9/00B32B9/04B32B27/06B32B21/12B32B21/14B32B33/00B27D1/04B27K3/02B27K3/50C08L97/02C08L33/10C08L27/18C08L23/06C08K9/08C08K9/02C08K7/10C08K3/22C04B20/02C04B20/06
CPCB27D1/04B27K3/0228B27K3/50B32B5/16B32B21/02B32B21/12B32B21/14B32B33/00B32B2250/03B32B2250/40B32B2262/10B32B2264/025B32B2264/0257B32B2264/067B32B2264/10B32B2264/12B32B2307/546B32B2307/558C04B20/023C04B20/06C08K2003/2227C08L97/02C08L2205/025C08L2205/035C08L33/10C08L27/18C08L23/06C08K9/08C08K9/02C08K7/10C08K3/22C04B14/4643
Inventor 邵跃骅刘池伟胡扬州郭海涛
Owner 阜阳大可新材料股份有限公司