Flexible paint for plastics and preparation method of flexible paint

A technology of flexibility and coating, which is applied in the field of flexible coating and its preparation, can solve the problems of embrittlement of plastic parts and insufficient flexibility of coating, and achieve the effects of improving flexibility, reducing VOC emissions, and low VOC emissions

Inactive Publication Date: 2019-09-20
东莞市瑞盟涂料有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In view of this, the present invention aims at the deficiencies in the prior art, and its main purpose is to provide a flexible coating for plastics and its preparation method, which can effectively solve the problem of insufficient flexibility of the existing coatings and the brittleness of plastic accessories. the problem of

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A kind of flexible paint for plastics, including the following raw materials in mass percentage: solid thermoplastic acrylic resin 70%; bisphenol F type liquid epoxy resin 18%; leveling agent 5%; the rest are ketones and ester solvents . The solid thermoplastic acrylic resin includes the following mass percentage raw materials: 33% styrene; 14% methyl methacrylate; 25% isooctyl acrylate; 14% high chlorinated polypropylene resin; 7% high chlorinated polyethylene resin 1.5% of dibenzoyl peroxide; all the other are acrylic acid monomers containing alkyl, and the preparation method of solid thermoplastic acrylic resin is prior art, and the preparation method of solid thermoplastic acrylic resin is not described in detail at this, the described alkane containing The base acrylic monomer is one of isobornyl methacrylate, isobornyl acrylate, cyclohexyl methacrylate, tert-butyl cyclohexyl methacrylate, and 3.3.5. trimethylcyclohexyl methacrylate one or more species.

[0022] ...

Embodiment 2

[0028] A kind of flexible paint for plastics, including the following raw materials in mass percentage: solid thermoplastic acrylic resin 65%; bisphenol F type liquid epoxy resin 15%; leveling agent 4%; the rest is ketones and ester solvents . The solid thermoplastic acrylic resin includes the following mass percentage raw materials: 30% styrene; 13% methyl methacrylate; 24% isooctyl acrylate; 15% high chlorinated polypropylene resin; 6% high chlorinated polyethylene resin 2.2% of dibenzoyl peroxide; all the other are acrylic acid monomers containing alkyl, the preparation method of solid thermoplastic acrylic resin is prior art, the preparation method of solid thermoplastic acrylic resin is not described in detail at this, the described alkane containing The base acrylic monomer is one of isobornyl methacrylate, isobornyl acrylate, cyclohexyl methacrylate, tert-butyl cyclohexyl methacrylate, and 3.3.5. trimethylcyclohexyl methacrylate one or more species.

[0029] A flexibl...

Embodiment 3

[0035] A kind of flexible coating for plastics, including the following raw materials in mass percentage: 60% of solid thermoplastic acrylic resin; 20% of bisphenol F liquid epoxy resin; 3% of leveling agent; the rest are ketones and ester solvents . The solid thermoplastic acrylic resin comprises the following mass percent raw materials: 34% styrene; 10% methyl methacrylate; 24.5% isooctyl acrylate; 10% high-chlorinated polypropylene resin; 8% high-chlorinated polyethylene resin 2.5% of dibenzoyl peroxide; all the other are alkane-containing acrylic acid monomers, and the preparation method of solid thermoplastic acrylic resin is prior art, and the preparation method of solid thermoplastic acrylic resin is not described in detail at this, and described alkane-containing The base acrylic monomer is one of isobornyl methacrylate, isobornyl acrylate, cyclohexyl methacrylate, tert-butyl cyclohexyl methacrylate, and 3.3.5. trimethylcyclohexyl methacrylate one or more species.

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flexibilityaaaaaaaaaa
Login to View More

Abstract

The invention discloses flexible paint for plastics and a preparation method of the flexible paint. The flexible paint for the plastics comprises the following raw materials in mass percent: 60-70% of solid thermoplastic acrylic resin, 15-20% of bisphenol F liquid epoxy resin, 3-5% of a leveling agent and the balance of ketone and ester solvents. The paint prepared by adopting the formula and method of the invention is applied to the coating of plastic fittings, the flexibility is greatly improved on the premise of guaranteeing that the paint has relatively good adhesive force after the coating and solidification, the plastic fittings do not have a brittle phenomenon, the use requirements are satisfied, the ketone and ester solvents are adopted, and the VOC (volatile organic compounds) emission can be effectively reduced and is extremely low, so that the flexible paint is completely in conformity with environmental protection standards.

Description

technical field [0001] The invention relates to the technology in the field of coatings, in particular to a flexible coating used on plastics and a preparation method thereof. Background technique [0002] Coatings are chemical products widely used in the fields of architectural coating, industrial metal, agricultural and construction equipment coating. Synthetic resin is one of the earliest, largest and most widely used coatings. It has the characteristics of good weather resistance, high adhesion, bright paint film, and convenient construction. Due to the diversity of synthetic resins, a variety of self-drying or drying enamel paints, primers, topcoats, and varnishes are produced. These synthetic resins with different properties are widely used in bridges and other buildings, as well as in the coating fields of machinery, vehicles, ships, and instruments. achieve universal application. Synthetic resin coatings have a wide range of uses. The coatings currently used on ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D151/06C09D163/00C09D7/20
CPCC09D151/06C09D7/20C08L63/00
Inventor 陈解生
Owner 东莞市瑞盟涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com