Preparation method of heat-conducting, high-temperature-resistant and durable lubricant

A durable lubricant and high temperature resistant technology, applied in lubricating compositions, petroleum industry, etc., can solve the problems of high and low temperature resistance, weather resistance, poor production and living needs, etc., and achieve excellent water resistance, excellent temperature applicability, excellent Lubricity and extreme pressure effects

Inactive Publication Date: 2019-09-20
蒋辉
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Thermally conductive silicone grease is a high thermally conductive organic silicon material compound, which can maintain the grease state during use at a temperature of -50~+200°C for a long time, but has outstanding defects such as high and low temperature resistance, water resistance, ozone resistance, and weather aging resistance. Can not meet the needs of real production and life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A method for preparing a heat-conducting, high-temperature-resistant and durable lubricant, comprising the following steps: 1. Weighing each raw material according to a predetermined ratio, adding and melting 1-cyanobenzocyclobutene and terephthaloyl chloride monomer Form a prepolymer. After the prepolymer cools down, add an active diluent to keep it warm. After cooling, add a solution containing a catalyst, mix well, and vacuum evaporate the solvent that dissolves the catalyst. The specific steps are to prepare 1-cyanobenzocyclobutene After heating to 150°C, slowly add terephthaloyl dichloride monomer within 1 hour, keep warm at this temperature for 3 hours, and the two undergo addition melt copolymerization until the system is completely dissolved and uniform to obtain a prepolymer. The phthaloyl chloride monomer is, after the temperature of the prepolymer is lowered to 100°C within 30 minutes, a prepolymer reactive diluent is added to obtain a diluted prepolymer, whic...

Embodiment 2

[0025] A method for preparing a heat-conducting, high-temperature-resistant and durable lubricant, comprising the following steps: 1. Weighing each raw material according to a predetermined ratio, adding and melting 1-cyanobenzocyclobutene and terephthaloyl chloride monomer Form a prepolymer. After the prepolymer cools down, add an active diluent to keep it warm. After cooling, add a solution containing a catalyst, mix well, and vacuum evaporate the solvent that dissolves the catalyst. The specific steps are to prepare 1-cyanobenzocyclobutene After heating to 140°C, slowly add terephthaloyl dichloride monomer within 1 hour, keep warm at this temperature for 3 hours, the two undergo addition melt copolymerization reaction until the system is completely dissolved and uniform, and a prepolymer is obtained. The phthaloyl chloride monomer is, after the temperature of the prepolymer is lowered to 100°C within 30 minutes, a prepolymer reactive diluent is added to obtain a diluted prep...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of a heat-conducting, high-temperature-resistant and durable lubricant. The preparation method comprises the following steps: carrying out addition melting copolymerization on 1-cyanobenzocyclobutene and a paraphthaloyl chloride monomer to form a prepolymer, preparing a borosiloxane ferrocene prepolymer from dimethylchlorosilane and dicyclopentadiene, and reasonably matching the components to obtain the heat-conducting, high-temperature-resistant and durable lubricant; in addition, a plurality of inorganic components, a clean dispersing agent, an antioxidant and polyadamantane-1,3-diformyl-m-phenylenediamine are compounded for blending modification; therefore, the lubricant has a synergistic lubricating effect and excellent lubricating performance, the lubricating performance reaches or exceeds the same level of a graphite type product, and the lubricant is excellent in miscellaneous oil resistance and long in service life. The lubricant is green and environment-friendly, and is a high-performance environment-friendly hot forging working fluid. The lubricant has the advantages of low raw material consumption, low pollution, long effective lubricating time, low labor intensity, long service life of equipment parts and high temperature resistance.

Description

technical field [0001] The invention relates to the technical field of lubricants, in particular to a preparation method of a thermally conductive, high temperature resistant and durable lubricant. Background technique [0002] Today, there are more and more machinery and equipment that need to work at high temperature, so people are looking for high temperature resistant lubricants everywhere to ensure the normal operation of such machinery and equipment. Especially in aerospace technology and atomic energy industry, only high temperature resistant lubricating materials can achieve good lubricating effect under the conditions of ultra-high temperature, ultra-low temperature, high vacuum, strong radiation, and ultra-high pressure. In the past, mineral oil lubricants were used. It is easy to decompose to produce gas and volatile dust, causing fabric pollution and air pollution, and the service life is not long, it needs to be stopped for about 1-2 weeks to replace the lubrica...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C10M169/04C08G83/00C10N30/06C10N30/08C10N30/10C10N30/12
CPCC08G83/00C10M169/044C10M2229/05C10N2030/06C10N2030/08C10N2030/10C10N2030/12C10N2030/26C10N2030/72
Inventor 蒋辉
Owner 蒋辉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap