Preparation method of strengthened nano dispersion alloy

A technology of dispersion strengthening and alloying, which is applied in the preparation of nano-dispersion-strengthening alloys, can solve the problems that the properties of alloys are difficult to meet engineering applications, the addition of nanoparticles is difficult, and the dispersion and distribution of particles are difficult, so as to reduce the floating and sinking speed of particles and reduce the cost. , the effect of uniform distribution

Active Publication Date: 2019-10-25
BEIJING COMPO ADVANCED TECH
View PDF13 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In addition to the above-mentioned problems, the alloy materials prepared by traditional methods have problems such as difficulty in adding nanoparticles, difficulty in controlling their agglomeration in the melt after addition and rapid separation from the melt, and it is difficult to obtain particles in the alloy matrix for a long time Maintaining a state of dispersed distribution, unable to ensure quantitative addition and a long enough suspension stable state to ensure the time requirements for the next step of processing, resulting in the performance of the alloy after forming is difficult to meet the needs of engineering applications

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of strengthened nano dispersion alloy

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] Such as figure 1 As shown, the present invention provides a preparation method of nano-dispersion strengthened alloy, comprising the following steps: heating the metal or alloy to be mixed to form a uniform liquid phase metal or alloy melt; adding nanoparticles to the In the liquid phase metal or alloy melt, each addition is accompanied by emulsification equipment for high-speed shear stirring, so that the moving acceleration of the added nanoparticles reaches G opt , until a uniformly dispersed emulsified suspension is finally formed; the suspension is subjected to subsequent processing to make a nano-dispersion strengthened alloy.

[0026] In the above steps, the size of the added nanoparticles is 1-100nm, in some embodiments, specifically 1nm, 10nm, 20nm, 30nm, 40nm, 50nm, 60nm, 70nm, 80nm, 90nm and 100nm.

[0027] In the above steps, high-speed shear emulsification and dispersion make the final acceleration of the mixed material 30-100G, specifically 30G, 40G, 50G,...

Embodiment 1

[0034] Put 3kg of pure metal copper ingot in a graphite melting furnace and heat it to 1200°C under the protection of nitrogen atmosphere; after the copper ingot is completely melted, add 3g of nano-alumina particles with a particle size of 100nm; Insert the emulsification head into the copper liquid, turn it on and gradually increase the speed to a line speed of 60m / s; after 30 minutes of high-speed shear emulsification and dispersion, add 3g of nano-alumina particles again, and high-speed shear emulsification for 30 minutes again, repeat this process, Up to a total of 30g of nano-alumina particles were added to form a suspension of nano-alumina particles-copper melt; the suspension of nano-alumina particles-copper melt was poured into a mold, and cooled by circulating water for 20 minutes to obtain a nano-alumina particle-copper melt suspension. Alumina dispersion strengthened copper castings.

[0035] The prepared nano-alumina dispersion-strengthened copper castings were te...

Embodiment 2

[0037] Put 2kg of Fe-Cr alloy ingot (Fe-Cr12wt%) in graphite smelting furnace and heat it to 1500°C under the protection of argon atmosphere; after the alloy ingot is completely melted, add 10g of nanometer yttrium oxide particles with a particle size of 80nm; The emulsification head of the high-speed shear emulsification disperser extends into the tin liquid, turns on and gradually increases the speed to a line speed of 40m / s; after 20 minutes of high-speed shear emulsification and dispersion, the nano-yttrium oxide particles-iron-chromium alloy melt is suspended The solution was poured into the mold and cooled rapidly by circulating water for 15 minutes to obtain nano-yttrium oxide dispersion-strengthened iron-chromium alloy castings.

[0038] The obtained nano-yttrium oxide dispersion-strengthened iron-chromium alloy casting was tested for particle distribution and performance. The results showed that in the prepared nano-yttrium oxide dispersion-strengthened iron-chromium a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a strengthened nano dispersion alloy. The method comprises the following steps that to-be-mixed metals or alloys are heated, and a liquid phase metal or alloy melt is formed; nanoparticles are added into the liquid phase metal or alloy melt in batches, equipment is used for performing shear emulsification dispersion each time the nanoparticles are added, the added nanoparticles are made to move in the melt at the acceleration speed Gopt, and finally, mixture dispersed turbid liquid is formed; and the mixture dispersed turbid liquid is subjectedto subsequent processing process treatment, and the strengthened nano dispersion metal or alloy is prepared. Preparation devices include the mixing container, the heating device and the emulsificationdevice. The emulsification device comprises a rotor and a stator, and gaps allowing the melt to pass through are formed in the peripheral side walls of the stator. According to the preparation methodand preparation devices of the strengthened nano dispersion alloy, the mechanical performance and high-temperature creep property of the metal or alloy are improved, and the finally produced finishedproduct is stable in performance, free of inclusion, low in cost and applicable to industrial continuous production.

Description

technical field [0001] The invention relates to the field of material preparation, in particular to a preparation method of a nano-dispersion strengthened alloy. Background technique [0002] Nano-dispersion strengthened alloy materials have excellent physical and mechanical properties, including room temperature strength and high temperature strength, wear resistance, electrical conductivity, thermal conductivity, etc. By introducing stable, uniform, nano-scale particles into the metal matrix to closely combine with the matrix, the diffusely distributed nanoparticles pin dislocations and increase the dislocation density, thereby enhancing the work hardening effect; under high temperature conditions, the strengthening particles do not dissolve and growth, it has a strong hindering effect on dislocation movement and grain boundary migration, achieves high temperature softening resistance, and makes the material have better high temperature mechanical properties. At the same t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C1/10C22C1/02C22C33/04B22F9/08
CPCC22C1/1036C22C1/02C22C33/04B22F9/082B22F2009/0848C22C1/1047
Inventor 张少明贺会军林卓贤王志刚刘希学刘建赵朝辉朱捷张焕鹍朱学新
Owner BEIJING COMPO ADVANCED TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com