Flame-retardant inorganic interior wall coating and preparation method thereof

An interior wall coating, inorganic technology, applied in fireproof coatings, antifouling/underwater coatings, alkali metal silicate coatings, etc., can solve problems such as easy to get dirty, easy to condense, and hidden safety hazards, and achieve the purpose of inhibiting polymer decomposition , Improve storage stability, improve the effect of fire resistance

Pending Publication Date: 2019-11-01
SHENZHEN GRANDLAND ENVIRONMENTAL COATING CO LTD
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, at present, most of the existing interior wall decoration paints are made of organic materials and inorganic mineral materials, which are combustible in case of fire, thus bringing potential safety hazards. A series of problems such as dirty, poor scratch resistance, easy to crack, and easy to condense during the rainy season

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant inorganic interior wall coating and preparation method thereof
  • Flame-retardant inorganic interior wall coating and preparation method thereof
  • Flame-retardant inorganic interior wall coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] The present invention provides a kind of preparation method of flame retardant inorganic interior wall paint, comprises the following steps:

[0036] Step 1. Premixing of slurry system:

[0037] Add 250kg of deionized water into the dispersion container, and slowly add 3kg of hydroxyethyl cellulose of Yakuolong 250HBR under the state of dispersing and stirring (the speed is controlled at 300-600RPM), and at the same time add 2kg of BENTONE EW-NA bentonite, and then at 600 rpm Disperse at 600 rpm for 10 minutes, then add 8 kg of LOPON827 stabilizer at 600 rpm, and disperse for 5 minutes until the cellulose has no particles, no clusters, and is in the form of a transparent gel, ready for use;

[0038] Step 2. Add additives:

[0039] Under the stirring state of 600 rpm, add 1 kg of BYK024 antifoaming agent and 1 kg of Hoffman D26 preservative to the premixed slurry obtained in step 1 of the production tank in sequence, disperse for 5 minutes until uniform, and set aside ...

Embodiment 2

[0049] The present invention provides a kind of preparation method of flame retardant inorganic interior wall paint, comprises the following steps:

[0050] Step 1. Premixing of slurry system:

[0051] Add 265kg of deionized water into the dispersing container, slowly add 3.5kg of hydroxyethyl cellulose of Yakuolong 250HBR under the state of dispersing and stirring (rotating speed is controlled at 300-600RPM), and add 1.5kg of BENTONE EW-NA bentonite at the same time, and then Disperse at 600 rpm for 10 minutes, then add 6 kg of LOPON827 stabilizer at 600 rpm, and disperse for 5 minutes until the cellulose has no particles, no clusters, and it is transparent gel, ready for use;

[0052] Step 2. Add additives:

[0053] Under the stirring state of 600 rpm, add 5 kg of BYK024 antifoaming agent and 1.5 kg of Hoffmann D26 preservative to the premixed slurry obtained in step 1 of the production tank in sequence, and disperse for 5 minutes to a uniform state. use;

[0054] Step 3,...

Embodiment 3

[0063] The present invention provides a kind of preparation method of flame retardant inorganic interior wall paint, comprises the following steps:

[0064] Step 1. Premixing of slurry system:

[0065] Add 300kg of deionized water into the dispersion container, and slowly add 4kg of hydroxyethyl cellulose of Yakuolong 250HBR under the state of dispersing and stirring (controlling the speed at 300-600RPM), and add 1kg of BENTONE EW-NA bentonite at the same time, and then at 600 rpm Disperse at 600 rpm for 10 minutes, then add 5 kg of LOPON827 stabilizer at 600 rpm, and disperse for 5 minutes until the cellulose has no particles, no clusters, and is in the form of a transparent gel, ready for use;

[0066] Step 2. Add additives:

[0067] Under the stirring state of 600 rpm, add 3 kg of BYK024 antifoaming agent and 2 kg of Hoffman D26 preservative to the premixed slurry obtained in step 1 of the production tank in sequence, and disperse for 5 minutes to a uniform state, ready fo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
minimum film forming temperatureaaaaaaaaaa
densityaaaaaaaaaa
Mohs hardnessaaaaaaaaaa
Login to View More

Abstract

The invention provides a flame-retardant inorganic interior wall coating and a preparation method thereof. The coating is prepared by mixing the following components comprising, by weight, 250-315 parts of deionized water, 3-5 parts of hydroxyethyl cellulose, 0.5-2 parts of bentonite, 3-8 parts of a stabilizer, 1-5 parts of a defoaming agent, 1-2 parts of a preservative, 100-250 parts of magnesiumhydroxide, 90-190 parts of titanium dioxide, 30-80 parts of calcined kaolin, 50-80 parts of 800# heavy calcium carbonate, 150-230 parts of inorganic potassium silicate, 50-100 parts of a styrene-acrylic emulsion and 2-5 parts of a thickener. The paint has the characteristics of flame retardancy, compactness, multicolor, scratch resistance, cracking resistance, dew formation resistance, mildew resistance, stain resistance, easiness in scrubbing and good storage stability.

Description

technical field [0001] The invention relates to the technical field of building decoration functional materials, in particular to a flame retardant inorganic interior wall coating and a preparation method thereof. Background technique [0002] Among the interior wall decoration materials of modern buildings, interior wall decoration paint is suitable for the interior decoration of various buildings, especially for The decoration of curved buildings has always occupied an important position in wall decoration at home and abroad. [0003] However, at present, most of the existing interior wall decoration paints are made of organic materials and inorganic mineral materials, which are flammable in case of fire, thus bringing potential safety hazards. In addition, the walls using the existing interior wall decoration paints still have soft hardness, easy Dirty, poor scratch resistance, easy to crack, and easy to condense during the rainy season. Contents of the invention [0...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D1/04C09D5/14C09D5/16C09D5/18C09D7/61C09D7/65
CPCC09D1/00C09D1/04C09D5/14C09D5/1687C09D5/18
Inventor 谷二宁徐新祥付超王鹏程刘述敏
Owner SHENZHEN GRANDLAND ENVIRONMENTAL COATING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com