A kind of bizn hydrotalcite photocatalyst and its preparation method and application

A catalyst, Shiguang's technology, applied in the direction of chemical instruments and methods, preparation of organic compounds, physical/chemical process catalysts, etc., can solve the problems of unfavorable practical application, cumbersome production process, harsh reaction conditions, etc., and achieve low raw material cost and high reaction rate. The effect of low condition requirement and reduction of reaction cost

Active Publication Date: 2021-07-16
SOUTH CHINA UNIV OF TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, methods for synthesizing hydrotalcite mainly include low-saturation co-precipitation method, hydrothermal synthesis method, ion exchange method, microwave crystallization method, etc., but these methods have harsh reaction conditions, cumbersome production process, and are not conducive to practical applications. question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of bizn hydrotalcite photocatalyst and its preparation method and application
  • A kind of bizn hydrotalcite photocatalyst and its preparation method and application
  • A kind of bizn hydrotalcite photocatalyst and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Mix 0.72g sodium lauryl sulfate, 20mL ethylene glycol and 1.1mL water, then add 1.5mL n-butanol solution dropwise (the volume ratio of ethylene glycol and n-butanol to water is 19.5:1, the surface active The dosage ratio of agent and water is 0.0025:1mol / ml), wait for the solution to stir until it is transparent. Add 0.002 mol of zinc acetate and 0.002 mol of bismuth nitrate pentahydrate (the ratio of zinc salt to water is 0.1:1 mol / L). After stirring for 1 h, 1.35 g of thiourea was added (the ratio of thiourea to water was 0.017:1 mol / mL), and the oil bath was heated to 80°C, and the heating was continued for 20 hours. After the heating is completed, cool down and perform suction filtration to collect the solid product, transfer the solid product to a constant temperature box and dry it at 60° C. to obtain a BiZn hydrotalcite photocatalyst.

Embodiment 2

[0040] Mix 0.72g of sodium lauryl sulfate, 20mL of ethylene glycol and 1.1mL of water, then add 1.5mL of n-butanol solution dropwise, and wait until the solution is stirred until it becomes transparent. 0.002 mol of zinc acetate and 0.002 mol of bismuth nitrate pentahydrate were added. After stirring for 1 h, 1.35 g of thiourea (or urea of ​​the same concentration) was added, and the oil bath was heated to 90° C., and the heating was continued for 26 hours. After the heating is completed, cool down and perform suction filtration to collect the solid product, transfer the solid product to a constant temperature box and dry it at 60° C. to obtain a BiZn hydrotalcite photocatalyst. figure 1 The SEM image obtained for this embodiment has a relatively clear two-dimensional ultra-thin nanosheet structure, and the thickness of the nanosheet is 5-10 nm. figure 2 The TEM image obtained in this example shows typical lattice fringes of BiZn hydrotalcite. image 3 For the XRD image obt...

Embodiment 3

[0042] Mix 0.72g of sodium lauryl sulfate, 20mL of ethylene glycol and 1.1mL of water, then add 1.5mL of n-butanol solution dropwise, and wait until the solution is stirred until it becomes transparent. 0.002 mol of zinc acetate and 0.002 mol of bismuth nitrate pentahydrate were added. After stirring for 1 h, 1.35 g of thiourea was added, and the oil bath was heated to 100° C., and the heating was continued for 30 hours. After the heating is completed, cool and perform suction filtration to collect the solid product, transfer the solid product to a constant temperature box and dry it at 60° C. to obtain a BiZn hydrotalcite photocatalyst.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a BiZn hydrotalcite photocatalyst and its preparation method and application. The catalyst is a two-dimensional ultra-thin BiZn nanosheet, and the thickness of the nanosheet is 5-10nm. The preparation method comprises: (1) mixing a surfactant, ethylene glycol and water, then adding n-butanol, and stirring the solution until it becomes transparent; (2) adding zinc salt and bismuth salt, and adding thiourea or urea after stirring to obtain a mixed (3) After the heating is completed, the BiZn hydrotalcite catalyst is obtained after cooling and filtering and drying, and the BiZn hydrotalcite photocatalyst can be used to catalyze the conversion of xylose into xylonic acid. The invention requires low reaction conditions, low raw material cost, simple and feasible synthesis method, reduces production cost, and makes the reaction have the potential for industrialization, and the photocatalytic reaction system is different from the traditional thermocatalytic process, and the process is energy-saving, green, safe and environmentally friendly.

Description

technical field [0001] The invention belongs to the interdisciplinary technical fields of two-dimensional materials, photocatalysis, and conversion of biomass into chemicals, and in particular relates to a BiZn hydrotalcite photocatalyst and a preparation method and application thereof. Background technique [0002] Hemicellulose is a very abundant biomass resource in nature. Hemicellulose is a heterogeneous polymer composed of several different types of monosaccharides, five- and six-carbon sugars, including xylose, arabinose, and galactose. And xylose is the main product of hemicellulose hydrolyzate, and xylose acid can be obtained by oxidation of xylose. Xylose acid is one of the important metabolites of vitamin C, and it plays a vital role in regulating the effective circulation and metabolism of vitamin C in organisms. Therefore, xylose in hemicellulose can be used to produce xylonic acid, which not only significantly reduces production costs and accelerates the devel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/18C07C51/295C07C59/105
CPCB01J23/007B01J23/18B01J35/004C07C51/295C07C59/105
Inventor 彭新文李铭赛钟林新马纪亮邹刃陈亮
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More